互通多孔碳/二氧化锰纳米复合材料的原位水热合成及电化学性能

以互通多孔碳（IPC）为载体，水热条件下在碳表面原位反应生成纳米结构的二氧化锰（MnO₂），制备互通多孔碳/二氧化锰纳米（IPC/MnO₂）复合电极材料. 采用扫描电镜（SEM），透射电镜（TEM），X射线衍射（XRD），热重分析（TGA）对其结构进行表征；采用循环伏安法、恒流充放电和交流阻抗对其电化学性能进行研究. 结果表明：生成的MnO₂均匀地负载在碳的表面，形成多层次结构，并且随着温度的升高IPC表面负载的MnO₂由纳米颗粒变为纳米片状结构；MnO₂纳米片具有典型的K-Birnessite 型晶体结构；复合物中MnO₂的含量约为34%（w）. 在100 ℃制备的IPC/MnO₂复合材料在三电极系统中最高比电容达到了411 F·g^-1；随着反应温度的升高,比容量先增长后基本保持不变. 以IPC/MnO₂为正极，活性炭（AC）为负极，1 mol·L^-1 Na₂SO₄溶液为电解液组装成IPC/MnO₂//AC 混合超级电容器，发现IPC/MnO₂电极的电容器其电位窗口从1 V扩展到1.8 V，容量可达86F·g^-1，且表现出良好的电容特性和大电流放电性能.     

Electrochemical instability of bis(trifluoromethylsulfonyl)imide based ionic liquids as solvents in high voltage electrolytes for potassium ion batteries

1. Download : Download high-res image (153KB)
2. Download : Download full-size image

     

Effects of pH and Dye Concentration on the Optical and Structural Properties of Coumarin-4 Dye-Doped SiO2-PDMS Xerogels

Optical and structural properties of coumarin-4 dye-doped SiO₂-PDMS xerogels synthesized by acid catalyzed (one-step) and acid-base catalyzed (two-step) sol-gel routes with varying pH (0.6 to 7) and dye content ( 5 × 10^–4 to 5 × 10^–2 mole) are reported. Spectroscopic methods such as photo-luminescence, FT-IR and FT-Raman were used for characterizations. The acid catalyzed xerogels prepared with pH < 2.5 exhibited two fluorescence peaks, I at 390 nm and II at 480 nm. The acid-base catalyzed xerogels synthesized with pH < 2.5 also exhibited two peaks, I at 400 nm and II at 475 nm. Peak II was not observed for the samples with pH 2.5. This phenomenon was attributed to the existence of pH dependent different forms of coumarin-4 molecule. The concentration-quenching phenomenon was observed for the acid catalyzed xerogels prepared with different dye concentration. TheFT-IR spectra indicated the existence of hydrogen bonds between the carbonyl groups of dye molecules and the silanol groups of gel matrix. The hydrogen bonding was the highest for the samples with the extremity pH, 0.6 and 7, resulting in the highest dye/gel matrix interactions, hence, the highest fluorescence peaks. The Raman studies indicated that the samples prepared with pH < 2.5 possessed relatively more number of 3-membered siloxane rings than 4-membered siloxane rings. The ring statistics was reversed for the samples with pH > 2.5. The number of silanol groups was higher for the samples with pH > 2.5.     

氧化共沉淀法制备纳米级掺锑α—Fe2O3气敏陶瓷粉料

氧化共沉淀法制备纳米级掺锑α┐Ｆｅ２Ｏ３气敏陶瓷粉料王忠春＊＊刘尔生陈耐生＊黄金陵（福州大学化学系福州３５０００２）关键词α－Ｆｅ２Ｏ３陶瓷，锑掺杂气敏材料，纳米材料１９９６－１０－０５收稿，１９９７－０４－２２修回福建省科委资助项目＊＊现在上海硅酸...     

手性液晶掺杂剂（S）—4‘—辛氧基—4—（2—酰氧基—丙氧基）联苯的合成

手性液晶掺杂剂（Ｓ）┐４┐辛氧基┐４┐（２┐酰氧基┐丙氧基）联苯的合成马汝建李培荣国斌＊（华东理工大学化学系上海２００２３７）关键词铁电液晶材料，手性液晶掺杂剂，合成，手征性１９９７－０２－０３收稿，１９９７－０８－０７修回铁电液晶显示器所用的材料...     

Hydrogen bonded layer-by-layer assembly of poly(2-vinylpyridine) and poly(acrylic acid): Influence of molecular weight on the formation of microporous film by post-base treatment

This article describes the buildup of hydrogen bonded multilayer film of poly(2-vinylpyridine) (P2VP) and poly(acrylic acid) (PAA), and the influence of polymer molecular weight on the formation of microporous film by post-base treatment. The formation of a microporous film involved a two-step mechanism: the release of PAA from P2VP/PAA multilayer, and the reorganization of the remaining P2VP on the substrate. Fourier transform infrared spectroscopy (FT-IR) indicated that the release of PAA from hydrogen bonded multilayer was a rapid process, which was almost independent of the molecular weight of PAA. Furthermore, the molecular weight of P2VP had a great effect on micropore formation by immersing the P2VP/PAA multilayer in basic solution. The rate of micropore formation increased with increasing molecular weight. We anticipate that a comparative study on P2VP/PAA films containing high or low molecular weight polymer provides a way to control the surface morphology, and will be helpful and constructive for the forthcoming discussion about the formation of the microporous film.     

Evaluation of the sputtering rate variation in SIMS ultra‐shallow depth profiling using multiple short‐period delta layers

We have developed multiple short‐period delta layers as a reference material for SIMS ultra‐shallow depth profiling. Boron nitride delta layers and silicon spacer layers were sputter‐deposited alternately, with a silicon spacer thickness of 1–5 nm. These delta‐doped layers were used to measure the sputtering rate change in the initial stage of oxygen ion bombardment. A significant variation of sputtering rate was observed in the initial 3 nm or less. The sputtering rate in the initial 3 nm was estimated to be about four times larger than the steady‐state value for 1000 eV oxygen ions. Copyright © 2003 John Wiley & Sons, Ltd.     

水相锌二次电池正极材料V2O5/C的电化学性能研究

采用溶胶－凝胶法合成了一种V₂O₅/C复合材料.扫描电镜（SEM）和红外光谱（FTIR）分析表明,这是一种外层V₂O₅胶体包覆内层乙炔分子的多孔复合材料.以V₂O₅/C作正极,锌片为负极,Zn(ClO₄)₂溶液为电解质组成水相锌二次电池,采用循环伏安（CV）和电化学阻抗谱（EIS）等方法研究发现:V₂O₅:C质量比为1:1时电极具有最好的电化学性能,电池开路电压达1.64 V; Zn^2＋能分别在1.01 V和1.26 V处分步嵌入V₂O₅/C结构中A、B两种位置,其嵌入电流密度峰值最高可达70 mA•g^－1,并且具有较好的循环充放电性能;在一定放电深度下,V₂O₅/C电极反应速率受Zn^2＋的扩散过程控制.     

聚丙烯微孔膜基渐变聚合物的制备,结构与性能的研究

以聚丙烯微孔膜为基材，通过扩散控制原位共聚合的方法在人填充了组成沿膜的厚度方向逐渐改变的无规共聚物，Ｘ－光电子能谱（ＸＰＳ）、全反射红外光谱（ＡＴＲ）以及动态粘弹谱的分析结果。说明所制备得到的合膜具有明显的渐变聚合物性质。     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.