Effect of take-up speed on physical properties and permeation performance of cellulose acetate hollow fibers

Cellulose acetate (CA) ultrafiltration hollow fibers were spun via the dry-jet wet spinning technique. The effect of the take-up speed on the mechanical properties, morphology, thermal properties, pure water permeation, retention, and surface characterization of hollow fiber membranes were investigated. Both the inner and outer diameters of the hollow fiber decreased with the increase of take-up speed. Macrovoids were observed on the inner surface of the drawn hollow fibers. The d-space decreased with the increase of the take-up speed. The ultimate tensile stress (UTS) increased and the breaking elongation decreased with the increase of take-up speed. The permeation performance was measured. The hydraulic permeability increased and the retention decreased slightly with the increase of the take-up speed. The surface roughness increased with the increase of the take-up speed. The thermal analysis results showed that the endothermic peak shifts to the higher temperature region and coefficient of thermal expansion (CTE) decrease for a higher take-up speed.     

ξ-potential and surface dye-ability of poly(vinyl alcohol) fiber with different degree of formalization in a cationic dye solution

Summary The surface dyeability of the poly(vinyl alcohol) fiber with different degree of formalization was studied by measuring -potential of the fiber in alkaline aqueous solutions (pH 10) of a cationic dye Methylene Blue. With the increase in the dye concentration, the sign of the -potential of the fiber changed from negative to positive and thereafter the positive value approximated to saturated value, and the amount of dye adsorbed (expressed in mol/cm²-fiber) increased also. These results may possibly be attributed to the formation of the electrostatic bond between the fiber and the dye. The linear relations were found between and logC _d and its slope did not change with rise of temperature. The free energy of dyeing G (negative) calculated from the slope of the -logC _id curve, etc. increased with increasing the degree of formalization of the fiber. This fact corresponds to the increase in the surface dye adsorption with increasing the degree of formalization. With increasing the degree of formalization, the heat of dyeing H (negative) increased and the entropy of dyeing S (positive) decreased. The positive value of S for each fiber, suggests the formation of hydrophobic bond as a driving force to the dyeing of Methylene blue on the fiber surface in addition to the electrostatic bond.This paper is Part XXVII in a series on Studies on -potentials and Surface Dyeability of Natural and Synthetic Fibers in Dye Solution. Part XXVI: T. Suzawa andK. Kawakami, Nippon Kagaku Kaishi1975, No. 7,1134.     

二氧化钛纤维表面担载Pt纳米结构的原子力显微镜研究

通过原子力显微镜研究了二氧化钛纤维表面担载Pt的表面形貌及其结构.结果表明,TiO2纤维表面担载的Pt具有微米尺度的近似六边形或者近似长方形的结构,与在单晶TiO2(110)表面的Pt纳米簇形貌相似,但尺度较大.TiO2纤维担载的Pt表面明显存在不同高度的台阶结构,台阶高度以2~4倍Pt(111)晶面面间距的高度为主.由Pt在TiO2纤维表面的形貌与纤维的纳米晶粒排布有序性推测可知,Pt与TiO2纤维存在强的相互作用,可能正是这种强相互作用和表面台阶结构才使TiO2表面担载的Pt虽是微米尺寸但仍具有高光催化活性.     

Racemic ofloxacin separation by supported-liquid membrane extraction with two organic phases

As the relation of chirality and activities of drugs is researched deeply, people become to re-alize the clinic importance of chirality. The different enantiomers of a drug can have vastly differ-ent pharmacological activities, pharmacokinetic processes and toxicity[1,2]. The most well-docu- mented example is that of the drug substance thalidomide. Bitter lessons and scientific research promote the interest in single-enantiomer drugs, so the potential of the chiral drug market is enormous[3]. …     

聚酰亚胺中空纤维膜用于甲醇/甲基叔丁基醚的分离

甲醇／甲基叔丁基醚混合物的膜法分离，大多采用渗透汽化方法，少有采用蒸汽渗透法。用聚酰亚胺中空纤维膜，对以蒸汽渗透和渗透汽化两种方式分离甲醇／甲基叔丁基醚混合物（甲醇质量分数为0．01－0．30）的效果进行了对比。结果显示，在甲醇质量分数低于0．05时，蒸汽渗透较渗透汽化法的分离性能优越。     

Dehydration of tetrafluoropropanol (TFP) by pervaporation via novel PBI/BTDA-TDI/MDI co-polyimide (P84) dual-layer hollow fiber membranes

