氟硅烷自组装单分子膜的制备及其摩擦学性能

利用分子自组装技术制备了全氟辛酰胺丙基硅烷单分子膜,用X射线光电子能谱(XPS)对组装膜的表面元素进行了表征;接触角测试表明,该组装膜具有很好的疏水-疏油性,其对水的接触角高达105°,对正十六烷的接触角为50°.摩擦磨损实验结果表明,全氟辛酰胺丙基硅烷自组装单分子膜可以大大降低基片的摩擦系数,使载玻片的摩擦系数从0.85左右降低到0.14左右,而且低负荷下具有很好的耐磨性.     

Impedance laser spectroscopy in a small RF-excited neon discharge

Laser impedance spectroscopy in a miniature neon RF-discharge operating at 0.27 bar was performed. The dominant role of the metastable atoms to the size and the sign of the RF-signal was investigated. Excellent linearity of the RF-signal but poor detection sensitivity of excited metastable neon atoms were found at low laser powers.     

Surface modification of low density polyethylene (LDPE) film by low pressure O2 plasma treatment

In this work, low pressure glow discharge O₂ plasma has been used to increase wettability in a LDPE film in order to improve adhesion properties and make it useful for technical applications. Surface energy values have been estimated using contact angle measurements for different exposure times and different test liquids. In addition, plasma-treated samples have been subjected to an aging process to determine the durability of the plasma treatment. Characterization of the surface changes due to the plasma treatment has been carried out by means of Fourier transformed infrared spectroscopy (FTIR) to determine the presence of polar species such as carbonyl, carboxyl and hydroxyl groups. In addition to this, atomic force microscopy (AFM) analysis has been used to evaluate changes in surface morphology and roughness. Furthermore, and considering the semicrystalline nature of the LDPE film, a calorimetric study using differential scanning calorimetry (DSC) has been carried out to determine changes in crystallinity and degradation temperatures induced by the plasma treatment. The results show that low pressure O₂ plasma improves wettability in LDPE films and no significant changes can be observed at longer exposure times. Nevertheless, we can observe that short exposure times to low pressure O₂ plasma promote the formation of some polar species on the exposed surface and longer exposure times cause slight abrasion on LDPE films as observed by the little increase in surface roughness.     

交流示波极谱法中if～E曲线的研究（Ⅱ）：if～E曲线的理论公式

提出利用i_f～E曲线代替常用的dE/dt～E曲线的新的交流示波极谱法,并研究了该法的基本理论,推导出i_f～E曲线的理论公式。     

Electroreductive polymerization of trans-[RuCl 2(vpy) 4] on Nd-Fe-B magnets: electrochemical impedance spectroscopy interpretation, Raman spectroscopy, X-ray photoelectron spectroscopy and scanning electron microscopy analysis

The electropolymerization of trans-[RuCl₂(vpy)₄] (vpy=4-vinylpyridine) monomer on Nd-Fe-B magnets was studied by electrochemical impedance spectroscopy (EIS). Impedance diagrams obtained during the polymerization process were used to monitor film formation. The EIS results gave insight into the electrochemical phenomena occurring at the magnet surface as the polymerization process progressed. The film structure and morphology were also studied by X-ray photoelectron spectroscopy, scanning electron microscopy and Raman spectroscopy. The Raman spectroscopy results showed that the polymerization takes place at the vinyl groups of the monomer and also that the redox polymer structure is very similar to that of the monomer. The ratio of the intensity of the XPS peaks for fluorine (from the electrolyte PF₆ ^–) and ruthenium present in the film showed that the polymer on Nd-Fe-B contained an equal proportion of Ru²⁺ and Ru³⁺, indicating that part of the film is positively charged, i.e. {[RuCl₂(vpy)₄]⁺} _n .     

Electrochemical synthesis, characterization and some properties of a polymer derived from thioflavin S

Polymeric films derived from thioflavin S were electrosynthesized on mild steel and silver electrodes in sulfuric acid and lithium perchlorate-containing aqueous solutions. The introduction of thioflavin S in an acidic solution protected the surface of steel from corrosion. The electrochemical behavior of the steel coated with a layer of poly(thioflavin) was examined by electrochemical impedance spectroscopy. The films exhibited a capacitive behavior and were semi-conductive in nature. Infra red reflectance measurements of the polymer films at the steel surface showed that the polymer structure retained the aromatic structure of the benzene and thiazole rings with the distinction of a nitrogen quinone vibrational band. Surface morphology of the polymer film was examined with scanning electron microscopy. The films are yellow, compact and dense when electrochemically formed onto steel surfaces when compared to a blue rather porous when formed onto silver electrode. The mechanism of electropolymerization of thioflavin is given and found similar to that of aniline with the possibility of metal chelation with the sulfur and/or nitrogen in the thiazole ring.     

