龋病人牙釉质表面硬度及抗磨损性能测试

采用人工方法制成人牙釉质浅龋及使用抗龋措施的龋损釉质样本，分别测量各组釉质表面显微硬度，并以微动摩擦磨损试验机测试其抗磨性能，试验结果表明：各组实验组釉质较对照组表面硬度都有不同程度下降，氟化钠前处理会使釉质表达硬度显著下降，人工浅龋牙釉质的抗磨损性能不如正常釉质，使用两种抗龋措施对其抗磨性能没有明显改善。     

Dependence of Performance of Organic Light-emitting Devices on Sheet Resistance of Indium-tin-oxide Anodes

IntroductionIndium-tin-oxide(ITO) has been widely used asthe anode material in organic light-emitting devices(OLEDs) because of its high transmittance in the visi-ble region and low electrical resistivity. In the pastyears, many investigations focused on …     

Scratch and Abrasion Resistant Coatings on Plastic Lenses—State of the Art,Current Developments and Perspectives

The manufacturing of ophthalmic lenses is one of the most important markets worldwide and, therefore, strong research efforts are undertaken to continuously improve the quality of the products, either silicate glasses or organic polymer lenses. Hybrid sol-gel based materials play a major role in this highly competitive field and have contributed significantly to the commercial success of the organic base materials. Recent developments concern fast curing and patternable coatings that might soon become part of this business. The compatibility of hybrid sol-gel materials either with organic dyes or with inorganic vacuum borne coatings offers further possibilities to develop highly sophisticated lenses meeting not only customer needs like perfect corrective function, high optical quality and protection, but also high durability as well as cosmetic and decorative aspects. An overview and a few recent developments are outlined below.     

Surface free energy of a solid from contact angle hysteresis

Nature of contact angle hysteresis is discussed basing on the literature data (Colloids Surf. A 189 (2001) 265) of dynamic advancing and receding contact angles of n-alkanes and n-alcohols on a very smooth surface of 1,1,2,-trichloro-1,2,2,-trifluoroethane (FC-732) film deposited on a silicon plate. The authors considered the liquid absorption and/or retention (swelling) processes responsible for the observed hysteresis. In this paper hysteresis is considered to be due to the liquid film left behind the drop during retreating of its contact line. Using the contact angle hysteresis an approach is suggested for evaluation of the solid surface free energy. Molecular spacing and the film structure are discussed to explain the difference in n-alkanes and n-alcohols behaviour as well as to explain the difference between dispersion free energy gamma(s)(d) and total surface free energy gamma(s)(tot) of FC-732, as determined from the advancing contact angles and the hysteresis, respectively.     

Surface modification of low density polyethylene (LDPE) film by low pressure O2 plasma treatment

In this work, low pressure glow discharge O₂ plasma has been used to increase wettability in a LDPE film in order to improve adhesion properties and make it useful for technical applications. Surface energy values have been estimated using contact angle measurements for different exposure times and different test liquids. In addition, plasma-treated samples have been subjected to an aging process to determine the durability of the plasma treatment. Characterization of the surface changes due to the plasma treatment has been carried out by means of Fourier transformed infrared spectroscopy (FTIR) to determine the presence of polar species such as carbonyl, carboxyl and hydroxyl groups. In addition to this, atomic force microscopy (AFM) analysis has been used to evaluate changes in surface morphology and roughness. Furthermore, and considering the semicrystalline nature of the LDPE film, a calorimetric study using differential scanning calorimetry (DSC) has been carried out to determine changes in crystallinity and degradation temperatures induced by the plasma treatment. The results show that low pressure O₂ plasma improves wettability in LDPE films and no significant changes can be observed at longer exposure times. Nevertheless, we can observe that short exposure times to low pressure O₂ plasma promote the formation of some polar species on the exposed surface and longer exposure times cause slight abrasion on LDPE films as observed by the little increase in surface roughness.     

Cu-P系稀土耐候钢中最佳稀土含量的研究

利用光学显微镜、图像分析仪和电子探针对低氧低硫的10PCuRE耐候钢板坯进行了观察和检测,采用干-湿周浸室内加速试验方法测得了试验钢的腐蚀率.用电化学方法测得了带锈样的阳极极化曲线.研究得出对于S:～0.004%,O:～0.002%的10PCuRE耐候钢,最佳稀土含量为0.0065%～0.012%,此稀土含量对非金属夹杂物的变质作用和耐蚀性能的提高最为有利.     

