New quaternary carbon and nitrogen stabilized polyborides: REB15.5CN (RE: Sc, Y, Ho, Er, Tm, Lu), crystal structure and compound formation

A new family of quaternary carbon and nitrogen containing Rare Earth (RE: Sc, Y, Ho, Er, Tm and Lu) borides: REB_15.5CN, has been synthesized and structurally characterized by powder X-ray diffraction data. They are all isotypic with Sc_1−xB_15.5CN whose structure was solved based on single-crystal X-ray data and HRTEM investigations. The structure refinement converged at a R(F²) value of 0.044 for 364 reflections. The new structure type of Sc_1−xB_15.5CN is composed of a three-dimensional network based on interconnected slabs of boron (B₁₂)^ico icosahedra and (B₆)^oct octahedra. A linear [CBC] chain and nitrogen tightly bridges icosahedra. Sc partially occupies voids in the sheets of boron octahedra. It crystallizes with the trigonal space group P³m1, with Z=2. Lattice parameters (nm) are as follows: for RE: Sc, a,b=0.5568(4), c=1.0756(2); Y, a,b=0.55919(6), c=1.0873(2); Ho, a,b=0.55883(7), c=1.0878(6); Er, a,b=0.55889(5), c=1.0880(6); Tm, a,b=0.5580(1), c=1.0850(6); Lu, a,b=0.55771(9), c=1.0839(4). Magnetic characterization of ErB₁₇C_1.3N_0.6 has been performed.     

Incorporation of rare-earth ions in Mg-Al layered double hydroxides: intercalation with an [Eu(EDTA)] chelate

Reaction of an aqueous slurry of an Mg₂Al-NO₃ layered double hydroxide with a four-fold excess of Na[Eu(EDTA)] gives a material which analyses for Mg_0.68Al_0.32(OH)₂[Eu(EDTA)]_0.10(CO₃)_0.11·0.66H₂O. The interlayer spacing of the material is 13.8 Å, corresponding to a gallery height of 9.0 Å, which accords with the maximal dimensions (9-10 Å) of the anion in metal-EDTA complex salts as determined by single crystal X-ray diffraction. Geometrical considerations show that the charge density on the layered double hydroxide layers is too high to be balanced by intercalation of [Eu(EDTA)]⁻ alone, necessitating the co-intercalation of carbonate ions which have a much higher charge density.     

Tetrafluoroaurate(III) der Lanthaniden M2F[AuF4]5 (M = Tb,Dy, Ho,Er)

Tetrafluoroaurates(III) of Lanthanoides M₂F[AuF₄]₅ (M = Tb, Dy, Ho, Er) Tetrafluoroaurates(III) M₂F[AuF₄]₅ with M = Tb, Dy, Ho, Er, all yellow, have been obtained. From single crystal data they crystallize triclinic, space group P1 -C¹_i (No. 2) with Tb: a = 1 194,34(7) pm, b = 798,46(6) pm, c = 902,02(7) pm, α = 89,033(7)°, β = 88,990(6)°, γ = 89,006(7)°; Dy: a = 1 191,66(9) pm, b = 796,33(8) pm, c = 899,65(9) pm, α = 88,956(8)°, β = 89,056(8)°, γ = 88,972(8)°; Ho: a = 1 189,06(10) pm, b = 795,46(6) pm, c = 896,81(7) pm, α = 88,912(8)°, β = 89,101(7)°, γ = 88,873(8)°; Er: a = 1 185,20(40), b = 793,98(14), c = 893,83(20), α = 88,751(23)°, β = 89,187(26)°, γ = 88,884(9)°     

A model of melting of rare gases within bubbles of crystalline metal matrix

Abstract

On the basis of experimental results obtained in the present and some other works a model of melting of rare gas solids within bubbles formed in a crystalline metal matrix as a result of ion implantation is proposed. Rare gas solid is supposed to melt on heating at the expense of the bubble volume expansion by emission of a dislocation loop. On this basis the melting temperature can be estimated as one which is enough to provide for a pressure inside a bubble sufficient for the initiation of the dislocation loop punching. Values of melting temperatures obtained in this way are in good agreement with available experimental data.     

