Structure and properties of the mesophase of syndiotactic polystyrene. VIII. Solvent sorption behavior of syndiotactic polystyrene/p‐chlorotoluene mesophase membranes

A crystalline δ form of a syndiotactic polystyrene (sPS) membrane was prepared from a solution of sPS (1 wt %) and p‐chlorotoluene (p‐CT) by a solution‐casting method. The mesophase (δ empty form) of sPS was obtained by the extraction of the guest solvent from the δ form of sPS by a stepwise solvent‐extraction method. The sPS/p‐CT mesophase membrane [p‐CT (A‐M)] was used for the sorption of 1 mol % p‐CT for different times and for the sorption of different concentrations of p‐CT, chlorobenzene (CB), p‐xylene (p‐X), toluene, and chloroform for 48 h. The presence of solvents in the sPS membrane was confirmed by IR analysis. A thermal study revealed that the sorption amount of 1 mol % p‐CT increased with increasing immersion time, and the sorption amounts of different solvents increased with increasing solvent concentration. Differential scanning calorimetry results showed that the desorption peak temperature increased as the amount of the solvent increased in the clathrated sPS membrane. Wide‐angle X‐ray diffraction results showed that 2θ at 8.25° was slightly shifted toward 8°, and there was no change in the peak position at 10° for p‐CT (A‐M), which was immersed in different solvents (1 mol %); however, the intensity of 2θ at 10° was not similar for all the samples. Among the solvents used for the sorption studies at 1 mol %, p‐CT (A‐M) could sorb more p‐CT and CB than p‐X, toluene, and chloroform. The solvent sorption isotherm was the Langmuir sorption mechanism. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3439–3446, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

Toughness mechanism in polypropylene composites: Polypropylene toughened with elastomer and calcium carbonate

Polypropylene (PP) was modified with elastomer or CaCO₃ particles of two different sizes (1 μm and 50 nm) in various volume fractions. The dispersion morphology and mechanical properties of the two systems were investigated as functions of the particle size and volume fraction of the modifier. The brittle‐to‐tough transition occurred when the matrix ligament thickness was less than the critical ligament thickness, which was about 0.1 μm for the PP used here, being independent of the type of modifier. At the same matrix ligament thickness, the improvement of the toughness was obviously higher with the elastomer rather than with CaCO₃, but adding CaCO₃ increased the modulus of PP. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1656–1662, 2004     

Ba（n，x）~（134）Cs，~（134）Ba（n，2n）~（133）Ba，

用中子活化法相对于５４Ｆｅ（ｎ，Ｐ）５４Ｍｎ反应，在１３．５０—１４．８０ＭｅＶ中子能区测量了Ｂａ（ｎ，ｘ）１３４Ｃｓ，１３４Ｂａ（ｎ，２ｎ）１３３Ｂａ，１４０Ｃｅ（ｎ，２ｎ）１３９Ｃｅ，１４２Ｃｅ（ｎ，２ｎ）１４１Ｃｅ和２３Ｎａ（ｎ，２ｎ）２２Ｎａ的反应截面．并将所测的结果和其他作者的结果进行了比较，中子能量是用９０Ｚｒ（ｎ，２ｎ）８９ｍ＋ｇＺｒ反应和９３Ｎｂ（ｎ，２ｎ）９２ｍＮｂ反应截面比法测定的。     

The epitaxial growth of gaas using alkylarsine: Part 2. molecular orbital calculation

Semi-empirical molecular orbital calculations were carried out for the compounds (C₂H₅)₃As, (C₂H₅)₃Ga and RAsH₂ (R = C₂H₅, i-C₃H₇, i-C₄H₉, and t-C₄H₉) by using the CNDO/2-U program, and their capability of β-elimination reaction is compared on the basis of the torsion energy to the transition state, electrostatic interactions and orbital overlapping between the central atom and the β-hydrogen, and bond order of the metal-carbon, and carbon-hydrogen bond. In the comparison of (C₂H₅)₃As with (C₂H₅)₃Ga, we found that the β-elimination of (C₂H₅)₃As could hardly be expected to take place in the thermal decomposition. The capability of β-elimination would be smaller in C₂H₅AsH₂ than that in (C₂H₅)₃As. Moreover when the ethyl group is replaced by a t-butyl group in RAsH₂, the β-elimination reaction appears to become more difficult and a large possibility for a radical process is suggested.     

Shape transition from InAs quantum dash to quantum dot on InP(3 1 1)A

We report on the shape transition from InAs quantum dashes to quantum dots (QDs) on lattice-matched GaInAsP on InP(3 1 1)A substrates. InAs quantum dashes develop during chemical-beam epitaxy of 3.2 monolayers InAs, which transform into round InAs QDs by introducing a growth interruption without arsenic flux after InAs deposition. The shape transition is solely attributed to surface properties, i.e., increase of the surface energy and symmetry under arsenic deficient conditions. The round QD shape is maintained during subsequent GaInAsP overgrowth because the reversed shape transition from dot to dash is kinetically hindered by the decreased ad-atom diffusion under arsenic flux.     