A novel PBI/P84 co-polyimide dual-layer hollow fiber membrane has been specifically fabricated through the dry-jet wet phase inversion process, for the first time, for the dehydration pervaporation of tetrafluoropropanol (TFP). Polybenzimidazole (PBI) was chosen as the outer selective layer because of its superior hydrophilic nature and excellent solvent-resistance together with robust thermal stability, while P84 co-polyimide was employed as the inner supporting layer because of its good solvent-resistance and thermal stability. The PBI/P84 membrane exhibits superior water selectivity and relatively high permeation flux. At 60 °C, the PBI/P84 dual-layer hollow fiber membrane shows a permeation flux of 332 g/(m² h) and a separation factor of 1990 for a feed solution containing of 85 wt% TFP. The preferential water sorption and the significant diffusivity difference between TFP and water are the main causes of high separation factor. However, an increase in feed temperature will greatly increase the permeation flux but seriously decrease the water selectivity. The activation energy data verify that water can preferentially permeate the PBI membrane due to the strong water affinity of PBI and a much smaller molecular size of water.     

Preparation of Tip‐Protected Poly(oxyphenylene) Coated Carbon‐Fiber Ultramicroelectrodes

A high‐yield, reliable, and reproducible method has been successfully developed to fabricate poly(oxyphenylene)‐coated carbon fiber ultramicroelectrodes (POCF UMEs) with tip radii r<2 μm. During the insulation process, the tip of the electrochemically etched electrode is protected by inserting it into an inert polymer while the remainder of the electrode is insulated by electrochemical deposition of a 1–3 μm thick poly(oxyphenylene) film. Optimum conditions for poly(oxyphenylene) deposition are developed and the resulting carbon fiber UMEs showed good cyclic voltammetric behavior even after storage for more than one year. These UMEs were tested for use as amperometric scanning electrochemical microscopy (SECM) tips and successfully imaged Au/Kel‐F and Al/SiC_p metal matrix composites.     

Mechanical properties of fiber reinforced styrene-butadiene rubbers using surface-modified UHMWPE fibers under EB irradiation

Aiming to develop a high performance fiber reinforced rubber of SBR, a special technique using electron beam (EB) irradiation-induced graft-polymerization was applied to ultra-high molecular-weight polyethylene (UHMWPE) fibers. Although UHMWPE is chemically inert, N-vinyl formamide (NVF) could be graft-polymerized onto the UHMWPE fiber surface with this special technique. A maximum grafting percentage of 23.6% was achieved. The composite of SBR and grafted UHMWPE fibers with maximum grafting indicated a linear increase in the initial modulus and strength with the fiber content. At the fiber content of 10%, the initial modulus was improved about five times with respect to that of the pure SBR, while the strength was done about twice. At this moment, only a small reduction could be observed in the strain compared with that of pure SBR. The fiber reinforced rubber with a good performance was obtained in the system of SBR and grafted UHMWPE fibers.     

Behaviors and mechanisms of copper adsorption on hydrolyzed polyacrylonitrile fibers

Polyacrylonitrile fiber (PANF) was hydrolyzed in a solution of sodium hydroxide and the hydrolyzed polyacrylonitrile fiber (HPANF) was used as an adsorbent to remove copper ions from aqueous solution. Scanning electron microscopy (SEM) showed that the hydrolysis process made the surface of HPANF rougher than that of PANF. Fourier transform infrared (FTIR) spectroscopy revealed that the HPANF contained conjugated imine (-Cz=Nz-) sequences. Batch adsorption results indicated that the HPANF was very effective in adsorbing copper, and the adsorption equilibrium could be reached within 10-20 min. Atomic force microscopy (AFM) showed that some aggregates formed on the surface of the HPANF after copper ion adsorption and the average surface roughness (R(a)) value of the HPANF changed from 0.363 to 3.763 nm due to copper adsorption. FTIR analysis indicated that copper adsorption caused a decrease of the light adsorption intensity of the imine (-Cz=Nz-) groups at 1573 and 1406 cm(-1) wavenumbers, and X-ray photoelectron spectroscopy (XPS) showed that the binding energy (BE) of some of the nitrogen atoms in the HPANF increased to a greater value due to copper adsorption. The FTIR and XPS results suggest that the adsorption of copper ions to the HPANF is attributed to the imine groups on the surface of the HPANF.     

左手材料阶跃型光纤的模场特性

从Maxwell方程组出发,讨论纤芯为左手材料,包层为右手材料阶跃型光纤,推导了矢量解的场方程.经过数学计算,求得了左手材料阶跃型光纤矢量解的特征方程.根据矢量模的分类,找到了TE模、TM模、HE模和EH模的特征方程.根据各模的特征方程,并且与右手材料光纤相关的特征方程,在靠近截止和远离截止两种情况下进行了比较,得到了左手材料光纤的某些奇异特性.