Preparation of TiO2 Sol Using TiCl4 as a Precursor

A titanium dioxide sol with narrow particle size distribution was synthesized using TiCl₄ as the starting material. The sol was prepared by a process where HCl was added to a gel of hydrated titanium oxide to dissolve it. The resulting aqueous titanic acid solution was heated to form titanium dioxide sol. The effects of preparation parameters were investigated. TiCl₄ was slowly added to distilled water at 5°C. Aqueous solution of sodium hydroxide was added to adjust the pH of the system to 8–12. After aging for a period of time, the peptized sol was filtered and sufficiently washed. The filtered cake was repulped in water. Hydrochloric acid was slowly added to the solution with stirring. After condensation reaction and crystallization, a transparent sol with suspended TiO₂ was formed. XRD results show that the crystalline phase was anatase. The suspended TiO₂ particles were rhombus primary particles with the major axis ca. 20 nm and the minor axis ca. 5 nm. The TiO₂ particles prepared at pH 8 had the largest surface area of 141 cm³/g and it was microporous. The compositions of the solution which yielded the smallest suspended TiO₂ particles were TiO₂:HCl (35% HCl) = 1:1 (molar ratio), concentration of TiO₂ = 10%. Hydroxypropyl cellulose with viscosity of 150–400 cps was added as a dispersant. The sol was excellent in dispersibility and long-term stability. Transparent thin films could be obtained through dip-coating glass substrate in the sol. The dip-coating on glass can be less than three times to have one monolayer TiO₂. The transparent TiO₂ thin film had strong hydrophilicity after being illuminated by UV light.     

CZE separations of basic proteins at low pH in fused silica capillaries with surfaces modified by silane derivatization and/or adsorption of polar polymers

Mixtures of several basic proteins have been used to test CZE capillaries with surfaces modified by new pretreatment procedures; the performance obtained has been compared with that achieved using capillaries treated by procedures described in the literature. It has been shown that addition of non-ionic polyvinylalcohols (PVA) to CZE buffer solutions deactivates even bare, i.e. untreated, fused silica surfaces and renders them suitable for separations of basic proteins. The performance obtained from such surfaces was comparable with that of capillaries modified by the more elaborate procedures of etching, silanol derivatization, and/or adsorptive coating (again with polymers). A home-made device is described which enables derivatization and coating reactions to be performed on fused silica capillaries under an inert atmosphere, i.e. one free from oxygen and water.     

环氧丙烯酸酯的紫外光固化

制备了适于配制紫外光固化涂料的环氧丙烯酸酯，研究了反应温度、阻聚剂、催化剂等因素对环氧树脂与丙烯酸反应的影响；讨论了反应机理和动力学；并利用红外光谱观察了产物的紫外光固化行为。季铵盐能有效地催化环氧树脂和丙烯酸的反应，当其用量为０．６％～１．２％时，在９０～１１０℃反应４．５～８小时后，环氧基转化率大于９７％。由此配制的光固化涂料经紫外光辐照能快速固化。     

Identification of radicals spin-trapped in autoxidized linoleic acids: A high performance liquid chromatography and electron spin resonance study

Radicals generated in linoleic acid and deuterated linoleic acid have been trapped by the spin trap 2-methyl-2-nitroso-propane (MNP) and identified by electron spin resonance (ESR) and ENDOR spectroscopy. The formation of two distinct secondary alkyl radical adducts (one conjugated, the other non-conjugated, as shown by their UV absorption spectra) was demonstrated by 11, 11-dideuterio-9-cis-12-cis-linoleic acid using HPLC and ESR spectroscopy.     

Surface and interface characterization of polyester‐based polyurethane/nano‐silica composites

Polyester‐based polyurethane/nanosilica composites were prepared via in situ polymerization and investigated by contact angle measurement, transmission electron microscopy (TEM), atomic force microscopy (AFM) and peel testing in an Instron testing machine. The contact angle and surface free energy results show that nanosilica tended to enrich at the interface between nanocomposite polymers and the substrates, TEM indicated that nanosilica particles were evenly dispersed in the bulk and AFM demonstrated that nanoparticles were located at both the surfaces and interfaces of nanocomposite polymers and that the roughness of both the surfaces and interfaces had a decreasing tendency as the nanosilica content increased, as did the adhesion strength between the nanocomposite polymers and substrates. Copyright © 2003 John Wiley & Sons, Ltd.     

