Electrocatalytic Oxidation of Dopamine by Ferrocene in Lipid Film Cast on a Glassy Carbon Electrode

ＩｎｔｒｏｄｕｃｔｉｏｎＤＡｉｓｏｎｅｏｆｅｓｓｅｎｔｉａｌｐａｒｔｉｃｉｐａｎｔｓｉｎｔｈｅｎｅｕｒｏ ｔｒａｎｓｍｉｓｓｉｏｎｐｒｏｃｅｓｓｉｎｍａｍｍａｌｉａｎｃｅｎｔｒａｌｎｅｒｖｏｕｓｓｙｓ ｔｅｍ .ＡｌｏｓｓｏｆＤＡ ｃｏｎｔａｉｎｉｎｇｎｅｕｒｏｎｓｍａｙｒｅｓｕｌｔｉｎｓｏｍｅｓｅｒｉｏｕｓｄｉｓｅａｓｅｓｕｃｈａｓＰａｒｋｉｎｓｏｎｉｓｍ .1Ｓｉｎｃｅｉｔｓｄｉｓｃｏｖ ｅｒｙｉｎｔｈｅ 195 0ｓ ,ＤＡｈａｓｂｅｅｎｏｆｉｎｔｅｒｅｓｔｔｏｎｅｕｒｏｓｃｉｅｎ ｔｉｓｔｓａｎｄｃｈｅｍ…     

液相沉积法制备光催化活性TiO2薄膜和纳米粉体

采用液相沉积法，在35℃通过向六氟钛酸铵水溶液中添加硼酸和结晶诱导剂锐 铁矿型TiO2纳米晶，沉积出具有光催化活性的Ti02薄膜和纳米粉体．用XRD，AFM， 阶梯仪,UV-vis，BET法对Ti02薄膜和粉体的沉积条件、结构、厚度和性能进行了测 定和表征，并用亚甲兰的降解，评价了TiO2薄膜和纳米粉体的光催化活性．结果表 明，当反应物六氟钛酸铵与硼酸的摩尔比为1：2—1：4时，沉积的粉体和薄膜含有 锐钛矿相Ti02；经300℃热处理的Ti02薄膜和纳米粉体具有最高的光催化活性，它 的光催化活性是未经热处理前的5倍．本文还解释了经300℃热处理的薄膜和纳米粉 体具有最高光催化活性的原因．     

Interlayer Energy Transfer from Naphthalene to Anthracene Chromophores Organized in Langmuir—Blodgett Films

Interlayer energy transfer between 2,3-naphthol-10-hexadecylaza-15-crown-5(NC16) and N-[1-(9-methoxyanthryl)] decylaza-15-crown-5(A10C) within multilayer Langmuir-Blodgett films has been studied by steady-state fluorescence spectra. The donor and acceptor could be separated precisely by inserting stearic acid (SA) spacers. The efficiency of the energy transfer increases with the decrease in the donor-acceptor distance by a quadratic manner, suggesting the donor excitations are delocalized in the layer.     

A Transparent Thin Film with Hexagonal Mesostructure Containing Rhodamine 6G

A transparent this film was prepared by depositing the sol-gel mixture for the synthesis of MCM-41 mesoporous molecular sieve doped with rhodamine 6G(R6G) dye on glass substrates. The film of silica-surfactant-R6G materials, which was identified to possess hexagonally ordered mesostructure,was composed of nanocrystallites about 35 nm in diameter and 1-10μm in thickness. Cleanness of the substrates, concentration of the sol-gel mixture and rate of evaporation of the solvent were the key factors affecting transparency and homogeneity of the film. Moreover,optical change and lack in dye aggregation were observed to the R6G-functionalized MCM-41 thin film in contrast with that in ethanol solution.     

光降解性聚乙烯薄膜降解过程的表征

用全反射傅里叶红外光谱、Ｘ射线光电子能谱和示差扫描量热仪研究了含光敏剂的低密度聚乙烯薄膜在光降解过程中降解速率的变化规律，结果表明，光降解性聚乙烯薄膜在降解过程初期，降解速率很小，光敏剂显示抗氧化剂性能；降解２４ｈ后，降解速率迅速增加，直至薄膜破坏，光敏剂显示光引发剂性能。作为对比，同时研究了光敏剂和其它两种添加剂对聚乙薄膜光解速率的协同效应和两种添加剂体系显示的性能。     

STRUCTURE OF CRYSTALLINE DOMAINS IN SEMICRYSTALLINE BLOCK COPOLYMER THIN FILMS

Thin film morphology of a symmetric semicrystalline oxyethylene/oxybutylene diblock copolymer （E76B38） on silicon was investigated by tapping mode atomic force microscopy （AFM）. It is found that the nascent thin film is composed of multiple polymer layers having mixed thicknesses of L ≈ L0 and L ≈ L0/2 （L0 is the long period of the block copolymer in bulk） besides the first layer near the substrate. This shows that the crystalline domain in the block copolymer consists of double poly（oxyethylene） layers. Annealing leads to disappearance of the polymer layers with thickness L ≈L0/2, indicating that such polymer layers are metastable.     

表面活性剂模板在空气-水界面ZrO2薄膜中的稳定性

采用模板——十二烷基苯磺酸(DBS-H)在空气-水界面组装ZrO₂薄膜，研究了DBS-H在ZrO₂自组装薄膜中的水溶性、化学稳定性、热稳定性和光化学稳定性。模板的各类稳定性将直接控制ZrO₂薄膜结构，主要表现在层间距变化上。从模板与Na₂SiO₃反应的研究中获得了一种制备ZrO₂ / SiO₂复合氧化物薄膜的新方法，并推测出该复合薄膜的结构。     

厚度诱导的YBa2Cu3O7-δ超导薄膜剩余应力及临界电流变化

本文通过脉冲激光沉积法制备了不同厚度(80nm、320nm、1000nm和2000nm)的YBa2Cu3O7-δ(YBCO)超导薄膜,对它们的剩余应力和临界电流特性进行了对比研究.通过系列的激光显微Raman光谱和磁化曲线测量分别获得了薄膜剩余应力和磁化临界电流密度(Jc)对薄膜厚度的依赖关系.结果显示超导薄膜内剩余应力越小,Jc越高.对于中等厚度的薄膜样品(320nm和1000nm),其膜内剩余应力较小,同时由其特征的磁通匹配场大小推知在该厚度范围内的样品具有较高的线性缺陷密度,从而显示出较高的Jc值.     

凝固浴中物质极性对PAN结晶度的影响

采用恒温加热和双扩散两种脱除溶剂的方式制备PAN大分子薄膜,运用X射线衍射仪、傅里叶红外、紫外分光光度计等进行表征,研究凝固浴中沉淀剂极性对PAN大分子结晶度的影响。结果表明在凝固相分离过程中,沉淀剂对PAN大分子结晶度的影响是通过与氰基发生亲和作用实现的。沉淀剂极性越大,与PAN大分子之间亲合作用越强,对分子链的束缚越明显,使PAN分子调节自身构象变得困难,阻碍结晶的生长。电解质的加入能够弱化这种亲合作用,提高PAN的结晶度。