Influence of organic modifiers on morphology and crystallization of poly(ϵ‐caprolactone)/synthetic clay intercalated nanocomposites

ε‐caprolactone was polymerized in the presence of neat montmorillonite or organomontmorillonites to obtain a variety of poly(ε‐caprolactone) (PCL)‐based systems loaded with 10 wt % of the silicates. The materials were thoroughly investigated by different X‐ray scattering techniques to determine factors affecting structure of the systems. For one of the nanocomposites it was found that varying the temperature in the range corresponding to crystallization of PCL causes reversible changes in the interlayer distance of the organoclay. Extensive experimental and literature studies on this phenomenon provided clues indicating that this effect might be a result of two‐dimensional ordering of PCL chains inside the galleries of the silicate. Small angle X‐ray scattering and wide angle X‐ray scattering investigation of filaments oriented above melting point of PCL revealed that polymer lamellae were oriented perpendicularly to particles of unmodified silicate, while in PCL/organoclay systems they were found parallel to clay tactoids. Calorimetric and microscopic studies shown that clay particles are effective nucleating agents. In the nanocomposites, PCL crystallized 20‐fold faster than in the neat polymer. The crystallization rate in nanocomposites was also significantly higher than in microcomposite. Further research provided an insight how the presence of the filler affects crystalline fraction and spherulitic structure of the polymer matrix in the investigated systems. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2350–2367, 2007     

Isothermal crystallization kinetics of poly(3‐hydroxybutyrate)/layered double hydroxide nanocomposites

Poly(3‐hydroxybutyrate) (PHB)/layered double hydroxides (LDHs) nanocomposites were prepared by mixing PHB and poly(ethylene glycol) phosphonates (PEOPAs)‐modified LDH (PMLDH) in chloroform solution. Both X‐ray diffraction data and TEM micrographs of PHB/PMLDH nanocomposites indicate that the PMLDHs are randomly dispersed and exfoliated into the PHB matrix. In this study, the effect of PMLDH on the isothermal crystallization behavior of PHB was investigated using a differential scanning calorimeter (DSC) and polarized optical microscopy. Isothermal crystallization results of PHB/PMLDH nanocomposites show that the addition of 2 wt % PMLDH into PHB induced more heterogeneous nucleation in the crystallization significantly increasing the crystallization rate and reducing their activation energy. By adding more PMLDH into the PHB probably causes more steric hindrance of the diffusion of PHB, reducing the transportation ability of polymer chains during crystallization, thus increasing the activation energy. The correlation among crystallization kinetics, melting behavior and crystalline structure of PHB/PMLDH nanocomposites can also be discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3337–3347, 2006     

Temperature‐modulated differential scanning calorimetry studies on the origin of double melting peaks in isothermally melt‐crystallized poly(L‐lactic acid)

In this work, the melting behaviors of nonisothermally and isothermally melt‐crystallized poly(L ‐lactic acid) (PLLA) from the melt were investigated with differential scanning calorimetry (DSC) and temperature‐modulated differential scanning calorimetry (TMDSC). The isothermal melt crystallizations of PLLA at a temperature in the range of 100–110 °C for 120 min or at 110 °C for a time in the range of 10–180 min appeared to exhibit double melting peaks in the DSC heating curves of 10 °C/min. TMDSC analysis revealed that the melting–recrystallization mechanism dominated the formation of the double melting peaks in PLLA samples following melt crystallizations at 110 °C for a shorter time (≤30 min) or at a lower temperature (100, 103, or 105 °C) for 120 min, whereas the double lamellar thickness model dominated the formation of the double melting peaks in those PLLA samples crystallized at a higher temperature (108 or 110 °C) for 120 min or at 110 °C for a longer time (≥45 min). © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 466–474, 2007     

Effect of nanotube functionalization on the properties of single‐walled carbon nanotube/polyurethane composites

A commercially available aliphatic thermoplastic polyurethane formulated with a methylene bis(cyclohexyl) diisocyanate hard segment and a poly(tetramethylene oxide) soft segment and chain‐extended with 1,4‐butanediol was dissolved in dimethylformamide and mixed with dispersed single‐walled carbon nanotubes. The properties of composites made with unfunctionalized nanotubes were compared with the properties of composites made with nanotubes functionalized to contain hydroxyl groups. Functionalization almost eliminated the conductivity of the tubes according to the conductivity of the composites above the percolation threshold. In most cases, functionalized and unfunctionalized tubes yielded composites with statistically identical mechanical properties. However, composites made with functionalized tubes did have a slightly higher modulus in the rubbery plateau region at higher nanotube fractions. Small‐angle X‐ray scattering patterns indicated that the dispersion reached a plateau in the unfunctionalized composites that was consistent with the plateau in the rubbery plateau region. The room‐temperature modulus and tensile strength increase was proportionally higher than almost all increases seen previously in thermoplastic polyurethanes; however, the increase was still an order of magnitude below what has been reported for the best nanotube–polymer systems. Nanotube addition increased the hard‐segment glass transition temperature slightly, whereas the soft‐segment glass transition was so diffuse that no conclusions could be drawn. Unfunctionalized tubes suppressed the crystallization of the hard segment; whereas functionalized tubes had no effect. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 490–501, 2007     

Side‐chain crystallization behavior of graft copolymers consisting of an amorphous main chain and crystalline side chains. II. Poly(n‐hexyl methacrylate)‐graft‐poly(ethylene glycol)