The Role of Binary and Many-centre Molecular Interactions in Spin Crossover in the Solid State. Part I. Equation for Free Energy

Summary. A formalism has been developed that describes spin crossover equilibrium in the solid state by taking into account the effects of n nearest neighbours of a given molecule on its partition function. In this way binary and many-body interactions of the order n + 1 are included into the theoretical model and represented by non-ideality parameters connected with the splitting of free energy levels. Binary interactions are characterised by the main splittings whereas higher order interactions manifest themselves in asymmetries of splittings within multiplets. The contribution of molecular interactions can also be written in terms of formal excess free energies of the second, third, fourth and higher orders. Simple relationships between excess free energies and parameters of multiplets have been found for binary, ternary and quaternary interactions. This formalism is reduced to that of the model of binary interactions when effects of surroundings are additive leading to equidistant free energy multiplets. Higher order interactions may cause an abrupt spin crossover but in a limited range of compositions around the transition point. The regression of experimental transition curves of one-step spin crossover may yield estimates of excess energies up to the fifth order.     

Control of optical properties of gel-derived oxide coating films containing fine metal particles

Control of the optical properties of gel-derived oxide films containing fine metal particles is described. The duration of the aging of Si(OC₂H₅)₄-derived sols and the amount of water for hydrolyzing Si(OC₂H₅)₄ were found to greatly affect the size and the shape of Au particles formed in the silica matrix, and accordingly the optical absorption of the Au/SiO₂ composite films. Employing dielectric media with high refractive indices like TiO₂ was shown to shift the absorption peak of Au particles to longer wavelengths. Pd/TiO₂ and Pt/TiO₂ composite films showed absorption in the visible region.     

Topographical properties of polymer films deposited in capillaries for electrophoretic separations of large organic molecules

Topography and thickness of hydrophilic polymer coatings of fused-silica capillaries for capillary electrophoresis (CE) were investigated using atomic force microscopy (AFM), scanning electron microscopy (SEM), and profilometry. Three hydrogels, poly(2-hydroxyethyl methacrylate) [poly(HEMA)], poly(diethylene glycol monomethacrylate) [poly(DEGMA)], and poly(triethylene glycol monomethacrylate) [poly(TEGMA)], were deposited using two procedures, either by simple physical sorption of the polymers, or by derivatization of the capillary wall surface with glycidyl methacrylate (EPMA) followed by polymerization of the appropriate monomers. The performance of the modified capillaries was tested under CE conditions (decrease in the electroosmotic flow, EOF dependence on pH, separation of milk and standard proteins). It has been found that the most important property of the polymer coating is its thickness, whereas its topography and the degree of its hydrophobicity are less significant. Film deposition by physical adsorption is preferable to polymerization on the derivatized surface.     

Physicochemical characterization of biological glass coatings

Metallic implants are widely used in orthopaedic surgery but metal release has been reported by several authors. High metallic ion concentration in surrounding tissues may play a major role in therapeutic failure. We have investigated in vivo and in vitro two biological glasses (BVA and BVH) used as coatings of metal implants. Physicochemical characterization was made by several complementary methods, particularly particle induced x‐ray emission (PIXE) and energy‐dispersive x‐ray spectroscopy (EDXS) associated with electronic microscopy. Analyses clearly show the differences of behaviour between both glasses. The BVA glass is bioactive, i.e. it develops a direct chemical bond between prosthesis and bone by the formation of a calcium phosphate layer at its surface. These structural and compositional modifications are caused by hydrolysis of the glass. After its dissolution BVA glass is replaced by bone, which ensures better integration of the implant in the bone site. The BVH glass is not bioactive and is used as a cement to isolate the metal implant from the biological environment, but the coating disaggregates with implantation time and glass grains migrate through the bony lacuna network. Copyright © 2003 John Wiley & Sons, Ltd.     

Inhibition of Pb-Leaching from Lead Crystal Glass by Coating with Films Prepared by the Sol-Gel Method

The chemical durability of lead glass tumblers (24% PbO) in a 4% (v/v) acetic acid solution before and after coating with sol-gel derived SiO2 films was assessed to determine the extent of reduction in Pb-leaching that can be achieved. It was found that by coating the internal surface of the glass tumblers with 1 ml of 10% TEOS solutions at 100°C and densifying the coating formed at 500°C for 1 h, it was possible to reduce Pb-leaching to about one quarter of that of the uncoated glass.