烧结温度和升温速率对Pb(Sb1/3Mn2/3)0.05Zr0.47Ti0.48O3压电陶瓷性能的影响

采用传统固相法制备了Pb(Sb1/3 Mn2/3)0.05Zr0.47Ti0.48 O3 (PMS-PZT)压电陶瓷.利用XRD、SEM和EDS等研究PMS-PZT陶瓷体系在烧结过程中形成的过渡液相和形成过渡液相温度(1100℃)附近的升温速率对陶瓷结构、压电和介电性能的影响.结果表明:不同烧结温度下,所有样品均为单一的钙钛矿四方相,过渡液相不会对相的结构有影响,但是当烧结温度较低时,过渡液相在烧结后期以玻璃相在晶界附近富集,对陶瓷的压电和介电性能有很大影响.随着烧结温度和升温速率的升高,PMS-PZT晶粒尺寸增大,晶粒均匀性和规则性得以改善,晶化质量得到提高;d33测试和阻抗分析测试结果表明PMS-PZT样品在1100℃附近以7 ℃·min-1升温速率并在1250℃烧结时具有最好的压电和介电性能:d33 =313 C/N,kp=0.59,Qm=1481,εr=1437,tanδ=0.53;.     

Laser polishing of additive manufactured Ti alloys

Laser-based additive manufacturing has attracted much attention as a promising 3D printing method for metallic components in recent years. However, surface roughness of additive manufactured components has been considered as a challenge to achieve high performance. In this work, we demonstrate the capability of fiber laser in polishing rough surface of additive manufactured Ti-based alloys as Ti-6Al-4V and TC11. Both as-received surface and laser-polished surfaces as well as cross-section subsurfaces were analyzed carefully by White-Light Interference, Confocal Microscope, Focus Ion Beam, Scanning Electron Microscopy, Energy Dispersive Spectrometer, and X-ray Diffraction. Results revealed that as-received Ti-based alloys with surface roughness more than 5 µm could be reduce to less than 1 µm through laser polishing process. Moreover, microstructure, microhardness and wear resistance of laser-polished zone was investigated in order to examine the thermal effect of laser polishing processing on the substrate of additive manufactured Ti alloys. This proof-of-concept process has the potential to effectively improve the surface roughness of additive manufactured metallic alloy by local polishing method without damage to the substrate.     

飞秒激光加工蓝宝石超衍射纳米结构

蓝宝石具有超强硬度及耐腐蚀、耐高温、在紫外-红外波段具有良好的透光性等优点,在军工业以及医疗器械方面具有广泛的应用前景.然而这些优点又对蓝宝石的机械加工或化学腐蚀加工带来困难.飞秒激光脉冲具有热损伤小、加工分辨率高、材料选择广等特点,被广泛应用于固体材料改性和高精度三维微纳器件加工.本文提出了利用飞秒激光多光子吸收特性在蓝宝石表面实现超越光学衍射极限的精细加工.利用聚焦后的波长为343 nm的飞秒激光,配合高精密三维压电位移台,实现激光焦点和蓝宝石晶体的相对三维移动,在蓝宝石晶体衬底上进行精确扫描,得到了线宽约61 nm的纳米线,纳米线间的最小间距达到142 nm左右.利用等离子体模型解释了加工得到的纳米条纹的产生原因,研究了激光功率、扫描速度对加工分辨率的影响.最终本工作实现了超越光学衍射极限的加工精度,为实现利用飞秒激光对高硬度材料的微纳结构制备提供了参考.     

100 GPa以上冲击压力区蓝宝石的近红外发光

采用三层夹心靶结构,利用铜箔与抛光蓝宝石之间良好的接触条件,使用辐射式高温计观测到c取向蓝宝石在130～172 GPa冲击高压下的红外辐射。实验信号显示,位于近红外波段的蓝宝石冲击辐射随着压力的增加而变强;强度对比显示,蓝宝石的近红外发射强于界面发射。基于冲击作用下滑移带的温度高于冲击平衡温度的概念,将蓝宝石体内滑移带温度作为蓝宝石发射温度代入线性吸收公式,从而将蓝宝石发光强度的增加和界面冷却引起的发光强度下降相结合;将得到的界面一蓝宝石发射强度数值模拟结果与实验结果相比较,发现二者能够重合。由实验信号的上升趋势得到三个压力下0.85μm近红外波长处蓝宝石的冲击吸收系数数值。     

Ag implantation-induced modification of Ni–Ti shape memory alloy thin films

Nanocrystalline thin films of Ni–Ti shape memory alloy are deposited on an Si substrate by the DC-magnetron co-sputtering technique and 120?keV Ag ions are implanted at different fluences. The thickness and composition of the pristine films are determined by Rutherford Backscattering Spectrometry (RBS). X-Ray diffraction (XRD), atomic force microscopy (AFM) and four-point probe resistivity methods have been used to study the structural, morphological and electrical transport properties. XRD analysis has revealed the existence of martensitic and austenite phases in the pristine film and also evidenced the structural changes in Ag-implanted Ni–Ti films at different fluences. AFM studies have revealed that surface roughness and grain size of Ni–Ti films have decreased with an increase in ion fluence. The modifications in the mechanical behaviour of implanted Ni–Ti films w.r.t pristine film is determined by using a Nano-indentation tester at room temperature. Higher hardness and the ratio of higher hardness (H) to elastic modulus (E_r) are observed for the film implanted at an optimized fluence of 9?×?10¹⁵ ions/cm². This improvement in mechanical behaviour could be understood in terms of grain refinement and dislocation induced by the Ag ion implantation in the Ni–Ti thin films.     

