薄层软刻蚀法制备PMMA微图案结构

对现有的软刻蚀方法提出了改进,让其与压印技术及毛细力刻蚀技术相结合形成一种薄层软刻蚀技术,并以这种技术制备出PMMA薄膜微图案化结构.在30 mm/h的拉膜速度以及弹性印章表面图形深度确定不变的情况下,PMMA流体能够完全填充到弹性印章的微通道中,SEM和光学显微镜照片证明得到的PMMA微图案是相互分离的.因此,薄层软刻蚀技术可以克服普通微模塑方法制备分离图形困难和纳米压印技术中需要使用巨大机械压力的缺点.     

Antifungal and Surface Properties of Chitosan-Salts Modified PMMA Denture Base Material

Chitosan (CS) and its derivatives show antimicrobial properties. This is of interest in preventing and treating denture stomatitis, which can be caused by fungi. Therefore, the aim of this study was the development of a novel antifungal denture base material by modifying polymethyl methacrylate (PMMA) with CS-salt and characterizing its antifungal and surface properties in vitro. For this purpose, the antifungal effect of chitosan-hydrochloride (CS-HCl) or chitosan-glutamate (CS-G) as solutions in different concentrations was determined. To obtain modified PMMA resin specimens, the CS-salts were added to the PMMA before polymerization. The roughness of these specimens was measured by contact profilometry. For the evaluation of the antifungal properties of the CS-salt modified resins, a C. albicans biofilm assay on the specimens was performed. As solutions, both the CS-G and CS-HCl-salt had an antifungal effect and inhibited C. albicans growth in a dose-dependent manner. In contrast, CS-salt modified PMMA resins showed no significant reduced C. albicans biofilm formation. Furthermore, the addition of CS-salts to PMMA significantly increased the surface roughness of the specimens. This study shows that despite the antifungal effect of CS-salts in solution, a modification of PMMA resin with these CS-salts does not improve the antifungal properties of PMMA denture base material.     

PP/PMMA/PP-g-MAH共混物的结晶和相形态研究

采用偏光显微镜和相差显微镜详细研究PP/PMMA不相容聚合物共混物体系和PP/PMMA/PP-g-PMMA增容共混体系的结晶和相形态.偏光显微照片的研究结果表明,增容剂PP-g-MAH中PP结晶需要克服更多的能垒,导致PP结晶形态变得不完善,球晶尺寸变小.比较PP/PMMA和PP/PMMA/PP-g-MAH的相差显微照片可以看出,由于增容剂的加入,PP与PMMA相之间的界面变得模糊,两相的相容性变好.随着PP-g-MAH中MAH接枝率的增加,PMMA分散相的尺寸减小且变得均匀;当增容剂的接枝率为2.41%,添加的质量分数为4.71%,PP/PMMA共混体系中PMMA分散相的相?尺寸可达最小.PP-g-MAH作为反应型增容剂,一方面与PP在界面区域产生共晶;另一方面,MAH极性基团与PMMA的极性基团间产生的强的化学键合作用,使得界面区域的PP-g-MAH分子采取有利于降低构象熵的构象来起到增容作用.PP/PMMA共混物在130℃等温结晶的结果显示,PMMA相对PP的结晶形态的影响较小,PP结晶呈现典型的均相成核特征.PP/PMMA共混体系中加入PP-g-MAH,PP结晶尺寸减少.与非等温结晶相比,等温结晶的PP/PMMA共混物中PMMA相区尺寸明显偏大.     

Thermal and optical properties of silver-poly(methylmethacrylate) nanocomposites prepared by in-situ radical polymerization

Surface modified silver nanoparticles dispersed in chloroform were encapsulated in poly(methylmethacrylate) (PMMA) by in-situ radical polymerization of methyl methacrylate initiated by 2,2′-azobisisobutyronitrile. The particle size distribution of colloidal silver nanoparticles was determined using transmission electron microscopy. The obtained transparent nanocomposite films were characterized using UV-vis spectroscopy, ¹H NMR spectroscopy and gel permeation chromatography. Effective medium Maxwell-Garnett theory was used in order to explain optical properties of nanocomposite films taking into account inhomogeneous spatial distribution of silver nanoparticles in PMMA matrix. The influence of the silver nanoparticles on the thermal properties of the PMMA matrix was investigated using thermo-gravimetric analysis and differential scanning calorimetry. Thermo-oxidative stability of the PMMA in the presence of low content of inorganic phase is significantly improved. The glass transition temperatures of nanocomposites are slightly lower compared to the pure polymer.     