Resistance of supersulfated cement to strong sulfate solutions

One of the principal uses of supersulfated cement has been for structures exposed to sea water and sulfate bearing ground waters. The resistance to such environments has been related to the absence of calcium hydroxide and the combination of much of the free alumina into ettringite during hydration. This paper reports the resistance of SSC to sulfate solutions in which ettringite has been decomposed. Prism samples were subjected to initial water storage at 25°C for both 28 days and 6 months. Samples were also cured for 6 months at 95°C and at both 11% and 100% R.H. The control samples of 28 days were compared with the 6 months samples of a more mature undecomposed SSC paste. After curing the prisms were measured and all the samples were immersed in three sulfate solutions (0.7M Na₂SO₄ , 0.7M MgSO₄ and saturated CaSO₄), and water at the same time. Measurements of linear expansion over 6 months were carried out. Core and surface material following immersion was examined by DTG and XRD. The study indicated that SSC is resistant to sodium and calcium sulfate solutions. Strong magnesium sulfate solutions decomposed the samples under all conditions. A possible mechanism for this attack is suggested. This revised version was published online in July 2006 with corrections to the Cover Date.     

Influence of Some Aggressive Media on Corrosion Resistance of Mortars With Spent Cracking Catalyst

The influence of spent catalyst from catalytic cracking in fluidized bed on the hydration process of cement and the properties of cement mortars were studied. The spent catalyst was used as an additive to cement in the mortars (10 and 20% of cement). The samples of mortars kept in water for28 days, then they were placed in sulfate and chloride media for 2 months (the control samples were kept in water for 3 months). After this time they were subjected to bending strength and compressive strength determinations. Thermogravimetric and infrared absorption studies were performed and capillary elevation, capability of binding heavy metals, and changes in mass and apparent density were determined too. The studies disclosed the pozzolana nature of spent catalyst and its influence on cement mortars being in contact with corrosive media. This revised version was published online in August 2006 with corrections to the Cover Date.     

主动冷却点阵夹层防热结构温度响应计算模型北大核心CSCD

针对点阵夹层结构主动热防护问题,建立了夹层结构面板和芯体导热与冷却剂对流耦合的非稳态传热理论模型,利用有限体积法离散控制方程并在MATLAB中进行了迭代求解.模型首次考虑了面板与夹芯杆之间的收缩热阻,并利用分离变量法得到了收缩热阻的近似解析解.基于单胞模型和周期性边界条件,模拟得到了模型所需的表面对流传热系数h_(b)和h_(fin).最后,选取多单胞计算工况进行数值模拟和理论模型对比,并讨论了收缩热阻对模型预测精度的影响.结果表明:理论模型能够准确预测夹层结构及内部流体的温度变化,理论与仿真之间的最大误差不超过1%;随着外加热流密度不断增大,忽略收缩热阻使得计算结果造成的误差不断增大;与数值模拟相比,理论模型可显著地减少计算时间并节省计算资源,尤其适用于非均匀、非稳态复杂热载荷下点阵夹层结构的温度响应计算.     

Normalized Dynamic Characterization and Application of Multiple Heat Storage Materials Based on Standard Thermal Resistance北大核心CSCD

基于标准热阻和能量流法,推导出储热材料与换热流体的瞬态换热热阻,通过类比电路分析法,获得了储热-换热过程的瞬态热量流模型及动态响应时间常数。进一步引入节点温度,重新定义换热热阻,获得了储热与换热过程耦合的三阶电路瞬态热量流模型,求解得到了加热、储热和释热三类时间常数,可用于协同表征储热材料中储热与释热的快慢程度,从而实现了多类储热材料的归一化动态表征。通过数值模拟验证与应用对比分析,发现基于多时间常数的归一化动态模型用于表征储热材料的动态特性是可行的,可直接对不同换热、储热材料进行对比分析。案例分析发现与固体储热材料换热时,液态金属的动态换热能力优于熔融盐,而相比于水蒸气和CO₂,空气与陶瓷材料换热能更快达到稳态。