Fabrication and characterization of sputtered titanium dioxide films

TiO₂ thin films were prepared under various conditions by using a reactive RF sputtering technique. The structural, optical and electrical characteristics of the films have been investigated. All as-deposited films were amorphous. After annealing at T > 673 K, the crystallinity of the observed tetragonal anatase phase appeared improved. The optical band gap, determined by using Tauc plot, has been found to amount to 3.38 ± 0.03 and 3.21 ± 0.03 eV for the direct and indirect transition, respectively. Also the complex optical constants for the wavelength range 300-2500 nm are reported. Using the two-point probe technique, the dark resistivity has been measured as a function of the film thickness, d. The resistivity, ρ, of the samples has been found to decrease markedly with increasing thickness, but only for d < 100 nm. The behaviour of ρd versus d was found to fit properly with the Fuchs and Sondheimer relation with parameters ρ_o = 4.95 × 10⁶ Ω cm and mean free path, l = 310 ± 2 nm. The log ρ versus 1/T curves show three distinct regions with values for the activation energy of 0.03 ± 0.01, 0.17 ± 0.01 and 0.50 ± 0.02 eV, respectively.     

Au/SiO2纳米多层薄膜的制备及其性质表征

利用多靶磁控溅射技术制备了Au/SiO₂纳米颗粒分散氧化物多层复合薄膜.研究了在保持Au单层颗粒膜沉积时间一定时薄膜厚度一定、变化SiO₂的沉积时间及SiO₂的沉积时间一定而改变薄膜厚度时，多层薄膜在薄膜厚度方向的微观结构对吸收光谱的影响.研究结果表明：具有纳米层状结构的Au/SiO₂多层薄膜在560 nm波长附近有明显的表面等离子共振吸收峰，吸收峰的强度随Au颗粒的浓度增加而增强，在Au颗粒浓度相同的情况下，复合薄膜 关键词： 2纳米复合薄膜')" href="#">Au/SiO₂纳米复合薄膜 多靶磁控溅射 吸收光谱 有效介质理论     

Effects of UV photon irradiation on SiOx (0 < x < 2) structural properties

Thin films of a-SiO_x (0 < x < 2) were prepared by reactive r.f. magnetron sputtering from a polycrystalline-silicon target in an Ar/O₂ gas mixture. The oxygen partial pressure in the deposition chamber was varied so as to obtain films with different values of x. The plasma was monitored, during depositions, by optical emission spectroscopy (OES) system. Energy dispersive X-ray (EDX) measurements and infra-red (IR) spectroscopy were used to study the compositional and structural properties of the deposited layers.Structural modifications of SiO_x thin films have been induced by UV photons’ bombardment (wavelength of 248 nm) using a pulsed laser. IR spectroscopy and X-ray photoemission spectroscopy (XPS) were used to investigate the structural changes as a function of x value and incident energy. SiO_x phase separation by spinodal decomposition was revealed. The IR peak position shifted towards high wavenumber values when the laser energy is increased. Values corresponding to the SiO₂ material (only Si⁴⁺) have been found for laser irradiated samples, independently on the original x value. The phase separation process has a threshold energy that is in agreement with theoretical values calculated for the dissociation energy of the investigated material.For high values of the laser energy, crystalline silicon embedded in oxygen-rich silicon oxide was revealed by Raman spectroscopy.     

c轴定向氮化铝薄膜的制备

利用电子回旋共振 (ECR)微波增强化学气相沉积法 (PECVD)并使用氮气 (N2 ) ,氩气 (Ar)和AlCl3蒸气作为气源在直径为 6 .35cm的 (10 0 )单晶硅片表面制备了c轴定向氮化铝 (AlN)薄膜 ,并使用X射线衍射仪及其X射线特征能谱和扫描电镜 (SEM)分析了薄膜特征 ,研究了微波功率、基板温度和N2 流量对薄膜c轴定向的影响 ,得到了c轴偏差角小于 5°的高质量大面积AlN薄膜。     

溅射功率对多层膜质量的影响

用磁控溅射技术制备薄膜，用X射线衍射研究在基片和靶间距离固定的情况下不同的溅射功率对薄膜结构的影响。结果表明：过低的溅射功率下淀积的薄膜有畸变的X射线衍射特征峰，特征峰强度小，半峰全宽大。而比较高溅射功率得到的薄膜有比较尖锐的X射线衍射特征峰，强度高和半峰全宽非常窄。研究表明，X射线衍射特征峰强度小和半峰全宽大的薄膜结构疏松，而强度高和半峰全宽非常窄的薄膜结构致密。     

反应离子镀光学薄膜的微观结构分析

用反应离子镀方法制备了ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜，用透射电子显微镜分别观察了由反应离子镀方法及传统蒸镀法二种不同工艺制得的ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜的断面结构，并对ＴｉＯ２单层膜进行了喇曼分析和卢瑟福背散射分析。     

用电泳技术制备YBCO高温超导厚膜

介绍了电泳技术制备YBCO高温超导厚膜的实验方法和YBCO高温超导厚膜的电学性质测量 ,讨论了在学生小型科研实验或设计实验中开展此实验的学时安排、注意事项和实验内容的扩展 .     

Effect of nonstoichiometry on Raman scattering of VO2 films

We report on Raman scattering of VO2 films prepared by radio frequency magnetron sputtering under different conditions. Our investigations revealed that the dominated Raman peaks shift towards high frequency for both V-rich and O-rich VO2 films, compared with the stoichiometry VO2 films. The experimental evidence is presented and the cause for nonstoichiometry dependence of Raman spectra of VO2 films is discussed.     

Electrical characterization of low temperature deposited TiO2 films on strained-SiGe layers

Thin films of titanium dioxide have been deposited on strained Si_0.82Ge_0.18 epitaxial layers using titanium tetrakis-isopropoxide [TTIP, Ti(O-i-C₃H₇)₄] and oxygen by microwave plasma enhanced chemical vapor deposition (PECVD). The films have been characterized by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). Dielectric constant, equivalent oxide thickness (EOT), interface state density (D_it), fixed oxide charge density (Q_f/q) and flat-band voltage (V_FB) of as-deposited films were found to be 13.2, 40.6 Å, 6×10¹¹ eV⁻¹ cm⁻², 3.1×10¹¹ cm⁻² and −1.4 V, respectively. The capacitance–voltage (C–V), current–voltage (I–V) characteristics and charge trapping behavior of the films under constant current stressing exhibit an excellent interface quality and high dielectric reliability making the films suitable for microelectronic applications.     

后退火温度对溅射沉积Pb(Zr0.52Ti0.48)O3铁电薄膜结构和性能的影响

在具有Ti缓冲层的Pt(111)底电极上,用射频溅射工艺在较低的衬底温度(370℃)和纯Ar气氛中沉积Pb(Zr0.52Ti0.48)O3(PZT)薄膜,沉积过程中基片架作15°摇摆以提高膜厚的均匀性。然后将样品在大气中进行5min快速热退火处理,退火温度550-680℃。用XRD、SEM分析薄膜的微结构,RT66A标准铁电测试系统测量样品的铁电和介电性能。结果表明,所沉积的Pt为(111)取向,仅当后退火温度高于580℃,沉积在Pt(111)上的PZT薄膜才能形成钙钛矿结构的铁电相,退火温度在580-600℃时结晶为(110)择优取向,退火温度高于600℃时结晶为(111)择优取向。PZT薄膜的极化强度随退火温度的升高而增加,但退火温度超过650℃时漏电流急剧上升,因此退火处理的温度对PZT薄膜的结构和性能有决定性的影响。