激光诱导Ti等离子体电子温度的实验研究

室温,常压下,利用Nd∶YAG脉冲激光器产生的波长为1 064 nm, 脉宽12 ns,能量分别180, 230和280 mJ的脉冲激光冲击Ti靶,使用中阶梯光栅光谱仪检测了三种激光能量下对应的光谱。调节延时器DG645的延迟时间,检测了延迟0～500 ns时间范围内Ti等离子体对应激光能量下的发射光谱,分析光谱,可以得到了九条不同的的TiⅠ 和TiⅡ等离子体谱线,证明在该实验条件下,Ti靶能够充分吸收能量电离且离子谱线具有不同的演化速率,利用Saha-Boltzmann法计算并分析Ti等离子体电子温度,实验结果表明：相同的延迟时间,激光能量越大,谱线相对强度越大,电子温度越高,谱线相对强度的变化量随激光能量的变化量增大而增大;在延时0～150 ns内,三种激光能量下的等离子体电子温度和谱线的相对强度都随延迟时间的增加而快速下降,其中280 mJ激光能量下的等离子体电子温度和谱线强度下降速率较快;在150～250 ns范围内,电子温度和谱线强度均随延迟时间的增加有一个缓慢的上升,180 mJ激光能量下的等离子体电子温度和谱线强度的上升速率较快。250～500 ns范围内,三种激光能量下的电子温度和谱线强度均随延迟时间的增加而缓慢下降。     

Pb(Zr,Sn,Ti)O3反铁电陶瓷的低温相变扩散与极化弛豫

用弱场介电温谱、热释电流谱、强场电滞回线和变温X射线衍射谱研究了微量La掺杂Pb(Zr ,Sn ,Ti)O3(PZST)反铁电 (AFEt)陶瓷在 - 10 0— 180℃温区内的结构与电学特性 .弱场介电温谱显示 ,AFEt陶瓷在低温段(- 10 0— 5 0℃ )呈现介电频率弥散 (0 1— 10 0kHz)和扩散型相变的特征 ,而变温X射线衍射谱却表明材料在这一温区内保持四方相结构 ;低温下经强场作用后 ,AFEt被诱导为亚稳三方铁电态 ,介电频率弥散消失 .基于多元复杂化合物的组分起伏理论 ,讨论了PZSTAFEt陶瓷的相变扩散与极化弛豫新现象 .     

Upconversion in Highly Doped Er3+-Yb3+ Fiber Pumped by Ti:Sapphire Laser at 800 nm

The up-conversion processes were investigated in highly doped Er3+-Yb3+ silica fiber pumped by CW or mode-locked Ti:Sapphire laser at 800 nm band. The mechanism is different from that at 980 nm pumped band. The pumping wavelength and power dependences of green, blue and red fluorescence emission were obtained. The up-conversion efficiencies of different doped concentration were investigated. The strong infrared emissions, which limit the efficiency of up-conversion were observed.     

Design of the Seed Source for High Power KrF Excimer Laser System

１ＩｎｔｒｏｄｕｃｔｉｏｎＥｘｃｉｍｅｒｌａｓｅｒｓａｒｅｔｈｅｐｕｌｓｅｄｇａｓｌａｓｅｒｗｈｉｃｈｏｐｅｒａｔｅａｔａｎｕｍｂｅｒｏｆｆｉｘｅｄｗａｖｅｌｅｎｇｔｈｓｉｎｔｈｅｒｅｇｉｏｎｏｆｕｌｔｒａｖｉｏｌｅｔ．Ｈｏｗｅｖｅｒ,ｉｔｓｐｕｌｓ...     

良性前列腺增生组织对钛宝石激光的吸收和散射特性

研究了经尿道等离子体双极电切除术(PKRP)切除和经尿道前列腺电切术(TURP)切除的前列腺增生(BPH)组织对640, 660, 680, 700, 720, 740, 760, 780, 800, 820, 840, 860和880 nm波长的钛宝石激光的光学特性及其差异,实验采用双积分球测量系统以及反向倍增法获取BPH组织的吸收和散射特性参数。结果表明：PKRP和TURP切除的BPH组织对这1３个不同波长的激光的吸收系数和约化散射系数都是随着激光波长增大而明显减小的,PKRP切除的BPH组织对这同一波长的激光的吸收系数和约化散射系数都明显较TURP切除的BPH组织对相应的波长的激光的吸收系数和约化散射系数要小,PKRP和TURP切除的BPH组织的吸收系数以及约化散射系数的最大值都在640 nm,其值分别为(0.885±0.022)和(0.955±0.024)mm-1以及(1.564±0.039)和(1.658±0.042)mm-1,其差异分别为7.91%以及6.01%,其最小值都在880 nm,其值分别为(0.443±0.011)和(0.455±0.011)mm-1以及(1.117±0.028)和(1.197±0.030)mm-1,其差异分别为2.71%以及7.16%。PKRP和TURP切除的BPH组织对660 nm的吸收系数的差异最大,其值为8.95%,其差异最小在860 nm,其值为1.75%,PKRP和TURP切除的BPH组织对800 nm的约化散射系数的差异最大,其值为9.13%,其差异最小在640 nm,其值为6.01%。