The structure of monolayer SiO2 on Mo(1 1 2): A 2-D [Si-O-Si] network or isolated [SiO4] units?

In this letter, atomically resolved scanning tunneling microscopic (STM) images obtained from monolayer SiO₂/Mo(1 1 2) are presented. The results are consistent with a previously proposed structural model of isolated [SiO₄] units based on vibrational features observed by high-resolution electron energy loss spectroscopy (HREELS) and infrared reflection-absorption spectroscopy (IRAS), and oxygen species identified by ultra-violet photoemission spectroscopy (UPS). These results are inconsistent with a structural model that assumes a two-dimensional (2-D) [Si-O-Si] network. These data illustrate that a metal substrate, although coated with an oxide thin layer, can be directly imaged at the atomic-scale with STM.     

Controlled structure and density of “living” polystyrene brushes on flat silica surfaces

Thin layers of polystyrene were grown from surface-grafted nitroxide initiators via controlled “living” free radical polymerization. The “reactive” Langmuir-Blodgett deposition method allowed an effective control of the initiator layer density leading to PS brushes with different and high grafting density and stretching. The influence of the grafting density on the layer structure was studied. Comparison with theoretical predictions for monodispersed brushes in bad solvent was discussed. The thickness was found to vary linearly with molecular weight and the density dependence was shown using wetting measurements. Special features of controlled radical nitroxide polymerization from a surface were discussed. A direct comparison of the molecular weight and polydispersity between surface and bulk polymers was made by de-grafting the brushes into a toluene/HF solution. Finally, some evidence of a “surface Fischer” effect was shown from re-initiated layers. Received 20 December 2001     

Magnetic properties of the Cr(0 0 1) surface studied by spin-polarized scanning tunneling spectroscopy

The magnetic properties of the Cr(0 0 1) surface have been studied by spin-polarized scanning tunneling spectroscopy (SP-STS). Spatially resolved mapping of the spectroscopic dI/dU signal at an energy close to the spin-polarized Cr(0 0 1) surface state allows the confirmation of the topological antiferromagnetic order of the Cr(0 0 1) surface. It is shown that the presence of screw dislocations leads to the formation of domain walls which exhibit a width of 120–170 nm. A long-period modulation of the SP-STS signal was not observed indicating that the bulk spin-density wave is modified at the surface due to symmetry breaking.     

Site segregation in size-mismatched nanoalloys: Application to Cu-Ag

In order to determine the energetic driving forces for surface segregation in bimetallic clusters, we use a combined approach coupling numerical simulations within an N-body interatomic potential and a lattice-gas model. This approach, which has been used successfully to study both the superficial segregation in semi-infinite alloys and the intergranular segregation, allows us to determine the relative contributions of the three elementary driving forces for the different sites of the cluster surface (vertices, edges and facets) in both dilute limits for the Cu-Ag system. We show that the segregation hierarchy based on broken-bond arguments (preferential segregation to the vertex sites, less to edge sites, and least to facet sites) is not at all universal. In particular, unusual hierarchies are predicted when the sizes of the constituents are strongly different. Furthermore, we compare the segregation driving forces for cubo-octahedral and icosahedral clusters. They are similar for the vertex sites and edge sites, whereas they differ significantly for the sites of the triangular facets. The segregation of the species with the largest atomic radius (Ag) is indeed largely enhanced in the icosahedral structure due to dilations of the orthoradial distances.     

改进形态学相关算法以识别高相似度灰度图像

从形态学角度定义了灰度联合图像相似度，提出两种基于位表示法形态学相关算法的改进算法，通过提取位表示法的图像片边缘特征或二元化位表示法的图像片功率谱，以提高位表示法形态学相关算法对高相似度灰度图像的识别能力。     

生长温度对磁控溅射ZnO薄膜的结晶特性和光学性能的影响

采用反应射频磁控溅射方法，在Si (100) 基片上制备了具有高c轴择优取向的ZnO薄膜.利用 原子力显微镜、透射电子显微镜、X射线衍射分析、拉曼光谱等表征技术，研究了沉积温度 对ZnO薄膜的表面形貌、晶粒尺度、应力状态等结晶性能的影响；通过沉积温度对透射光谱 和光致荧光光谱的影响，探讨了ZnO薄膜的结晶特性与光学性能之间的关系.研究结果显示， 在室温至500℃的范围内，ZnO薄膜的晶粒尺寸随沉积温度的增加而增加，在沉积温度为500 ℃时达到最大；当沉积温度为750℃时，ZnO薄膜的晶粒尺度有所减小；在室温至750℃的范 围内，薄膜中ZnO晶粒与Si基体之间均存在着相对固定的外延关系；在沉积温度低于500℃时 ，制备的ZnO薄膜处于压应变状态，而750℃时沉积的薄膜表现为张应变状态.沉积温度的不 同导致ZnO薄膜的折射率、消光系数、光学禁带宽度以及光致荧光特性的变化，沉积温度对 紫外光致荧光特性起着决定性的作用.此外，探讨了影响薄膜近紫外光致荧光发射的可能因 素. 关键词： ZnO薄膜 表面形貌 微观结构 光学常数     

