Microscopically structural studies of lithium niobate powders

On the basis of the crystallographic characteristics of lithium niobate (LN) crystals, Law of Bravais and Pauling's third rule (i.e. Polyhedral Sharing Rule) are employed with the aim to find the relationship between the crystal structure and morphological faces of LN powders. In order to validate our analytical results, we have successfully synthesized LN powders and measured the corresponding X-ray powder diffraction. Our results show that the structural analysis is consistent with the experimental data and is helpful and effective for us to control the single-crystal growth and to design superstructures at the specific plane, starting from the viewpoint of the microscopic behaviors of constituent chemical bonds and polyhedra in the crystallographic frame.     

Aluminum(III) complexes containing O,O chelating ligand

The stoichiometric reactions of trimethylaluminum with 2,6‐(MeOCH₂)₂C₆H₃OH (LH) revealed compounds L₃Al ( 1 ) and L₂AlMe ( 2 ). On the other hand reaction of 1 equiv. of LH with trimethylaluminum did not lead to the formation of complex LAlMe₂ ( 3 ), rather 2 together with Me₃Al were observed as a result of a disproportionation of 3 . Compounds 1 and 2 were characterized by elemental analysis, ¹H and ¹³C NMR spectroscopy and in the case of 1 by X‐ray diffraction. Derivative 2 underwent transmetalation with Ph₃SnOH, giving LSnPh₃ ( 4 ) as the result of a migration of ligand L from the aluminum to the tin atom. The identity of 4 was established by elemental analysis, ¹H, ¹³C and ¹¹⁹Sn NMR spectroscopy and ¹H, ¹¹⁹Sn HMBC experiments. The system 2 and B(C₆F₅)₃ in a 1:1 molar ratio was shown to be active in the polymerization of propylene oxide and ε‐caprolactone. Copyright © 2007 John Wiley & Sons, Ltd.     

SPS法研究ZnTPP对TiO_2的光谱敏化

本文利用表面光电压谱(Surface Photovohage spectroscopy,简称SPS)研究了ZnTPP对TiO_2粉末的光谱敏化,发现用ZnTPP修饰后的TiO_2(金红石和锐钛矿)粉末在可见区420、550和590nm附近有三个光伏响应带,它们分别对应于ZnTPP的Soret、Q(1,0)和Q(0,0)带。经过严格的实验和分析,证明这三个带是由ZnTPP对TiO_2的敏化光电压引起的,而不是ZnTPP自身的光伏响应。在敏化效果上,亚稳的锐钛矿优于金红石。同时,我们对这种光敏表面的光诱导电荷转移机制和SPS作为一种研究光谱敏化方法的可行性进行了讨论。     

Thermoanalytical investigation of layered titanium salts

The investigated materials have similar routes of thermal decomposition; i.e. they lose their crystal water first, then at a higher temperature their structural one. At least the result TiP₂O₇ goes through a phase change at about 1000 K. The amorphous titanium phosphate lost its crystal and structural water at higher temperature than those of crystalline forms. Both α- and γ-titanium phosphates and also their transition metal containing forms have layered structure. In case of α- and γ-forms after the loss of crystal water a phase change occurs which is followed by the decomposition of the molecule. Various transition metals containing γ-titanium phosphates lose their crystal water at the same temperature, with the exception of Ni containing ones. The process is finished in this case at temperature 90 K higher than that of the others. This revised version was published online in July 2006 with corrections to the Cover Date.     

石英晶体微天平技术研究纳米TiO_2表面Cu(Ⅱ)吸附与光化学还原过程

环境中排放的重金属离子Cu!对水生和陆生生物有强的毒害性。饮用水中Cu!的浓度高于1.0mg·L-1时,将会导致人畜得血色沉着病和胃肠粘膜病[1]。Cu!无法进行生物降解,除去废水中Cu!的常见方法有离子交换、置换、化学沉淀等[2],然而这些方法需要消耗大量的化学试剂,成本高。近来,研     

电流密度对钙磷沉积层组成和结构的影响(英文)

用X射线衍射、激光拉曼光谱以及等离子体原子发射光谱等技术研究了电化学沉积钙磷陶瓷过程中 ,电流密度对电沉积层组成和结构的影响 .实验表明阴极表面得到的沉积物是几种钙磷盐组成的混合物 ,且其成份随电流密度的改变而发生较大的变化 .在电解液温度为 75℃条件下 ,当控制电流密度较低时 ,沉积层主要由CaHPO4· 2H2 O (DCPD)和Ca8H2 (PO4) 6· 5H2 O (OCP)组成 ;随着电流密度的增加 ,阴极表面逐渐生成Ca3 (PO4) 2 ·nH2 O (TCP)和Ca10 (PO4) 6(OH) 2 (HAP) .当电流密度大于 5mA/cm2 时 ,电沉积层的主要成份为羟基磷灰石 (HAP) .     

铝钛合金溴化物对直链烷烃异构化反应的催化作用

首次研究了铝铁合金溴化物的合成及其对直链烷烃异构化反应的催化作用,讨论了正戊烷的异构化反应,得到其动力学方程为1nC/C_0=-0.50t,表观活化能为26.3 kJ/moJ,测定了正己烷、正庚烷、正辛烷在不同溶剂中、不同温度下催化异构化反应的动力学曲线,为铝铁合金溴化物的工业应用提供了理论依据。