Synthesis and Molecular Structure of [Ru3(CO)10(μ-dppa)] (dppa = Ph2PN(H)PPh2) Provided by Its Dioxane Solvate

The sodium benzophenone ketyl-induced reaction of [Ru₃(CO)₁₂] with bis(diphenylphosphanyl)amine Ph₂PN(H)PPh₂ (dppa) in THF resulted in the formation of the expected metal cluster [Ru₃(CO)₁₀(μ-dppa)] ( 1 ) in high yield. 1 was fully characterized by spectroscopic means and crystals of the compound suitable for X-ray diffraction were obtained from dichloromethane/dioxane. The molecular structure of 1 as its dioxane solvate was determined by X-ray crystallography. The compound crystallized in a new crystal structure of [Ru₃(CO)₁₀(μ-dppa)] in the triclinic space group P1 , whereas that compound was described in an earlier report crystallizing from chloroform in the monoclinic space group P2₁/c.     

Facile Synthesis of MOF-derived Mn3O4@N-doped Carbon with Efficient Oxygen Reduction

Integration of MnO_x into the carbon matrix proves a viable strategy to improve the electrochemical performance of MnO_x materials. Mn₃O₄ nanoparticle-decorated N-doped carbon composites (Mn₃O₄@N-doped carbon) were facilely prepared from a non-porous eight-fold interpenetrated Zn^II-based MOF, which involves first synthesis of bimetallic Mn/Zn-MOF in one-pot reaction followed by direct pyrolysis at 1000 °C. In 0.1 m KOH solution, the optimal Mn₃O₄@N-doped carbon exhibits decent oxygen reduction activity with the onset potential (E_onset) of 0.94 V (vs. RHE) and half-wave potential (E_1/2) of 0.81 V (vs. RHE), excellent methanol tolerance as well as good durability.     

EMI shielding and dynamic mechanical analysis of graphene oxide-carbon nanotube-acrylonitrile butadiene styrene hybrid composites

Carbon nanomaterials such as carbon nanotubes (CNTs), graphene and their hybrid have been studied extensively. Despite having excellent properties of CNTs and graphene have not yet been fully realized in the polymer composites. During fabrication agglomeration of CNTs and restacking of graphene is a serious concern that results in the degradation of properties of nanomaterials into the final composites. To improve the dispersion of CNTs and restacking graphene, in the present research work, we focused on the hybridization of graphene oxide and CNTs. Multiwalled carbon nanotubes (MWCNTs), functionalized carbon nanotubes (FCNTs), and graphene oxide-carbon nanotubes (GCNTs) reinforced acrylonitrile butadiene styrene (ABS) composites were prepared separately by vacuum filtration followed by hot compression molding. Further, dynamic mechanical analysis (DMA), and electromagnetic interference (EMI) shielding properties of ABS composites reinforced carbon nanofillers were investigated. The dynamic mechanical properties of polymers strongly depend on the adhesion of fillers and polymer, entanglement density of polymer chains in the presence of carbon fillers. The dynamic mechanical characteristics such as storage, loss modulus, and damping factor of prepared composites were significantly affected by the incorporation of MWCNTs, FCNTs, and GCNTs. Maximum EMI shielding effectiveness of −49.6 dB was achieved for GCNT-ABS composites which were highest compared to MWCNTs-ABS composites (−38.6 dB) and FCNTs-ABS composites (−36.7 dB) in the Ku band (12.4–18 GHz). These results depict the great potential of GCNTs-ABS composites to be used in various applications of efficient heat dissipative EMI shielding materials for electronic devices.     

高碳铬铁在氢氧化钠水溶液中电化学氧化过程

铬铁电化学氧化法是一种新的制备铬酸钠的方法,然而高碳铬铁在NaOH水溶液中的电化学氧化过程尚不明确。 采用循环伏安法(CV)、稳态极化法(LSV)等电化学测试方法对金属铬、高碳铬铁在NaOH水溶液中的电化学氧化过程进行研究,通过扫描电子显微镜(SEM)、能量散射谱(EDS)和X射线光电子能谱(XPS)对高碳铬铁电解后固相产物表征,判断固相产物的组成。 结果表明,高碳铬铁不同于金属铬的电氧化过程,它在NaOH溶液中通过Cr(0)→Cr(Ⅵ)的电氧化方式生成铬酸钠,中间产物Cr(OH)₃和Fe(0)发生电化学反应生成稳定的FeCr₂O₄。 随着NaOH浓度的增加,电势较低时,受高碳铬铁中Fe(0)的影响,高碳铬铁容易在NaOH水溶液中发生钝化;当电势足够正时,钝化膜溶解,生成铬酸钠、氢氧化铁和亚铬酸亚铁,同时,阳极表面有氧气析出。 高碳铬铁电化学氧化制备铬酸钠的适宜条件:碱浓度≥2 mol/L,阳极电势≥1.6 V(vs.SCE)。     

烯丙基化碳纳米管改善丙烯酸酯压敏胶的性能

本文利用γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)对多壁碳纳米管(MWNTs)进行修饰使其表面接枝上烯丙基官能团,与丙烯酸酯类单体进行原位聚合,制备了一种耐高温丙烯酸酯压敏胶(PSA)。 通过傅里叶变换红外光谱仪(FT-IR)、热重分析仪(TGA)和扫描电子显微镜(SEM)表征了MWNTs和丙烯酸酯PSA的结构与性能,探讨了改性MWNTs的质量分数对PSA耐热性能和粘接性能的影响。 结果表明,与未改性的丙烯酸酯PSA相比,当改性MWNTs的质量分数为1.5%时,改性丙烯酸酯PSA的耐热性能和粘接性能最佳,热分解温度从360 ℃提高到了382 ℃,耐热温度从80 ℃提高到了155 ℃,初粘力、持粘力和180°剥离强度分别从2 h和13.66 N/(25 mm)(12号小球)提高到了27 h和17.34 N/(25 mm)(17号小球)。     