Surface free energy of CrNx films deposited using closed field unbalanced magnetron sputtering

CrN_x thin films have attracted much attention for semiconductor IC packaging molding dies and forming tools due to their excellent hardness, thermal stability and non-sticking properties (low surface free energy). However, few data has been published on the surface free energy (SFE) of CrN_x films at temperatures in the range 20-170 °C. In this study CrN_x thin films with CrN, Cr(N), Cr₂N (and mixture of these phases) were prepared using closed field unbalanced magnetron sputtering at a wide range of Cr⁺² emission intensity. The contact angles of water, di-iodomethane and ethylene glycol on the coated surfaces were measured at temperatures in the range 20-170 °C using a Dataphysics OCA-20 contact angle analyzer. The surface free energy of the CrN_x films and their components (e.g., dispersion, polar) were calculated using the Owens-Wendt geometric mean approach. The influences of CrN_x film surface roughness and microstructure on the surface free energy were investigated by atomic force microscopy (AFM) and X-ray diffraction (XRD), respectively. The experimental results showed that the lowest total SFE was obtained corresponding to CrN at temperature in 20 °C. This is lower than that of Cr(N), Cr₂N (and mixture of these phases). The total SFE, dispersive SFE and polar SFE of CrN_x films decreased with increasing surface temperature. The film roughness has an obvious effect on the SFE and there is tendency for the SFE to increase with increasing film surface roughness.     

Laser ablation lithography on thermoelectric semiconductor

In this paper, experimental results of the investigation of the periodic structure on thermoelectric semiconductor Cu₂Se are presented. Periodic structures were formed on surfaces of semiconductors due to multi-beam interaction of Q-switched Nd:YAG laser, which was operated in the lowest order of Gaussian mode and pulse duration 7 ns. Surface temperature evolution and transient reflectivity are studied during laser treatment. Creation of Cu islands in the maximal intensity of interference pattern was found.     

Continuous peeling extrusion of SEBS block copolymers

During continuous peeling, a central polymer rod free of visible defects was continuously extruded while being peeled at the die exit. Continuous peeling can occur at flow rates orders of magnitude higher than those at which initial surface cracking is observed. Thus, if continuous peeling can be controlled it may have potential industrial applications. The aim of this work was to study how different extrusion parameters (temperature, flow rate, die length and diameter) affect the presence of continuous peeling. The melt exiting the die has been filmed to link physical measurements and observations and to determine whether or not continuous peeling is present. Different criteria have been considered to represent the extrusion conditions under which continuous peeling may occur. Surface tension criteria can be used to try to predict the appearance and disappearance of continuous peeling. A correlation formula is also proposed for the rod diameter in terms of surface tension. Our results show that the ratio of the rod diameter to the die diameter is approximately 25% greater in the case of short-orifice dies (L/D ≈ 0) than for long capillaries (L/D ≈ 10). The correlations obtained allow analysis and discussion of flow regimes for possible applications.     

Validation of an optimization procedure to improve low frequency characteristics of rooms

A set of experiments was carried out to validate an optimization procedure based on finite element method (FEM). The idea of the procedure, fully presented in previous edition of this journal [Zhu X, Zhu Z, Cheng J. Using optimized surface modifications to improve low frequency response in a room. Appl Acoust 2004;65:841-60], is to produce an optimal geometry modification on the wall for improving low frequency sound uniformity in small rooms. Four experimental models were set up with a scale of 1:5. One was modified according to the optimized result and the others were treated with no optimization consideration. Measured frequency responses of four rooms were compared with numerical results calculated by FEM models. The transient responses in these rooms were also measured and analyzed. The agreements between calculation and measurement are satisfactory though the discrepancies due to the uncertainty of acoustic behavior of the room boundaries remain. The optimization procedure has been supported by the results that the optimized room produces the flattest frequency response and also the most smooth energy decay within the frequency range studied. The reductions of response fluctuation have reached 4.3 dB for prediction and 2.6 dB for measurement, respectively.