Preparation of uniform TiO2 nanostructure film on 316L stainless steel by sol-gel dip coating

Sol was prepared by the mixing of tetra-η-butyle titanat, ethyl aceto acetate, and ethanol in an optimized condition. Polished 316L specimens were coated with the sol by dip-coating method. The influences of drying condition, withdrawal speed, calcination temperature, addition of dispersant, and pH of sol on TiO₂ nanostructure coating were investigated. Choosing of alcohol as drying atmosphere hindered the crack formation. The relation between coating thickness and withdrawal speed was evaluated. The optimum temperature to create a uniform distribution of nanoparticles of anatase was derived as 400 °C. Average roughness of coating was found about 10.61 nm by AFM analysis. Dispersant addition promoted formation of a uniform film as well as prevention of agglomeration. Acidic sol provided smaller particles than neutral sol.     

Microstructure, bonding strength and thermal shock resistance of ceramic coatings on steels prepared by plasma electrolytic oxidation

Ceramic coatings were successfully prepared on steel by plasma electrolytic oxidation (PEO) in aluminate electrolyte and silicate electrolyte, respectively. The microstructure of the coatings including surface morphology, phase and element composition were studied by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. The bonding strength between the ceramic coating and the substrate was tested using different methods including tensile tests and shearing tests. The thermal shock resistance of the coatings was also evaluated. The results indicated that coatings obtained in both electrolytes were porous and coarse. The average diameters of the pores were below 10 μm. PEO coatings obtained in aluminate electrolyte were composed of Fe₃O₄ and FeAl₂O₄, while those obtained in silicate electrolyte were in a noncrystal state. PEO coatings obtained in aluminate electrolyte showed similar change trend of tensile strength and shearing strength with increasing treating time, namely, a relatively high values with middle time treating and low value with short and long time treating. The best coating was the samples treated with 30 min, whose tensile strength was 20.6 MPa and shearing strength was 16 MPa. The tensile strength and shearing strength of coatings obtained in silicate electrolyte were not strongly influenced by the treating time, the values of which were range in 14 ± 2 MPa and 11 ± 2 MPa, respectively. Coatings obtained in both electrolytes showed the best thermal shock resistance with middle time treating. Coatings obtained in silicate electrolyte show a little better thermal shock resistance than those obtained in aluminate electrolyte.     

重金属碲酸盐玻璃中Ho~(3+)的红外辐射特性

制备了高折射率Ho3+单掺和Ho3+/Yb3+共掺低声子能量重金属碲酸盐玻璃.根据Judd-Ofelt理论对吸收光谱进行拟合,求得Ho3+强度参数Ωt(t=2,4,6)分别为4.373×10-20,1.906×10-20和1.451×10-20cm2,并进一步计算了Ho3+在红外区各能级跃迁的振子强度、自发辐射跃迁概率、辐射寿命和荧光分支比等光谱参数.982 nm激发下,铋碲酸盐玻璃中Yb3+直接敏化Ho3+,在红外区产生有效红外发射.Ho3+吸收与发射截面在1.95和2.05μm处分别高达5.63×10-21和6.24×10-21cm2,大于Ho3+掺杂磷酸盐和氟化物玻璃,这有利于降低激光抽运阈值,实现高效Ho3+激光输出.较低的声子能量和较大的发射截面表明,Ho3+/Yb3+共掺杂铋碲酸盐玻璃有望成为良好的红外激光工作物质.     

自适应双边滤波红外弱小目标检测方法

针对红外弱小目标检测,提出一种基于自适应双边滤波的背景预测算法.该算法利用空域低通滤波和图像灰度信息的非线性组合,自适应的对背景进行预测,达到提高弱小目标检测性能的目的.仿真和实验表明：与小波滤波的检测算法相比,该算法能够更加有效地从结构化背景中检测目标抑制背景.     

