壳聚糖/聚乙烯醇共混超细纤维的制备及紫外光交联研究

用静电纺丝法制备壳聚糖/聚乙烯醇的共混超细纤维,采用扫描电镜考察了纺丝液浓度、共混物配比、喷丝口内径对纤维形貌的影响.此外,为减少壳聚糖/聚乙烯醇纤维膜的溶胀变形,在上述体系中加入可光交联的单体二缩三乙二醇双甲基丙烯酸酯(TEGDMA)、引发剂2-羟基-2-甲基-1苯基丙酮(1173),对电纺纤维进行紫外光交联.结果表明,当壳聚糖与聚乙烯醇质量比为8:2的共混体系中加入占混合溶液质量分数4%的TEGDMA、0.12%的1173作为交联剂时,所得的无纺布纤维直径比较均一,平均约为200 nm,经光交联处理后其耐水性能得到提高.     

离子交换纤维吸附去除As(Ⅲ)

制备了一种新型的离子交换纤维RPFA-I,用于去除水体中亚砷酸根离子的研究.在研究的范围内,Fre-undlich型吸附等温方程能够很好地描述等温吸附平衡数据;吸附动力学数据符合Lagergren二级速度方程;pH=6.22时,吸附量达到最大;用0.1mol/L的NaOH溶液可以实现纤维的再生,再生性能优良.     

Micellar electrokinetic capillary chromatography using polymeric hollow fibers

Summary In this paper, polymeric hollow fibers prepared from pH-stable polypropylene were used as columns for micellar electrokinetic capillary chromatography (MECC). The electroosmotic flow (EOF) for polypropylene hollow fibers was evaluated in the pH range of 5.0–12.0. With untreated polypropylene hollow fibers a stabilized but enhanced EOF was achieved when SDS was used in the buffer, decreasing the separation window for uncharged substances in MECC to impractical levels. Uncharged acrylamide and charged 2-acryloylamido-2-methylpropane sulfonic acid surface modifications were used to lower the strength of the EOF, increase the separation window and prevent local overheating that could melt the column wall.     

γ-射线辐照对尼龙6纤维结构的影响

<正> 过去的大多数研究表明,高能射线辐照会引起聚乙烯及聚丙烯等稀烃类聚合物分子链交联及降解,而且会导致结晶度下降。张利华等人最近的研究表明,对于尼龙1010塑料,仅当辐照剂量高到一定程度后,辐照才会破坏结晶。此外,Stowe等人曾经研究过近紫外线对尼龙66纤维结构的影响,结果表明,在空气气氛中的近紫外辐照主要导致尼龙66纤维降解,并使纤维结晶度提高。有关高能射线辐照对高度取向的合成纤维结构及性能的影响的研究尚不多见。本工作将讨论γ-射线对于尼龙6纤维结构的影响。     

FFC-1离子交换纤维对酸碱有害气体吸附性能的研究

系统考察了不同直径及反离子形式的FFC-1聚羧酸离子交换纤维对酸碱有害气体的穿透吸附,各种温、湿度条件下的吸水率,以及作为有害气体吸附滤除材料的重复使用与再生性能。研究表明:FFC-1纤维直径的减小有利于提高对有害气体的动态吸附容量。在体系温度、相对湿度分别为15℃、50%时,以3D腈纶为起始原料的钠型FFC-1离子交换纤维的吸水率≥350mg/g.纤维;对SO2的穿透吸附容量可达200mg/g.纤维。FFC-1离子交换纤维具有良好的重复使用与再生能力,经20次再生循环使用后,纤维交换容量未见明显变化。     

INTROMISSION OF WATER-REPELLENT AND HYDROSCOPIC PROPERTIES SIMULTANEOUSLY TO PP BY PLASMA DISCHARGE METHOD

Plasma-induced surface graft copolymerization of acrylic acid on polypropylene non-woven fabric (PP-g-AA) and polypropylene membrane were reported. The extents of grafting were controlled by the plasma and polymerization condition. Hexadecyltrimethyl ammonium bromide was then coupled with the carboxyl group of PP-g-AA to obtain a polyion complex (PIC). At last, CF4 plasma was used to give PICs hydrophobic property. The moisture regain and water-repellency of the processed PICs was investigated. The surfaces were characterized using ATR FT-IR and XPS. The result indicates that the products have very high ability to adsorb moisture, even better than cotton fiber. At the same time, the products show excellent hydrophobic property, which can‘t be wetted by those reagents whose surface tensions were higher than 327mN/m.     

碳纤维微电极恒电位活化及测定金属离子的研究

碳纤维微电极已被广泛应用于电化学研究和分析测定,该电极尺寸极小,在分析性能上与常规电极有显著不同,在不镀汞的情况下,用碳纤维电极直接测定金属离子几乎没有明显的伏安响应,本文提出用+2.5 V恒电位预先活化碳纤维电极,使测定灵敏度大为提高,在双电极体系和静止溶液中,采用溶出伏安法可测定10~(-9)级金属离子,以同样的方法清洗电极,测定结果重现性良好,由于分析过程中不使用汞,该电极的测定范围大大增加,特别是用于氧化还原电位较正的金属离子测试,根据循环伏安法、扫描电镜和电子能谱的研究,发现碳纤维表面状况在处理前后有很大变化,并与测定灵敏度密切相关。     

Adsorption separation of terpene lactones from Ginkgo biloba L. extract using glass fiber membranes modified with octadecyltrichlorosilane

In this study porous glass fiber membranes were modified by reaction with octadecyl-trichlorosilane to form C18 hydrophobic membranes. The contact angle and the CH2 vibration bands at 2855 and 2920 cm(-1) found by FTIR measurements verified the successful immobilization of C18 groups on the glass fiber membranes. The resulting C18 hydrophobic membranes were used to adsorb terpene lactones from crude Ginkgo biloba L. extracts. In batch adsorption processes, the modified C18 membranes exhibited a better adsorption performance than commercial C18 solid phase extraction adsorbents. Different desorption solvents were tested and ethyl acetate was found to preferentially desorb terpene lactones from the modified C18 membranes. In flow adsorption experiments at 1 mL/min, terpene lactone contents higher than 6 wt% (the standardized content) could be achieved in the elution step using ethyl acetate.     

STUDIES ON THE PREPARATION OF ZINC-CONTAINING ACTIVATED CARBON FIBERS AND THEIR ANTIBACTERIAL ACTIVITY

1. INTRODUCTION Microbial pollution will bring about various problems in industry and other vital fields, such as causing decomposing of materials, harming people抯 health. In order to reduce these problems, new antibacterial materials have been demanded. Recently, much attention has been paid to inorganic materials including zinc oxide [1~4]. These inorganic antibacterial materials are now substituting for organic materials to avoid releasing noxious organic molecules harmful to humans;…     

MORPHOLOGIES AND GAS SEPARATION PROPERTIES OF MELT-SPUN ASYMMETRIC POLY(4-METHYL-1-PENTENE)HOLLOW FIBER MEMBRANES*

Poly(4-methyl-1-pentene) (PMP) hollow fiber membranes were prepared by the melt-spun and cold-stretch(MSCS) method. Scanning electronic microscopy (SEM) was used to characterize the section and surface structures of themembranes with special asymmetric structure. The preliminary results of gas permeation measurements indicated that the resultant hollow fiber membranes have the potential ability for oxygen/nitrogen separation.