Influence of cubic α-Fe2O3 particles on the thermal stability of poly(methyl methacrylate) synthesized by in situ bulk polymerization

Poly(methyl methacrylate)/α-Fe₂O₃ composites were prepared by in situ bulk radical polymerization of methyl methacrylate in the presence of the cubic α-Fe₂O₃ particles using 2,2′-azobisisobutyronitrile as initiator. The cubic α-Fe₂O₃ particles were synthesized by forced hydrolysis of FeCl₃ and characterized by X-ray diffraction analysis and transmission electron microscopy. The molar masses and molar mass distribution of synthesized PMMA samples were determined by gel permeation chromatography. The influence of α-Fe₂O₃ filler particles on the thermal properties of the PMMA matrix was investigated using thermogravimetry and differential scanning calorimetry. The molar mass and polydispersity of PMMA extracted from composite samples were not influenced by cubic α-Fe₂O₃ particles. The obtained composites have better thermal and thermooxidative stability than pure PMMA. On the other hand, the values of the glass transition temperature of composite samples were identical to the glass transition temperature of pure PMMA.     

Effect of ZnO and organo-modified montmorillonite on thermal degradation of poly(methyl methacrylate) nanocomposites

Since a few years ago, a topic of interest consists in developing composites filled with nanofillers to improve thermal degradation and flammability property of poly(methyl methacrylate) (PMMA). In the present work, the effects of ZnO nanoparticles and organo-modified montmorillonite (OMMT) on the thermal degradation of PMMA were investigated by thermogravimetric analysis (TGA). PMMA-ZnO and PMMA-OMMT nanocomposites were prepared by melt blending with different (2, 5, and 10 wt%) loadings. SEM and TEM analyses of nanocomposites were performed in order to investigate the dispersion of nanofillers in the matrix. According to TGA results, the addition of ZnO nanoparticles does not affect the thermal degradation of PMMA under an inert atmosphere. However, in an oxidative atmosphere, two contrary effects were observed, a catalytic effect at lower concentration of ZnO in the PMMA matrix and a stabilizing effect when the ZnO concentration is higher (10 wt%). In contrast, the presence of OMMT stabilizes the thermal degradation of PMMA whatever be the atmosphere. Differential thermal analysis (DTA) curves showed surprising results, because a dramatic change of exothermic reaction of the PMMA degradation process to an endothermic reaction was observed only in the case of OMMT. During the degradation of PMMA-ZnO nanocomposites, pyrolysis-gas chromatography coupled to mass spectrometer (Py-GC/MS) showed an increase in the formation of methanol and methacrylic acid while a decrease in the formation of propanoic acid methyl ester occurred. In the case of PMMA-OMMT systems, a very significant reduction in the quantity of all these degradation products of PMMA was observed with increasing OMMT concentration. It is also noted that during PMMA-OMMT degradation less energy was released as the decomposition is an endothermic reaction and the material was cooled.     

Atmospheric‐pressure spin plasma jets processing of polymethylmethacrylate surface using experimental design methodology

