Kinetic features of ethylene polymerization over supported catalysts [2,6‐bis(imino)pyridyl iron dichloride/magnesium dichloride] with AlR3 as an activator

The effects of polymerization temperature, polymerization time, ethylene and hydrogen concentration, and effect of comonomers (hexene‐1, propylene) on the activity of supported catalyst of composition LFeCl₂/MgCl₂‐Al(i‐Bu)₃ (L = 2,6‐bis[1‐(2,6‐dimethylphenylimino)ethyl] pyridyl) and polymer characteristics (molecular weight (MW), molecular‐weight distribution (MWD), molecular structure) have been studied. Effective activation energy of ethylene polymerization over LFeCl₂/MgCl₂‐Al(i‐Bu)₃ has a value typical of supported Ziegler–Natta catalysts (11.9 kcal/mol). The polymerization reaction is of the first order with respect to monomer at the ethylene concentration >0.2 mol/L. Addition of small amounts of hydrogen (9–17%) significantly increases the activity; however, further increase in hydrogen concentration decreases the activity. The IRS and DSC analysis of PE indicates that catalyst LFeCl₂/MgCl₂‐Al(i‐Bu)₃ has a very low copolymerizing ability toward propylene and hexene‐1. MW and MWD of PE produced over these catalysts depend on the polymerization time, ethylene and hexene‐1 concentration. The activation effect of hydrogen and other kinetic features of ethylene polymerization over supported catalysts based on the Fe (II) complexes are discussed. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5057–5066, 2007     

Graphitic nanofillers in PMMA nanocomposites—An investigation of particle size and dispersion and their influence on nanocomposite properties

Mechanical, thermal, and electrical properties of graphite/PMMA composites have been evaluated as functions of particle size and dispersion of the graphitic nanofiller components via the use of three different graphitic nanofillers: “as received graphite” (ARG), “expanded graphite,” (EG) and “graphite nanoplatelets” (GNPs) EG, a graphitic materials with much lower density than ARG, was prepared from ARG flakes via an acid intercalation and thermal expansion. Subsequent sonication of EG in a liquid yielded GNPs as thin stacks of graphitic platelets with thicknesses of ～10 nm. Solution‐based processing was used to prepare PMMA composites with these three fillers. Dynamic mechanical analysis, thermal analysis, and electrical impedance measurements were carried out on the resulting composites, demonstrating that reduced particle size, high surface area, and increased surface roughness can significantly alter the graphite/polymer interface and enhance the mechanical, thermal, and electrical properties of the polymer matrix. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2097–2112, 2007     

Simultaneous Measurement of Particle Size and Particle Velocity by the Spatial Filtering Technique

The objective of this study was to compare the measuring results of a fiber‐optical probe based on a modified spatial filtering technique with given size distributions of different test powders and also with particle velocity values of laser Doppler measurements. Fiber‐optical spatial filtering velocimetry was modified by fiber‐optical spot scanning in order to determine simultaneously the size and the velocity of particles. The fiber‐optical probe system can be used as an in‐line measuring device for sizing of particles in different technical applications. Spherical test particles were narrow‐sized glass beads in the range 30–100 μm and irregularly shaped test particles were limestone particles in the range 10–600 μm. Particles were dispersed by a brush disperser and the measurements were carried out at a fixed position in a free particle‐laden air stream. Owing to the measurement of chord lengths and to the influence of diffraction and divergent angle, the probe results show differences from the given test particle sizes. Owing to the particle‐probe collisions, the mean velocity determined by the probe is smaller than the laser Doppler mean velocity.     

Particle Size Analysis by Transmission Fluctuation Spectrometry: Experimental Results Obtained with a Gaussian Beam and Analog Signal Processing

Transmission fluctuation spectrometry (TFS) is a method for the analysis of particle size distributions based on the statistical fluctuations of a transmission signal. Complete information on the PSD and particle concentration can be retrieved by a special transformation of the transmission signal, whereby the expectancy of the transmission square (ETS) is determined after the signal has been subjected to a procedure of spatial and temporal averaging. By varying the averaging parameters over a wide range, a spectrum of ETSs is obtained and introduced into a linear equation system, which yields the PSD. In the experimental realization presented here, variable temporal averaging is realized in the frequency domain with a series of low pass filters at different cutoff frequencies while spatial averaging inevitably occurs as the particles pass through a focused Gaussian beam of finite cross section. Experimental results on spherical particles (glass beads) and non‐spherical particles (SiC) are presented. The PSDs are resolved in 30 intervals within a particle size range from 1–1000 μm, employing a modified Chahine inversion algorithm. So far, the measurements are limited to moderate particle concentrations. Some influences affecting the measurements, especially for higher particle concentrations, are discussed in detail.     