Poly(L‐lysine) and clay nanocomposite with desired matrix secondary structure: Effects of polypeptide molecular weight

Nanocomposites (NC) were formed using cationic poly(L ‐lysine) (PLL), a semicrystalline polypeptide, that was reinforced by sodium montmorillonite (MMT) clay via solution intercalation technique. By varying solution conditions such as pH, temperature, and polypeptide concentration in the presence of clay platelets, the secondary structure of PLL was controllably altered into α‐helical, β‐sheet, and random coil. The high molecular weight polypeptide shows a strong propensity to fold into the β‐sheet structure when cast as films, irrespective of the initial secondary structure in solution. Nanocomposite local morphology confirms intercalated MMT platelets with PLL over a wide range of compositions. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 239–252, 2007.     

Influence of organic modifiers on morphology and crystallization of poly(ϵ‐caprolactone)/synthetic clay intercalated nanocomposites

ε‐caprolactone was polymerized in the presence of neat montmorillonite or organomontmorillonites to obtain a variety of poly(ε‐caprolactone) (PCL)‐based systems loaded with 10 wt % of the silicates. The materials were thoroughly investigated by different X‐ray scattering techniques to determine factors affecting structure of the systems. For one of the nanocomposites it was found that varying the temperature in the range corresponding to crystallization of PCL causes reversible changes in the interlayer distance of the organoclay. Extensive experimental and literature studies on this phenomenon provided clues indicating that this effect might be a result of two‐dimensional ordering of PCL chains inside the galleries of the silicate. Small angle X‐ray scattering and wide angle X‐ray scattering investigation of filaments oriented above melting point of PCL revealed that polymer lamellae were oriented perpendicularly to particles of unmodified silicate, while in PCL/organoclay systems they were found parallel to clay tactoids. Calorimetric and microscopic studies shown that clay particles are effective nucleating agents. In the nanocomposites, PCL crystallized 20‐fold faster than in the neat polymer. The crystallization rate in nanocomposites was also significantly higher than in microcomposite. Further research provided an insight how the presence of the filler affects crystalline fraction and spherulitic structure of the polymer matrix in the investigated systems. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2350–2367, 2007     

Isothermal crystallization kinetics of poly(3‐hydroxybutyrate)/layered double hydroxide nanocomposites

Poly(3‐hydroxybutyrate) (PHB)/layered double hydroxides (LDHs) nanocomposites were prepared by mixing PHB and poly(ethylene glycol) phosphonates (PEOPAs)‐modified LDH (PMLDH) in chloroform solution. Both X‐ray diffraction data and TEM micrographs of PHB/PMLDH nanocomposites indicate that the PMLDHs are randomly dispersed and exfoliated into the PHB matrix. In this study, the effect of PMLDH on the isothermal crystallization behavior of PHB was investigated using a differential scanning calorimeter (DSC) and polarized optical microscopy. Isothermal crystallization results of PHB/PMLDH nanocomposites show that the addition of 2 wt % PMLDH into PHB induced more heterogeneous nucleation in the crystallization significantly increasing the crystallization rate and reducing their activation energy. By adding more PMLDH into the PHB probably causes more steric hindrance of the diffusion of PHB, reducing the transportation ability of polymer chains during crystallization, thus increasing the activation energy. The correlation among crystallization kinetics, melting behavior and crystalline structure of PHB/PMLDH nanocomposites can also be discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3337–3347, 2006     

Controlled/living polymerization of 2‐(diethylamino)ethyl methacrylate and its block copolymer with tert‐butyl methacrylate by atom transfer radical polymerization

Polymerization of 2‐(diethylamino)ethyl methacrylate (DEAEMA) via homogeneous atom transfer radical polymerization under various reaction conditions is described. The effects of the initiators and solvents were examined. With 1,1,4,7,10,10‐hexamethyl triethylenetetramine/copper(I) chloride/p‐toluenesulfonyl chloride as the ligand/catalyst/initiator system in methanol, poly(DEAEMA) with a polydispersity index as low as 1.07 was synthesized. Kinetic studies demonstrated the polymerization was very well controlled and exhibited the living characteristic of the process. Well‐defined block copolymers of DEAEMA and tert‐butyl methacrylate (tBMA) were successfully synthesized. The copolymers could be synthesized with equally good results by starting with either p(DEAEMA) or p(tBMA) as the macroinitiators. However, only the macroinitiators terminated with chlorine should be used. The corresponding macroinitiators with bromine as a transferable group did not yield well‐defined copolymers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2688–2695, 2003