Atmospheric‐pressure spin plasma jets (APSPJs) have been developed to induce surface modifications on polymethylmethacrylate (PMMA). In this study, an experimental design methodology was used to investigate the influence of process parameters [such as radio frequency (RF) power, processing gap, and number of treatment cycles] on the characteristics of PMMA surface treated by APSPJs. It was observed from the atomic force microscope (AFM) and scanning electron microscope (SEM) results that the surface morphology of PMMA treated by direct plasma is much rougher than that treated by remote plasma. The direct plasma used in APSPJs processing created a substantial amount of nanostructure grains. Moreover, the measured XPS results showed that the O/C ratios of the PMMA surface were substantially increased and subsequently water contact angle decreased on direct plasma treatment. This decrease is due to an increase of oxygen‐containing functional groups on the PMMA surface by the APSPJs processing. From the statistical analysis, the RF power and the processing gap were found to play a major role in enhancing the hydrophilic properties of PMMA surface. In contrast, the number of treatment cycles played only a secondary role in this case. Finally, in this study the APSPJs processing was demonstrated to be an effective method for surface modification of PMMA by controlling processing parameters during the treatment process. Copyright © 2009 John Wiley & Sons, Ltd.     

Focused ion beam irradiation—morphological and chemical evolution in PMMA

For poly(methyl methacrylate) (PMMA) as a representative of amorphous thermoplastic polymers, the milling effects, and the chemical changes due to ion bombardment with a focused ion beam (FIB) at normal incidence are studied with scanning force microscopy (SFM), scanning electron microscopy (SEM)/energy dispersive X‐ray (EDX), and infrared (IR) spectroscopy for varying conditions of Ga⁺ treatment, including the effect of partial water pressure. Stopping and Range of Ions in Matter (SRIM) simulation results for 30 keV Ga⁺ at normal incidence show that the zone of primary ion–polymer interaction extends ca 100 nm into the PMMA. Accordingly, this interaction region is much wider than the original beam diameter. The width of the region where the recoiled ions interact strongly with the polymer chains is larger. Secondary processes, such as fragment diffusion and phonon transport, are expected to extend even farther into the polymer. SEM and SFM reveal distinct topologies of areas milled without or in presence of water vapour. Water vapour–assisted FIB milling produces more roughness and defects. The infrared attenuated total reflection spectroscopy (IR‐ATR) spectra indicate that ion milling in PMMA damages methacrylate side groups in particular. In contrary to metals, an increase in the degree of milling is found when the beam spot overlap parameter increases. Copyright © 2009 John Wiley & Sons, Ltd.     

Wall-jet conductivity detector for microchip capillary electrophoresis

A new end-column ‘hybrid’ contactless conductivity detector for microchip capillary electrophoresis (CE) was developed. It is based on a “hybrid” arrangement where the receiving electrode is insulated by a thin layer of insulator and placed in the bulk solution of the detection reservoir of the chip, whereas the emitting electrode is in contact with the solution eluted from the channel outlet in a wall-jet arrangement. The favorable features of the new detector including the high sensitivity and low noise, can be attributed to both the direct contact of the ‘emitting’ electrode with the analyte solution as well as to the insulation of the detection electrode from the high DC currents in the electrophoretic circuit. Such arrangement provides a 10-fold sensitivity enhancement compared to currently used on-column contactless conductivity CE microchip detector as well as low values of noise and easy operation. The new design of the wall-jet conductivity detector was tested for separation of explosive-related methylammonium, ammonium, and sodium cations. The new detector design reconsiders the wall-jet arrangement for microchip conductivity detection in scope of improved peak symmetry, simplified study of inter-electrode distance, isolation of the electrodes, position of the wall-jet electrode to the separation channel, baseline stability and low limits of detection.     

一种可控纳米柱阵列的研制

在一次阳极氧化法制备多孔氧化铝(anodized aluminum oxide,AAO)的基础上,进行了二次、三次、四次氧化制备AAO,并对多次氧化制备多孔AAO的电流变化曲线和模板表面的形貌特点等进行了比较分析.二次、三次、四次氧化制备的AAO纳米孔孔径依次增大、孔间距减小,而模板表面的纳米孔有序性分布没有明显变化.控制一次氧化AAO模板的除膜时间,～10 min即可得到孔径规则、高度有序的AAO膜.最后,利用所制备的不同孔深和孔径的AAO为模板,通过热纳米压印复制技术制备了长度和直径等性质可控的PMMA纳米柱阵列. 关键词： 纳米柱阵列 聚甲基丙烯酸甲酯 多孔氧化铝模板 多次氧化法