Surface and interface characterization of polyester‐based polyurethane/nano‐silica composites

Polyester‐based polyurethane/nanosilica composites were prepared via in situ polymerization and investigated by contact angle measurement, transmission electron microscopy (TEM), atomic force microscopy (AFM) and peel testing in an Instron testing machine. The contact angle and surface free energy results show that nanosilica tended to enrich at the interface between nanocomposite polymers and the substrates, TEM indicated that nanosilica particles were evenly dispersed in the bulk and AFM demonstrated that nanoparticles were located at both the surfaces and interfaces of nanocomposite polymers and that the roughness of both the surfaces and interfaces had a decreasing tendency as the nanosilica content increased, as did the adhesion strength between the nanocomposite polymers and substrates. Copyright © 2003 John Wiley & Sons, Ltd.     

Control of optical properties of gel-derived oxide coating films containing fine metal particles

Control of the optical properties of gel-derived oxide films containing fine metal particles is described. The duration of the aging of Si(OC₂H₅)₄-derived sols and the amount of water for hydrolyzing Si(OC₂H₅)₄ were found to greatly affect the size and the shape of Au particles formed in the silica matrix, and accordingly the optical absorption of the Au/SiO₂ composite films. Employing dielectric media with high refractive indices like TiO₂ was shown to shift the absorption peak of Au particles to longer wavelengths. Pd/TiO₂ and Pt/TiO₂ composite films showed absorption in the visible region.     

Topographical properties of polymer films deposited in capillaries for electrophoretic separations of large organic molecules

Topography and thickness of hydrophilic polymer coatings of fused-silica capillaries for capillary electrophoresis (CE) were investigated using atomic force microscopy (AFM), scanning electron microscopy (SEM), and profilometry. Three hydrogels, poly(2-hydroxyethyl methacrylate) [poly(HEMA)], poly(diethylene glycol monomethacrylate) [poly(DEGMA)], and poly(triethylene glycol monomethacrylate) [poly(TEGMA)], were deposited using two procedures, either by simple physical sorption of the polymers, or by derivatization of the capillary wall surface with glycidyl methacrylate (EPMA) followed by polymerization of the appropriate monomers. The performance of the modified capillaries was tested under CE conditions (decrease in the electroosmotic flow, EOF dependence on pH, separation of milk and standard proteins). It has been found that the most important property of the polymer coating is its thickness, whereas its topography and the degree of its hydrophobicity are less significant. Film deposition by physical adsorption is preferable to polymerization on the derivatized surface.     

Physicochemical characterization of biological glass coatings

Metallic implants are widely used in orthopaedic surgery but metal release has been reported by several authors. High metallic ion concentration in surrounding tissues may play a major role in therapeutic failure. We have investigated in vivo and in vitro two biological glasses (BVA and BVH) used as coatings of metal implants. Physicochemical characterization was made by several complementary methods, particularly particle induced x‐ray emission (PIXE) and energy‐dispersive x‐ray spectroscopy (EDXS) associated with electronic microscopy. Analyses clearly show the differences of behaviour between both glasses. The BVA glass is bioactive, i.e. it develops a direct chemical bond between prosthesis and bone by the formation of a calcium phosphate layer at its surface. These structural and compositional modifications are caused by hydrolysis of the glass. After its dissolution BVA glass is replaced by bone, which ensures better integration of the implant in the bone site. The BVH glass is not bioactive and is used as a cement to isolate the metal implant from the biological environment, but the coating disaggregates with implantation time and glass grains migrate through the bony lacuna network. Copyright © 2003 John Wiley & Sons, Ltd.     

Inhibition of Pb-Leaching from Lead Crystal Glass by Coating with Films Prepared by the Sol-Gel Method

The chemical durability of lead glass tumblers (24% PbO) in a 4% (v/v) acetic acid solution before and after coating with sol-gel derived SiO2 films was assessed to determine the extent of reduction in Pb-leaching that can be achieved. It was found that by coating the internal surface of the glass tumblers with 1 ml of 10% TEOS solutions at 100°C and densifying the coating formed at 500°C for 1 h, it was possible to reduce Pb-leaching to about one quarter of that of the uncoated glass.     

Coating and water permeation properties of SiO2 thin films prepared by the sol-gel method on nylon-6 substrates

Nylon-6 substrates were coated with SiO₂ thin films by the sol-gel method and their water permeability coefficient was evaluated. Methyltriethoxysilane (MTES) and tetraethoxysilane (TEOS) were used as starting materials. The addition of MTES to TEOS has enabled the formation of crack-free thin films on the substrates. The thin films strongly adhered to the substrates. The water permeability coefficients of nylon-6 substrates coated with these thin films decreased with the increase in the ratio of TEOS to the total alkoxides. The pretreatment of the nylon-6 substrates with -aminopropyltriethoxysilane was found to be effective to suppress the water permeability. The water permeability was suppressed by about 40% under the optimal condition.     

镀液中Ce^3＋离子对锡镀层结构缺陷和可焊性的影响

应用荧光分析法、X光电子能谱法(XPS)及正电子湮没寿命谱法(PALS)等研究了从含硫酸铈添加剂的酸性光亮锡镀液获得的锡镀层结构缺陷与可焊性的关系。结果表明,电镀时Ce与Sn不发生共沉积,Ce~(3+)的主要作用是阻化Sn~(2+)的水解和氧化使镀液稳定,因而使锡镀层纯度提高、结构致密、表层氧含量减少,有利于提高镀层的可焊性。当Ce~(3+)浓度控制在3.5g/L左右时,可使镀层结构缺陷较少,可焊性较佳,说明结构缺陷是影响锡镀层可焊性的直接原因。     

Printed plastic electronics and paperlike displays

Plastic electronic materials and high‐resolution printing methods may be important technologies for new classes of consumer electronic devices that are lightweight, mechanically flexible and bendable, and that can cover large areas at low cost. This article summarizes some of our recent work in this area. It focuses on the materials and patterning techniques that we used to produce plastic active‐matrix backplane circuits for a type of paperlike display. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3327–3334, 2002     

Metal Oxide Thin Films Containing Au Nano-Particles Prepared with Gas Diffusion Method

Au particles dispersed thin metal oxide films were prepared from precursor films containing HAuCl₄ with H₂S gas diffusion method. HAuCl₄ was uniformly dissolved in the films as promoted by hydroxypropyl cellulose (HPC). The mechanism of the Au particle formation was studied. It was found that HAuCl₄ was converted directly to Au metal particles upon contacting with H₂S gas. Au particles generated by this method were characterized with small particle size, sharp size distribution and high volume fraction in the films. The surface plasma resonance absorption of Au particles shifted to longer wavelength when TiO₂ component was introduced in the matrix.     

羧基丙烯酸酯涂料合成及其防雾性能研究

采用种子乳液聚合法合成了一种互穿网络型羧基丙烯酸酯类聚物乳液，研究了加料方式对羧基分布的影响，结果表明丙烯酸加入到核单体中有利于羧基分布在乳胶粒表面。在体系中引入离子键交联结构提高了乳液涂料的硬度和耐水性能，离子键交联ＰＩＬＮ型涂料具有优良的防雾性能。