Electrolytical production of Ni + Mo + Si composite coatings with enhanced content of Si

Ni + Mo + Si composite coatings were prepared by co-deposition of nickel with molybdenum and silicon powders from a nickel solution in which Mo and Si particles were suspended by stirring. The layers have been deposited on a carbon steel substrate (St3S) under galvanostatic conditions. The content of Si in deposited layers was about 2-5 wt.% depending on deposition current density and the value of electric charge. For comparison Ni + Mo composite coatings were obtained under analogous current conditions. Composite coatings of enhanced Si content (15 wt.%) were deposited from an electrolyte in which 40 g/dm³ of Si covered with electroless plated nickel was dispersed. Deposition current density was equal 0.1 A/cm² and the value of electric charge Q = 500 C/cm². The thickness of the coatings was about 100-300 μm depending on their kind, electric charge and the deposition current density. Surface and cross-section morphology were investigated by scanning electron microscope (SEM). All deposited coatings are characterized by great, developed surface area. No internal stresses causing their cracking were observed. Chemical composition of the layers was determined by X-ray fluorescence spectroscopy (XRF) method and quantitative X-ray analysis (QXRD). It was stated, that the content of molybdenum and silicon in Ni + Mo + Si coatings depends on deposition current density and the amount of the powder in bath. The results of structural investigation of the obtained layers by the X-ray diffraction (XRD) method show, that they consist in crystalline Mo or Mo and Si phases built into Ni matrix. Moreover, Ni + Mo + Si composite coatings were modified by thermal treatment. It has been found that the thermal treatment of Ni + Mo + Si composite coatings caused that the new phases (NiSi, Mo₂Ni₃Si and Ni₆Mo₆C_1.06) were obtained.     

Fabrication and characterization of sputtered titanium dioxide films

TiO₂ thin films were prepared under various conditions by using a reactive RF sputtering technique. The structural, optical and electrical characteristics of the films have been investigated. All as-deposited films were amorphous. After annealing at T > 673 K, the crystallinity of the observed tetragonal anatase phase appeared improved. The optical band gap, determined by using Tauc plot, has been found to amount to 3.38 ± 0.03 and 3.21 ± 0.03 eV for the direct and indirect transition, respectively. Also the complex optical constants for the wavelength range 300-2500 nm are reported. Using the two-point probe technique, the dark resistivity has been measured as a function of the film thickness, d. The resistivity, ρ, of the samples has been found to decrease markedly with increasing thickness, but only for d < 100 nm. The behaviour of ρd versus d was found to fit properly with the Fuchs and Sondheimer relation with parameters ρ_o = 4.95 × 10⁶ Ω cm and mean free path, l = 310 ± 2 nm. The log ρ versus 1/T curves show three distinct regions with values for the activation energy of 0.03 ± 0.01, 0.17 ± 0.01 and 0.50 ± 0.02 eV, respectively.     

The epitaxial sexiphenyl (0 0 1) monolayer on TiO2(1 1 0): A grazing incidence X-ray diffraction study

A para-sexiphenyl monolayer of near up-right standing molecules (nominal thickness of 30 Å) is investigated in-situ by X-ray diffraction using synchrotron radiation and ex-situ by atomic force microscopy. A terrace like morphology is observed, the step height between the terraces is approximately one molecular length. The monolayer terraces, larger than 20 μm in size, are extended along the [0 0 1] direction of the TiO₂(1 1 0) substrate i.e. along the Ti-O rows of the reconstructed substrate surface. The structure of the monolayer and its epitaxial relationship to the substrate is determined by grazing incidence X-ray diffraction. Extremely sharp diffraction peaks reveal high crystalline order within the monolayer, which was found to have the bulk structure of sexiphenyl. The monolayer terraces are epitaxially oriented with the (0 0 1) plane parallel to the substrate surface (out-of-plane order). Four epitaxial relationships are observed. This in-plane alignment is determined by the arrangement of the terminal phenyl rings of the sexiphenyl molecules parallel to the oxygen rows of the substrate.     

Correlated and non-correlated growth kinetics of pentacene in the sub-monolayer regime

We present a study of the growth kinetics of pentacene monolayer islands on SiO₂ in the submonolayer regime by using Atomic Force Microscopy (AFM). Two distinct growth modes, namely correlated growth (CG) and non-correlated growth (NCG), have been identified by Voronoi tesselation. These two modes are characterized by different island growth kinetics. In the case of correlated growth, the average island size 〈A〉 scales with deposition time t i.e. 〈A〉 ∝ t whereas for non-correlated growth, 〈A〉 ∝ t². The CG and NCG regimes are defined by the level of re-evaporation which determines the capture zones around the islands: Wigner-Seitz cells for CG and coronas of width λ_D (λ_D is the mean diffusion distance on SiO₂ before re-evaporation) for NCG. A simple model is proposed to reproduce the experimental growth kinetics in both modes.     

Probing antiferromagnetic order with heat capacity in exchange-biased structures

We explore the magnetic heat capacity in exchange-biased ferromagnet/antiferromagnet bilayers theoretically. We show that changes in the antiferromagnetic structure due to the reversal of the ferromagnet layer can be detected by distinct features in the heat capacity. This offers a method for probing antiferromagnetic domains in exchange-biased systems.     

Au/SiO2纳米多层薄膜的制备及其性质表征

利用多靶磁控溅射技术制备了Au/SiO₂纳米颗粒分散氧化物多层复合薄膜.研究了在保持Au单层颗粒膜沉积时间一定时薄膜厚度一定、变化SiO₂的沉积时间及SiO₂的沉积时间一定而改变薄膜厚度时，多层薄膜在薄膜厚度方向的微观结构对吸收光谱的影响.研究结果表明：具有纳米层状结构的Au/SiO₂多层薄膜在560 nm波长附近有明显的表面等离子共振吸收峰，吸收峰的强度随Au颗粒的浓度增加而增强，在Au颗粒浓度相同的情况下，复合薄膜 关键词： 2纳米复合薄膜')" href="#">Au/SiO₂纳米复合薄膜 多靶磁控溅射 吸收光谱 有效介质理论     

基于超分子结构共掺杂纳米复合薄膜的制备与荧光特性

为改善功能分了的特性,提出一种基于金属纳米粒子-偶氮染料复合物共掺杂超分子结构功能材料的设计新方法.并依照此方法制备出复合材料,观测了其显微结构,测量了其紫外-可见光吸收,研究了该超分子结构复合体系的荧光特性.实验发现,由于金属银纳米粒子的掺杂,使得超分子结构复合体系中功能分子甲基橙在溶液态体系的荧光强度增强近5倍,而在两种不同结构(共混结构和包覆结构)的薄膜态超分子结构体系中,其荧光强度分别被猝灭15%和20%.研究结果表明,复合膜中采用超分子结构完全能够改善功能分子的特性.     

射频磁控溅射法制备薄膜电池电极的计算机模拟初步

计算机模拟仿真射频磁控溅射实验制备薄膜及离于电池电极,研究了在特定实验条件下薄膜的生长过程,并分析了影响薄膜生长的部分因素。