用CR传输线模型研究涂层/金属体系阻抗谱

根据CR传输线模型和QR电路之间的关系,建立了拟合其初值的计算方法,借助Z-View软件,可求得各元件精确值.根据电容（Ci）和电阻（Ri）随特征频率（f*）的分布,推导了元件相对增量与恒相位角元件（Q）指数参数n的关系. 结果表明, 当n小于0.5时,Ci比Ri增加得更快,从新的角度说明了n的物理意义及其和界面脱层之间的关系.作为应用实例,拟合了不同特征的电化学阻抗谱,分析了有机涂层/金属腐蚀体系阻抗变化的具体过程,区分了点蚀和脱层因素对阻抗谱的影响,从高阻抗体系同时得到了与不同空隙率有关的涂层电容和电阻值,并根据涂层体系的不均匀特征探讨了模型结构的物理意义.     

Performance of hollow-fiber flow field-flow fractionation in protein separation

Since hollow-fiber flow field-flow fractionation (HF FIFFF) utilizes a cylindrical channel made of a hollow-fiber membrane, which is inexpensive and simple in channel assembly and thus disposable, interests are increasing as a potential separation device in cells, proteins, and macromolecules. In this study, performance of HF FIFFF of proteins is described by examining the influence of flow rate conditions and length of fiber (polyacrylonitrile or PAN in this work) on sample recovery as well as experimental plate heights. The interfiber reproducibility in terms of separation time and recovery was also studied. Experiments showed that sample recovery was consistent regardless of the length of fiber when the effective field strength (equivalent to the mean flow velocity at the fiber wall) and the channel void time were adjusted to be equivalent for channels of various fiber lengths. This supported that the majority of sample loss in HF FIFFF separation of apoferritin and their aggregates may occur before the migration process. It is finally demonstrated that HF FIFFF can be applied for characterizing the reduction in Stokes' size of low density lipoproteins from blood plasma samples obtained from patients having coronary artery disease and from healthy donors.     

第三组分Et2Mg对二茂锆/铝氧烷体系催化乙烯聚合反应的影响

研究发现在二茂锆-铝氧烷催化体系中添加少量Et2Mg能够明显促进在低Al/Zr摩尔比条件下乙烯高聚.以MAO作为助催化剂,Al/Zr/Mg摩尔比为1012时,得到高聚物,粘均分子量(Mv)为1.37×105,催化活性为2.83×104g聚合物/mol(Zr)h.而在同样的反应条件下,Cp2ZrCl2-MAO和-EAO二组份催化体系在如此低的Al/Zr摩尔比条件下无催化活性或以很低的催化活性生成低碳烯烃.对于这类三组份烯烃高聚催化体系的研究目前仍在进行中,以期得到有效的低Al/Zr比乙烯高聚茂金属催化体系.     

BaCe0.8Ho0.2O3-a陶瓷的性质与应用

Ceramic BaCe0.8Ho0.2O3-α with orthorhombic perovskite structure was prepared by conventional solid state reaction, and its conductivity and ionic transport number were measured by ac impedance spectroscopy and gas concentration cell methods in the temperature range of 600-1000 ℃ in wet hydrogen and wet air, respectively. Using the ceramics as solid electrolyte and porous platinum as electrodes, the hydrogen-air fuel cell was constructed, and the cell performance at temperature from 600-1000 ℃ was examined. The results indicate that the specimen was a pure protonic conductor with the protonic transport number of 1 at temperature from 600-900 ℃ in wet hydrogen, a mixed conductor of proton and electron with the protonic transport number of 0.99 at 1000 ℃. The electronic conduction could be neglected in this case, thus the total conductivity in wet hydrogen was approximately regarded as protonic conductivity. In wet air, the specimen was a mixed conductor of proton, oxide ion and electron hole. The protonic transport numbers were 0.01-0.09, and the oxide-ionic transport numbers were 0.27-0.32. The oxide ionic conductivity was increased with the increase of temperature, but the protonic conductivity displayed a maximum at 900 ℃, due to the combined increase in mobility and depletion of the carriers. The fuel cell could work stably. At 1000 ℃, the maximum short-circuit current density and power output density were 346 mA/cm^2 and 80 mW/cm^2, respectively.