3kA钕电解槽流场中颗粒受力分析

近年来随着NdFeB永磁的应用发展,对金属Nd质量的要求越来越高,而电解过程碳颗粒运动及溶解对金属质量的影响至关重要。通过理论与数值模拟相结合的方式对流场中不溶于电解液的碳固体颗粒的主要受力类型进行梳理,对其运动轨迹进行数值模拟研究,针对稀土电解槽进行了颗粒-流场的计算及模拟,研究发现曳力及重力是颗粒在电解槽中起主要作用的力。曳力是改变颗粒运动轨迹的影响因素,且曳力随粒径的增大而增大。0.07 mm颗粒粒径是区分主要作用力是重力还是曳力的临界值,颗粒粒径越大,越不利于电解槽得到纯净的Nd单质。对进一步改进电解槽槽型,从而得到质量更好、杂质更少的稀土金属,并对后续各物理场对颗粒的影响提供参考意义。     

纳米银/二维石墨相氮化碳/还原氧化石墨烯复合材料的制备及其光催化降解抗生素

为优化石墨相氮化碳(g-C₃N₄)光催化剂的结构,改善其对污染物的降解性能,本文以三聚氰胺为前驱体,通过高温煅烧和热氧化剥离制备了二维石墨相氮化碳(2D-C₃N₄),并用光还原法一步合成纳米银/二维石墨相氮化碳/还原氧化石墨烯(Ag/2D-C₃N₄/rGO)复合光催化剂。通过X射线粉末衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、紫外-可见漫反射光谱(UV-Vis DRS)、光致发光光谱(PL)、X射线光电子能谱(XPS)、氮气吸附脱附等温曲线(BET)等对材料进行表征。 以头孢曲松钠为目标污染物,探究pH值、催化剂用量、头孢曲松钠初始浓度等因素对催化剂的吸附、降解性能的影响,并探究降解反应机理。 当pH=6.0,催化剂用量为0.3 g/L,头孢曲松钠初始浓度为10.0 mg/L时,复合材料对头孢曲松钠的降解率可达到89.1%。 催化剂的稳定性较强,具有实际应用价值,可用于处理含头孢类抗生素的废水。     

二次包覆法制备煤沥青基硅/碳复合物及其锂离子电池性能

本文采用市售纳米硅为硅源,以软化点低、得碳率高、价格便宜的煤沥青作为碳源,通过两步包覆法制备了煤沥青基硅/碳(Si/C/C)复合物,并研究其作为锂离子电池负极材料的电化学性能。 结果表明,所得复合物的粒径在300~350 nm间,Si纳米粒子被C包覆并相互连结成C-Si-C网络结构,其中Si含量为27%的硅/碳复合物(Si/C/C-27%)作为锂电池电极材料表现了良好的储锂性能。 在0.1 A/g的小电流密度下,Si/C/C-27%的放电比容量为1281 mA·h/g;在3 A/g的大电流密度下,其放电比容量仍能保持在582 mA·h/g,表现了良好的倍率性能。Si/C/C-27%在2 A/g的电流密度下经过100次的循环后其比容量保持率为76.61%,表现了良好的循环稳定性。 相比于煤沥青基碳的一次包覆所得的硅/碳复合材料(Si/C),Si/C/C有效提高了Si纳米粒子的导电性并抑制了其在嵌锂和脱锂过程中的体积膨胀。 本文提出的二次包覆的新方法为制备具有优异电化学性能的锂离子电池负极材料提供了新的研究思路。     

氮掺杂碳点的制备及其对阿莫西林高灵敏检测

以天然物质石斛为原料,一步水热法合成高荧光量子产率的氮掺杂碳点(NCDs),通过透射电子显微镜(TEM)、X射线光电子能谱(XPS)、傅里叶变换红外光谱(FT-IR)、紫外-可见光吸收图谱(UV-Vis)及荧光光谱(PL)对合成的NCDs进行表征。 实验结果显示合成的NCDs发强烈的蓝色荧光,呈现为球形或准球形,均匀分散,尺寸范围在1~5 nm;其表面含有丰富的COOH、OH和NH₂等水溶性基团,最佳激发和发射波长分别为350和435 nm,且具有良好的发光稳定性。 通过测定,合成的NCDs的荧光量子产率高达29.19%。在pH=7.4的缓冲溶液中测定不同物质对NCDs的荧光影响,相同条件下发现只有阿莫西林能够对NCDs荧光进行明显猝灭,表明合成的NCDs可选择性的识别阿莫西林,通过NCDs的荧光强度变化构建一种可灵敏检测阿莫西林的传感器,检测线性范围为2.6~30 μmol/L,检出限为0.15 μmol/L。     

无电沉积法AuNPs-MWCNTs的制备及其对黄酮类化合物的电化学催化性能研究

利用多壁碳纳米管具有较低的还原电位,以多壁碳纳米管作为还原剂和负载基底,通过无电沉积法制备了负载纳米金粒子的碳纳米管催化剂。此种材料具有更多的活性位点,避免了纳米金粒子表面保护剂的存在造成其催化活性降低的缺陷,发现其对典型黄酮类化合物-芦丁和黄芩苷具有良好的电化学催化性能和较高的灵敏度,并将其应用于电化学分析检测黄酮类化合物。