Tuning size and catalytic activity of nano-clusters of cobalt oxide

Cobalt oxides were prepared by three different methods: (1) by reacting cobalt nitrate with oxalic acid, (2) co-precipitating cobalt nitrate with sodium carbonate, and (3) using sodium dodecyl sulphate as organic surfactant. All three samples were characterized before and after calcination by solvent extraction and the resulting products examined by IR spectroscopy. In the case of method 3, the removal of surfactant was followed by TGA studies. Products from all three methods were identified by XRD. Peaks in low angle XRD indicate the porous nature of the oxides. The morphology of the pores was studied by transmission electron microscopy. Some irregular pore structures were obtained for samples from methods 1 and 2, with an average size of 4–6 nm. Only the product from method 3 using SDS as template showed ordered structure and optimum size, and Brunauer-Emmet-Teller surface areas of the as-prepared, as well as the treated samples, exhibited H3 type hysteresis. The samples from the three methods were used as catalysts in the oxidation reaction of cyclohexane under mild conditions and the catalytic efficiency of the cobalt oxide was comparable with mesoporous cobalt oxides.     

Effect of reaction conditions on the molecular weight and polydispersity of linear poly(arylene ether phosphine oxide)s prepared from an AB monomer

A thorough study of the polymerization behavior of 4‐fluoro‐4′‐hydroxytriphenyl‐phosphine oxide, 2 , under nucleophilic aromatic substitution reactions has been carried out. The synthesis of 2 was achieved in excellent yields by the reaction of bis(4‐fluorophenyl)phenylphosphine oxide, 1 , with one equivalent of potassium hydroxide in DMSO/water. The structure and purity of 2 were confirmed via ¹H, ¹³C, and ³¹P NMR spectroscopy along with elemental analysis. Polymerization reactions of 2 in NMP or DMSO at 180 °C provided the corresponding linear poly(arylene ether phosphine oxide)s, PAEPOs, with number average molecular weights, M_n, ranging from 11,700 to 36,500 Da. All of the polymer samples were completely soluble in chloroform, tetrahydrofuran, DMSO, NMP, and DMAc. The polymerization reactions were accompanied by a competing intramolecular process that resulted in the formation of cyclic oligomeric species that were removed via a final precipitation from methanol. Analysis using ³¹P NMR spectroscopy and size exclusion chromatography (SEC) confirmed that the majority of the lower molecular weight cyclic species were removed via this process. The polymer samples formed tough films when chloroform solutions were slowly evaporated on a glass slide. The PAEPO samples prepared in this study exhibited excellent thermal stability with T_d (5%) values between 503 and 542 in air while the glass transition temperatures ranged from 223 to 237 °C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2099–2106, 2006     

Synthesis of polyacrylonitrile via reverse atom transfer radical polymerization catalyzed by FeCl3/isophthalic acid

FeCl₃ coordinated by isophthalic acid was first used as a catalyst in the azobisisobutyronitrile‐initiated reverse atom transfer radical polymerization of acrylonitrile. N,N‐Dimethylformamide was used as a solvent to improve the solubility of the ligand. An FeCl₃‐to‐isophthalic acid ratio of 0.5 not only gave the best control of the molecular weight and its distribution but also provided rather a rapid reaction rate. The effects of different solvents on the polymerization of acrylonitrile were also investigated. The rate of the polymerization in N,N‐dimethylformamide was faster than that in propylene carbonate and toluene. The molecular weight of polyacrylonitrile agreed reasonably well with the theoretical molecular weight in N,N‐dimethylformamide. The rate of polymerization increased with increasing polymerization temperature, and the apparent activation energy was calculated to be 59.9 kJ mol^?1. Reverse atom transfer radical polymerization was first used to successfully synthesize acrylonitrile polymers with a molecular weight higher than 80,000 and a narrow polydispersity as low as 1.22. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 219–225, 2006