Laser induced copper electroless plating on polyimide with Q-switch Nd:YAG laser

The results of laser induced deposition of copper on polyimide substrate from copper electrolyte solution are reported. Unlike most work reported in the literatures where CW Ar⁺ lasers were used, a second harmonic (532 nm wavelength) Q-switch Nd:YAG laser was used for our experiments. The deposition process was conducted by laser-catalyzing of the polyimide surface and subsequent photothermal-accelerated reduction of copper-complex ions in an alkaline reducing environment. The characteristics of the deposited copper line were investigated in terms of laser beam scanning speed, and the number of scans. The surface morphology and chemical composition of the deposited copper were analyzed using field emission scanning electron microscope (FESEM) and energy dispersive spectrometer (EDX). The optimum processing conditions have been identified. The copper deposit was found to adhere well to the substrate.     

不同入射角度下强流脉冲电子束能量沉积剖面和束流传输系数模拟计算

 强流脉冲电子束在材料中的能量沉积剖面、能量沉积系数和束流传输系数受其入射角的影响很大，理论计算了0.5~2.0MeV的电子束以不同的入射角在Al材料中的能量沉积剖面和能量沉积系数，并且还计算了0.4~1.4MeV电子束以不同入射角穿透不同厚度C靶的束流传输系数。计算结果表明，随着入射角的增大，靶材表面层单位质量中沉积的能量增大，电子在靶材料中穿透深度减小，能量沉积系数减小，相应的束流传输系数也减小；能量为0.5~2.0MeV的电子束当入射角在60°~70°时在材料表面层单位质量中沉积的能量较大。     

Approaches to improving critical current density of YBCO superconducting thick films deposited by electrophoresis

The irreversibility field (Hirr) of Y-based superconductor is much higher than that of Bi-based superconductor. Y-based superconductor is capable of maintaining stable electrical currents in high magnetic field and electric field, so it is a better suited mate-rial for electric-current applications. Commonly, the Y-based tapes comprise a YBCO thick film deposited on a flexible substrate, typically with an intermediate buffer layer, and an overcoat of noble metal. In this process, the interm…     

甲基对硫磷的快速测定及电化学性质

研究了杀虫剂甲基对硫磷的电化学性质。在pH10．38的Bdtton—Robinson缓冲溶液中，采用微分脉冲溶出伏安法在悬汞电极上得到一个还原峰，峰电位为-0．5V(vs．Ag/AgCl)，本工作对实验条件进行了深入的研究，结合线性扫描伏安法等手段。研究了体系的电化学行为。实验表明，甲基对硫磷在汞电极上具有吸附性，电极反应具有不可逆性。该法用于水果及水样中甲基对硫磷残余量的测定，结果满意。     

Fabrication and characterization of a PbTe quantum dots multilayer structure

Multilayer PbTe quantum dots (QDs) and SiO₂ were grown by pulsed laser deposition (PLD) and Plasma enhanced chemical vapor deposition (PECVD) techniques. The crystalline structure, QD size and size dispersion were observed by high-resolution transmission electron microscopy (HRTEM) measurements. This technique allows one to grow PbTe QDs as small as 1.8 nm diameter and 0.6 nm size dispersion. The whole structure can be used in a Fabry–Perot cavity for an optical device operating at the mid-infrared region.     

电致发光色纯性增强的硅基有机微腔

报道了硅基有机微腔的电致发光（EL）.该微腔由上半透明金属膜、中心有源多层膜和多孔硅分布Bragg反射镜（PS DBR）组成.半透明金属膜由Ag（２０nm）构成，充当发光器件的负电极和微腔的上反射镜.有源多层膜由Al (1 nm) / LiF(05 nm) /Alq3/Alq3:DCJTB/NPB/CuPc/ITO/SiO2组成，其中的Al/LiF为电子注入层，ITO为正电极，SiO2为使正、负电极电隔离的介质层.该PS DBR是采用设备简单、成本低廉且非常省时的电化学腐蚀法用单晶Si来制备的；该PS 关键词： 电化学腐蚀 电致发光 窄峰发射 硅基有机微腔     

密封容器中后处理制备Tl2Ba2CaCu2Oy高温超导薄膜及其性能研究

以铝酸镧（001）单晶为基片，采用两步法制备Tl2Ba2CaCu2Oy（Tl 2212）高 温超导薄膜.首先，利用脉冲激光沉积（PLD）工艺沉积Ba2CaCu2Ox非晶前驱体薄膜；然后，前驱体薄膜在高温（720—850℃）下密封钢容器里铊化结晶形成Tl 2212薄膜.XRD结果表明Tl2212 薄膜是沿c轴方向生长的，其相组成为Tl 2212，摇摆曲线（0012）的半高宽为0.72° ，SEM图像显示其表面光滑平整，其零电阻温度为106.2K. 关键词： Tl 2212超导薄膜 脉冲激光沉积     

离子束增强沉积VO2多晶薄膜的温度系数

用改进的离子束增强沉积方法和恰当的退火从V2O5粉末直接制备了VO2多晶薄膜.实验测试表明，薄膜的取向单一、相变特性显著、结构致密、界面结合牢固、工艺性能良好，薄膜的电阻温度系数（TCR）最高可达4.23%/K.从成膜机理出发，较详细地讨论了离子束增强沉积 VO2多晶薄膜的TCR高于VOx薄膜的TCR的原因.分析认为，单一取向的VO2结构使薄膜晶粒具有较高的电导激活能，致密的薄膜结构减少了氧空位和晶界宽度，使离子束增强沉积 VO2多晶薄膜结构比其他方法制备的VOx薄膜更接近于单晶VO2是其具有高TCR的原 关键词： VO2多晶薄膜 离子束增强沉积 热电阻温度系数     

采用空心阴极放电等离子体化学气相沉积方法制备a-CH薄膜

 研究了不同衬底-阴极距离、直流电压和H₂流量对a-CH薄膜沉积速率的影响。结果表明：衬底-阴极距离必须大于0.5cm，随着该距离的增加，薄膜的沉积速率减少；直流电压达550V时沉积速率最大；随着H2含量的增加，CH₄含量相对减少，沉积速率随之降低。用AFM观察了以该方法制得的448.4nm CH薄膜的表面形貌，表面粗糙度约为10nm。最后测出了不同条件下CH薄膜的UV-VIS谱，由此可以计算得到薄膜的禁带宽度及折射率。     

闪烁光纤在γ射线辐照下部分特性的蒙特卡罗模拟

 闪烁光纤在射线成像方面的应用越来越广泛。为了进一步了解闪烁光纤在射线辐照下的基本特性，基于蒙特卡罗方法，利用计算机模拟分析了γ射线在闪烁光纤中的好事例率与光纤长度及射线能量的关系，能量沉积效率与光纤长度及射线能量的关系。此项工作对于闪烁光纤阵列在射线成像，剂量场测量等方面的研究很有价值。