Photophysics and Electrochemistry of some Thione Far-Red/Near-IR Triplet Emitters

The photophysics and cyclic voltammetry of two novel phosphorescent thiones, 2,2-dimethyl-indan-1-one-3-thione (DMIKT) and 2,2-dimethyl-indan-1,3-dithione (DMIDT), and three known phosphorescent thiones, 4H-pyran-4-thione (PT), 4H-1-benzopyran-4-thione (BPT) and 2,2-dimethylindan-1-thione (DMIT), have been characterised and compared. The phosphorescence emission of DMIT, DMIKT and DMIDT extends from the red into the near-IR spectral region. The additional carbonyl or thione group of DMIKT and DMIDT causes a significant shift in the emission maxima to 680 nm compared to that of DMIT, at 637 nm, in perfluorinated hydrocarbons. In acetonitrile the emission maxima of DMIKT and DMIDT are at 696 and 706 nm, respectively, and the spectra show vibronic bands which extend out beyond 850 nm. There is a significant reduction in triplet lifetime along this series (from 44 (±2) μs (DMIT) to 10 ((±0.8) μs (DMIKT) in perfluorinated solvents, and 8.6 (±0.5) (DMIT), 1.3 (±0.5) (DMIKT) and 0.35 (±0.07) μs (DMIDT) in acetonitrile), as well as a reduction in the rate constant for ground-state quenching of the triplet, (from 9.8 ((±0.9) to 3.5 ((±0.6) and 1.3 ((±0.2) × 10⁹ mol⁻¹ dm³ s⁻¹ for the same compounds). The addition of the C=O or C=S groups also causes a decrease in phosphorescence quantum yield with the highest emission quantum yield obtained for DMIT (Φ _P = 0.149 (±0.015)). Electrochemical studies show that while PT and BPT exhibit irreversible redox behaviour, DMIT, DMIKT and DMIDT all show at least one reversible reduction wave attributed to a one-electron process centred on the C=S moiety. The suitability of these lumophores for use in OLEDs is discussed.     

Ultimate performance of quantum well infrared photodetectors in the tunneling regime

Thanks to their wavelength diversity and to their excellent uniformity, Quantum well infrared photodetectors (QWIP) emerge as potential candidates for astronomical or defense applications in the very long wavelength infrared (VLWIR) spectral domain. However, these applications deal with very low backgrounds and are very stringent on dark current requirements. In this paper, we present the full electro-optical characterization of a 15 μm QWIP, with emphasis on the dark current measurements. Data exhibit striking features, such as a plateau regime in the I(V) curves at low temperature (4–25 K). We show that present theories fail to describe this phenomenon and establish the need for a fully microscopic approach.     

掺钼ZnO透明导电薄膜的太赫兹电磁波传输性质

采用直流磁控反应溅射方法,通过调节氧分压在玻璃基底上制备了不同载流子浓度的掺Mo的ZnO（ZMO）透明导电薄膜.应用太赫兹电磁波时域光谱技术研究了ZMO导电膜的太赫兹电磁波透射性质及介电响应,得到了与频率相关的电导率、能量吸收和薄膜折射率,实验结果与经典Drude模型相符很好.ZMO导电膜的太赫兹电磁波脉冲透射性质表明,通过调节ZMO薄膜的载流子浓度,该导电膜可作为应用于衬底和光学器件等太赫兹电磁波频率范围的宽带抗反射涂层. 关键词： 太赫兹电磁波光谱 薄膜电导率 宽带抗反射 透明导电薄膜     

准分子激光全固态脉冲电源设计与实验研究

针对脉冲能量5~8 mJ的ArF准分子激光器,设计了基于可控硅开关结合三级磁脉冲压缩开关的全固态脉冲电源,采用国产可控硅和磁开关材料,获得了上升时间约150 ns,电压10~14 kV,传递能量0.35~0.68 J的激励脉冲,并实现了对准分子激光器快放电激励。三级磁开关总效率35%,分析表明磁开关损耗较大主要原因为电容能量转移不充分、导线铜损及磁芯材料铁损较大,并提出了相应改进办法。     

Infrared Absorption Intensity Analysis as a New Tool for Investigation of Salt Effect on Proteins

通过观测红外光谱的强度变化研究了在不同温度下盐离子对谷氨酸和三种水溶性蛋白质(细胞色素C、DsbC和DsbC-G49R)的影响. 证实了Onsager反应场理论. 区分并且定义了随温度变化的蛋白质盐效应盐溶过程和解离过程. 同时利用Van't Hoff关系式对实验结果进行线性拟合,获得了蛋白质及其二级结构在上述两个过程中的热力学常数.     

选区激光烧结瞬态温度场模拟与测试方法研究

采用有限元方法,考虑实际的边界条件和热物性参量的变化,对Al2O3覆膜陶瓷粉末的选区激光烧结过程瞬态三维温度场进行动态模拟.通过比色测温法对红外热成像系统的发射系数进行修正后,对选区激光烧结过程瞬态温度场进行测试.数值模拟和实测结果显示,两者吻合较好.