The phase behavior and crystallization of graft copolymers consisting of poly(n‐hexyl methacrylate) (PHMA) as an amorphous main chain and poly(ethylene glycol) (PEG) as crystallizable side chains (HMAx with 15 ≤ x ≤ 73, where x represents the weight percentage of PEG) were investigated. Small‐angle X‐ray scattering profiles measured above the melting temperature of PEG suggested that a microdomain structure with segregated PHMA and PEG domains was formed in HMA40 and HMA46. This phase behavior was qualitatively described by a calculated phase diagram based on the mean‐field theory. Because of the segregation of PEG into microdomains, the crystallization temperature of the PEG side chains in HMAx was higher than that in poly(methyl acrylate)‐graft‐poly(ethylene glycol) having a similar value of x, which was considered to be in a disordered state above the melting temperature. In HMAx with x ≤ 40, PEG crystallization was strongly restricted, probably because the PEG microdomains were isolated in the PHMA matrix. As a result, the growth of PEG spherulite was not observed because the PEG crystallization occurred after vitrification of the PHMA segregated domains. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 129–137, 2007     

Synthesis and characterization of poly(higher‐α‐olefin)s with a nickel(α‐diimine)/methylaluminoxane catalyst system: Effect of chain running on the polymer properties

Homopolymerization of octadecene‐1 at different reaction conditions has been studied. Significant chain running can be seen at higher polymerization temperatures. Interestingly, insertion of octadecene‐1 into a sterically hindered nickel‐cation/carbon (secondary) bond is observed. The microstructure of the polymer was established using NMR spectroscopy. The effects of chain running on polymer melting, crystallization behavior, and dynamic mechanical thermal properties were studied using DSC and DMTA. The extent of chain running (i.e., 2,ω‐, 1,ω‐enchainments) decreases with an increase in the carbon number of α‐olefins. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 191–210, 2007     

Chemical component exchange and transport phenomena accompanying phase transformations in minerals and materials

Chemical component exchange and transport phenomena accompanying the multistage phase transformations of several silicate and aluminosilicate-phosphate glasses and borates as model systems are considered. It is demonstrated that the component transport limitations modify the role of chemical affinity influence and determine the sequence of new compound formation.The work was supported by grant P040703406 from the National Committee of Scientific Research of Poland.     

Stereocontrol of diene polymers by topochemical polymerization of substituted benzyl muconates and their crystallization properties

We report the stereocontrol of diene polymers by the topochemical polymerization of alkoxy-substituted benzyl muconates in the solid state. A monomer stacking structure is controlled by the weak intermolecular interactions in the monomer crystals, depending on the structure and position of the alkoxy-substituent. The translational and alternating types of molecular stacking structures in a column provide diisotactic and disyndiotactic polymers, respectively, by the solid-state polymerization under UV and γ-ray irradiation. On the other hand, the meso and racemo structures of the resulting polymers are determined by the molecular symmetry of the used muconate monomers. The various substituted benzyl ester polymers are transformed into the same ethyl ester polymers with the four types of tacticities. The structure and crystallization behavior of the substituted benzyl ester polymers as well as the ethyl ester polymers have been revealed in detail. We clarify the effects of the tacticity on the crystallization property of the stereoregular polymuconates. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4952–4965, 2006     

Thermal stability of shear-induced precursor structures in isotactic polypropylene by rheo-X-ray techniques with couette flow geometry

Combined in situ rheo-SAXS (small-angle X-ray scattering) and -WAXD (wide-angle X-ray diffraction) studies using couette flow geometry were carried out to probe thermal stabilty of shear-induced oriented precursor structure in isotactic polypropylene (iPP) at around its normal melting point (162 °C). Although SAXS results corroborated the emerging consensus about the formation of “long-living” metastable mesomorphic precursor structures in sheared iPP melts, these are the first quantitative measures of the limiting temperature at which no oriented structures survive. At the applied shear, rate = 60 s⁻¹ and duration t_s = 5 s, the oriented iPP structures survived a temperature of 185 °C for 1 h after shear, while no stable structures were detected at and above 195 °C. Following Keller's concepts of chain orientation in flow, it is proposed that the chains with highly oriented high molecular weight fraction are primarily responsible for their stability at high temperatures. Furthermore, the effects of flow condition, specifically the shear temperature, on the distributions of oriented and unoriented crystals were determined from rheo-WAXD results. As expected, at a constant flow intensity (i.e., rate = 30 s⁻¹ and duration, t_s = 5 s), the oriented crystal fraction decreased with the increase in temperature above 155 °C, below which the oriented fraction decreased with the decrease in temperature. As a result, a crystallinty “phase” diagram, i.e., temperature versus crystal fraction ratio, exhibited a peculiar “hourglass” shape, similar to that found in many two-phase polymer–polymer blends. This can be explained by the competition between the oriented and unoriented crystals in the available crystallizable species. Below the shear temperature (155 °C), the unoriented crystals crystallized so rapidly that they overwhelmed the crystallization of the oriented crystals, thus depleting a major portion of the crystallizable species and increasing their contribution in the final total crystalline phase. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3553–3570, 2006     

Chiral soluble polymers and microspheres for enantioselective crystallization

A series of chiral polymers based on poly(N‐acryl) amino acids was synthesized using a convergent synthetic approach. These chiral polymers have been used as chiral additives to induce enantioselective crystallization of racemic or conglomerate amino acids in solutions. These polymeric additives showed strong capabilities to enhance highly enantioselective resolution during the crystallization of amino acids. In addition, these polymers caused unusual modifications of amino acid crystal morphologies. Furthermore, spherical microparticles of those same chiral polymers were also shown active in similar chiral discriminations during amino acid crystallizations occurring on microparticle surfaces. Our study demonstrates the high potential of chiral polymers and microparticles to resolve amino acids throughout crystallization processes. High enantiomeric excesses in one targeted enantiomer of amino acids can also be maximized via time‐dependent kinetic control of crystallizations. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3009–3017, 2006