Relationship between chemical bond parameters and superconducting temperature in HgBa2Can−1CunO2n+2+δ (n=1, 2, 3, 4)

Bond covalency and valence of elements in HgBa₂Ca_n−1Cu_nO_2n+2+δ (n=1, 2, 3, 4) were calculated and their relationship with T_c was discussed. For both oxygen and argon annealed samples, the results indicated that with the increase of n, the trend of bond covalency of Hg-O and Cu-O was the same or opposite compared with that of superconducting temperature. This may suggest that the magnitudes of Cu-O and Hg-O bond covalency are important in governing the superconducting temperature. For the highest T_c sample, Hg had the lowest valence, implying that lower valence of Hg was preferred in order to produce higher T_c. For fixed n, the valence of Cu in oxygen annealed samples was larger than that in argon annealed samples, indicating that oxygen annealed samples produced more carriers than argon annealed samples.     

In situ neutron diffraction study (300-1273 K) of non-stoichiometric strontium ferrite SrFeOx

The high-temperature cubic phase of non-stoichiometric strontium ferrite SrFeO_x (2.5≤x≤3.0) has been studied by in situ neutron powder diffraction in air over the temperature range 300-1273 K. The composition of SrFeO_x changes within the range 2.56≤x≤2.81 from 1273 to 673 K, respectively.Rietveld refinements of the diffraction patterns show that the high-temperature cubic phase of SrFeO_x is consistent with a face-centred Fm3c structure. This structure leads to agreement with previous density measurements. This cell allows the high-temperature structure of SrFeO_x to be described in terms of a solid solution of the composition end members. Cubic SrFeO_x at high temperature is found to closely obey Vegard's law. The density of cubic SrFeO_x is also found to exhibit a linear relationship with composition.     

[Na(18-C-6)]2[Cu(i-mnt)2]的合成与结构分析

研究了18-冠-6与Na2[Cu(i-mnt)2][i-mnt=异丁二腈烯二硫醇阴离子,S2CC(CN)2-2]的反应,得到的配合物[Na(18-C-6)]2[Cu(i-mnt)2](1)通过元素分析、红外光谱、X射线单晶衍射进行了结构分析.配合物为单斜晶系,空间群P2(1)/c.晶体学结构数据a=1.2819(11),b=1.1793(10),c=1.4928(13)nm,β=99.121(16)°,V=2.228(3)nm3,Z=2,Dcaled.=1.369g/cm3,F(000)=958,R1=0.0521,wR2=0.1003.1中的[Cu(i-mnt)2]基团通过配体i-mnt的氮原子与两个[Na(18-C-6)]基团中的钠原子成键,形成稳定的中性配合物.     

Synthesis and characterization of new bis(1-aryliminomethylenylnaphthalen-2-oxy)nickel complexes and their catalytic behavior for vinyl polymerization of norbornene

The synthesized 1-aryliminomethylenylnaphthalen-2-ol derivatives reacted with nickel chloride to form bis(1-aryliminomethylenylnaphthalen-2-oxy)nickel complexes. All resultant compounds were structurally characterized by elemental analyses, IR and H NMR, and the structures of the formed complexes were elucidated by X-ray crystal structure analysis. The complexes show high catalytic activities for the vinyl polymerization of norbornene in the presence of methylaluminoxane. The catalytic activity variations have been followed by gas chromatography through monitoring the conversion of norbornene.     

A New Two‐Dimensional Coordination Polymer of Mercury(II) with very High Thermal Stability

A 2D Hg^II coordination polymer containing ligands 1,2,4‐triazole (Htrz) and thiocyanate, [Hg(μ₃‐trz)(SCN)]_n ( 1 ) has been synthesized and characterized by elemental analysis and IR spectroscopy. The single‐crystal X‐ray data show the coordination number of Hg atoms is four and the ligand trz^? acts as a three‐fold donor. The thermal stability of compound 1 was studied by thermal gravimetric and differential thermal analyses. The composition and formation of the complex in methanol solution were found to be in support of its solid state structure.     