A new stable porous Pr-organic framework constructed by multi-iodine-substituted aromatic polycarboxylates: Synthesis,characterization, and selective adsorption of dyes

abstract

Poly[tris(dimethylformamide)(μ3-2,4,6-triiodol-1,3,5-benzene tricarboxylic acid)-praseodymium (III)] {Pr(TIBTC)(DMF)₃}_n (1) (H₃TIBTC = 2,4,6-triiodo-1,3,5-benzene tricarboxylic acid) was synthesized by the reaction of Pr(NO₃)₃·6H₂O and H₃TIBTC at 85°C in a pyrex vial. 1 was characterized by elemental analysis, IR, UV–vis, TGA, PXRD, and atomic force microscopy analytical means. Each of the central Pr ions and the three carboxyl groups from the same ligand constitute a SBU, which is then joined by a carboxyl group to form a building block. In order to further explore the functional properties of 1, we used this compound for adsorption experiments. It is found that 1 can effectively adsorb anionic dyes in aqueous solutions. In particular, there is a good adsorption efficiency for coomassie brilliant blue R-250. Therefore, 1 shows good prospects for selective adsorption of anionic dyes from wastewater solution.     

稀土分量的XRF法分析—熔珠粉末压薄片法

本法用50mg稀土氧化物样品,经四硼酸锂熔融后,粉碎压成薄片,以透空照射法,直接测定15项稀土分量和铀、钍。本法消除基体效应好,制样精度高,测定含量范围宽。     

高纯金属镨中痕量稀土杂质的电感耦合等离子体原子发射光谱分析及光谱干扰的校正

本文提出了PGS-2型平面光栅光谱仪(色散率0.18纳米,二级光谱)与PlasmaTherm ICP-5000D射频发生器联用,乙醇预去溶方式进样,同时直接测定高纯金属镨中5个痕量稀土杂质元素的方法。并讨论了基体浓度对检出限的影响以及光谱干扰及其校正方法。当样品溶液中镨的浓度为5毫克/毫升时,测定下限分别为镧、钕和钐0.002%,铈0.003%和钇0.0005%。获得了良好的实验结果,其相对标准偏差为1.2-6.2%。     

两种铽配合物与PVK混合体系的发光机理研究

研究了稀土配合物Tb(p-MBA)₃phen(样品Ⅰ)和Tb(p-ClBA)₃phen(样品Ⅱ)与导电聚合物材料PVK掺杂体系的光致发光和电致发光特性。发现在样品Ⅰ与PVK混合薄膜的光致发光中,除了三价铽离子的发光外,还能看到明显的PVK的发光;而在电致发光中,PVK的发光完全被抑制,只能看到Tb3+的绿光发射。对样品Ⅱ与PVK的混合发光层,无论其光致发光谱还是电致发光谱,都没有看到410 nm处PVK的发射。进一步测量两种材料的激发光谱,初步探讨了器件的发光机理。样品Ⅰ的发光可能来源于两个方面,一是PVK到稀土配合物的不完全的能量传递,二是由于载流子俘获机理;样品Ⅱ的发光则是由于PVK到稀土配合物的完全的能量传递。     

FTIR法研究氨基酸稀土配合物与磷脂的相互作用

利用傅里叶变换红外光谱（ＦＴＩＲ）法研究了不同类型氨基酸及其配合物与二棕榈酰磷脂酰胆碱脂质体浇铸膜的相互作用。结果表明，在有氨基酸存在下，二棕榈酰磷脂酰胆碱的红外谱图没有明显的变化；氨基酸稀土配合物与磷脂极性头基团有静电相互作用，作用的程度随稀土离子、氨基酸及稀土同氨基酸配比的不同而有所不同。