Estimation of growth rate in unidirectionally solidified multicrystalline silicon by the growth-induced striation method

Multicrystalline silicon was grown by unidirectional solidification method using the accelerated crucible rotation technique. The application of the accelerated crucible rotation technique in unidirectional solidification method induced growth striations across the axial direction of the grown crystal. This striation pattern was observed from carbon concentration distribution, obtained by using Fourier transform infrared spectroscopy. The generated striation pattern was found to be weak and discontinuous. Some striations were absent, probably due to back melting, caused during each crucible rotation. From the growth striations and applied time period in crucible rotation, the growth rate was estimated by using Fourier transformation analysis.     

The structure of CeAlO3 by Rietveld refinement of X-ray powder diffraction data

The room temperature structure of perovskite CeAlO₃ has been reinvestigated by X-ray powder diffraction. The Rietveld refinement has confirmed the tetragonal symmetry; but revealed a super cell, a=5.32489(6) Å and c=7.58976(10) Å, with the space group I4/mcm. In CeAlO₃, the distortion from the ideal cubic perovskite is caused by the cooperative tilting of the AlO₆ octahedra around the primitive cubic [001]_p-axis.     

Synthesis and Crystal Structure of the Hydrogen Polyphosphide Bis(Tetraphenylphosphonium) hydrogenheptaphosphide‐ammonia(1/3) (PPh4)2HP7 · 3NH3

(PPh₄)₂HP₇ · 3NH₃ was prepared by the reaction of K₃P₇ with a proton‐charged ion exchange resin in the presence of (PPh₄)Br in liquid ammonia, and characterized by low temperature X‐ray structure analysis. The thermally very unstable compound contains the hydrogenheptaphosphide anion HPequation/tex2gif-stack-1.gif, the nortricyclane‐like cage of which is slightly distorted by the attachment of the hydrogen atom.     

Syntheses, Characterization and Crystal Structures of Two-dimensional 4,4''-Bipyridyl Lead Halides,PbI2 (4,4'' -bpy) and PbBr2 (4,4'' -bpy)

Two-dimensional 4,4-bipyridyllead halides, PbI2 (4,4'-bpy) (1) and PbBr2 (4,4'-bpy) (2), were synthesized. The structures were determined by means of X-ray single crystal diffraction.The structure shows a distorted octahedral configuration with six-coordinated central lead atoms. In crystals 1 and 2, the molecules are packed in a two-dimensional network structure through bridging halide atoms and 4,4'-bipyridine ligands between the adjacent lead atoms.     

Crystal structure and magnetic properties of two new cobalt selenite halides: Co5(SeO3)4X2 (X=Cl, Br)

Two new isostructural cobalt selenite halides Co₅(SeO₃)₄Cl₂ and Co₅(SeO₃)₄Br₂ have been synthesized. They crystallize in the triclinic system space group P−1 with the following lattice parameters for Co₅(SeO₃)₄Cl₂: a=6.4935(8) Å, b=7.7288(8) Å, c=7.7443(10) Å, α=66.051(11)°, β=73.610(11)°, γ=81.268(9)°, and Z=1. The crystal structures were solved from single-crystal X-ray data, R1=3.73 and 4.03 for Co₅(SeO₃)₄Cl₂ and Co₅(SeO₃)₄Br₂, respectively. The new compounds are isostructural to Ni₅(SeO₃)₄Br₂.Magnetic susceptibility measurements on oriented single-crystalline samples show anisotropic response in a broad temperature range. The anisotropic susceptibility is quantitatively interpreted within the zero-field splitting schemes for Co²⁺ and Ni²⁺ ions. Sharp low-temperature susceptibility features, at T_N=18 and 20 K for Co₅(SeO₃)₄Cl₂ and Co₅(SeO₃)₄Br₂, respectively, are ascribed to antiferromagnetic ordering in a minority magnetic subsystem. In isostructural Ni₅(SeO₃)₄Br₂ magnetically ordered subsystem represents a majority fraction (T_N=46 K). Nevertheless, anisotropic susceptibility of Ni₅(SeO₃)₄Br₂ is dominated at low temperatures by a minority fraction, subject to single-ion anisotropy effects and increasing population of S_z=0 (singlet) ground state of octahedrally coordinated Ni²⁺.