激光熔覆硬质合金强化化纤切断刀的研究

在机械压制法预置硬质合金WC/Co粉末的条形55Si2Mn弹簧钢上,用激光熔覆方法制备了化纤切断刀.调整熔覆层粉末配方中Al、TiC的加入量,结果表明加适量的Al粉能有效地抑制气孔,加TiC粉末能提高熔覆硬度.通过优化激光熔覆工艺参数,得到了无气孔缺陷、组织性能良好、硬度达到HV0.21250的激光熔覆层,达到了化纤切断刀的性能要求.     

Ni-B非晶态合金催化苯丙酮酸加氢合成苯丙氨酸

通过化学还原法制备了纳米非晶态Ni-B合金催化剂,考察了其对苯丙酮酸胺化加氢合成苯丙氨酸的催化性能.结果表明,相对于传统雷尼镍和漆原镍催化剂,非晶态合金催化剂表现出更为优异的活性和选择性,并且当非晶态Ni-B合金负载在SiO2载体上时,其活性和选择性均得到较大提高(高达97.67%).非晶态合金催化剂对苯丙氨酸合成反应表现出较好活性和选择性的原因主要是硼提供部分电子给镍的效应以及非晶态合金颗粒的纳米尺寸效应.     

SnSxSe2-x单晶纳米片的可控制备与表征

锡二硫族化合物可以通过改变硫和硒的含量来连续调控三元合金材料的带隙、载流子浓度等物理化学性质,在电子和光电子器件应用上具有巨大的潜力。本文采用化学气相沉积(CVD)技术可控地制备了不同元素组分的SnS_xSe_2-x(x=0,0.2,0.5,0.8,1.0,1.2,1.5,1.8,2.0)单晶纳米片。采用扫描电子显微镜(SEM)、原子力显微镜(AFM)、能量色散X射线光谱(EDS)、透射电子显微镜(TEM)以及拉曼光谱等手段对SnS_xSe_2-x纳米片进行了综合表征。结果表明本方法成功实现了元素百分比可调的SnS_xSe_2-x单晶纳米片的可控制备。重点研究了依赖于元素百分比的SnS_xSe_2-x的拉曼特征谱,实验结果与基于密度泛函理论(DFT)的第一性原理计算得到的SnS_xSe_2-x的拉曼仿真谱高度吻合,理论计算结果较好地诠释了实验拉曼光谱发生变化的原因。本研究提供了一种元素百分比可调的三元SnS_xSe_2-x单晶纳米片的可控制备方法,同时对锡二硫族化合物的明确、无损识别提供了方案。     

形状记忆合金椭圆孔口问题的有限单元法

基于Lagoudas形状记忆合金(SMA)三维本构模型,假设材料为各向同性,推导了SMA平面应力状态的增量型本构方程,继而编写了ABAQUS用户自定义材料(UMAT)子程序,研究了在双向拉伸情况下,外载荷、温度、椭圆孔口长短轴之比对超弹性SMA椭圆孔口板中应力诱发马氏体相变区的影响。数值结果表明:应力诱发马氏体相变首先发生在椭圆孔口长轴端点部位,在外加载荷作用下逐渐扩展到板内,并由内向外形成马氏体相区、相变混合区和奥氏体相区;SMA板内应力诱发马氏体完全相变区面积与施加外载荷成正相关,与温度成负相关;随着椭圆孔口长短轴之比增大,SMA板内应力诱发马氏体完全相变区面积呈现出先减小后增大的趋势;拉应力差值相同时,相较于拉应力沿椭圆孔口长轴方向较大的情况,当拉应力沿椭圆孔口短轴方向较大时,SMA板内完全相变区面积较大,椭圆孔口周边应力集中现象更明显。     

镁及镁合金中微量磷的测定方法研究

磷与钼酸铵形成磷钼杂多酸络幌物,用乙酸丁酯萃取分离,用SnCl2还原反萃取后借磷钼蓝光度法测定镁及镁合金中微量磷。在波长700 nm处工作曲线线性范围0~1.5μg/mL,相关系数为0.9995,络合物表观摩尔吸光系数ε=1.45×104L.mol-1.cm-1,相对标准偏差在1.40%~3.10%之间,加标回收率在99.3%~101.0%之间,本法与ICP法相对照结果比较满意。     

混合稀土储氢合金中氧和氮的测定

研究了混合稀土储氢合金中氧和氮的测定方法。针对稀土金属高温易挥发、分解的特点,选择适宜的加热温度,使用镍浴,选择高温座坩埚进行试验：选择出了合适的助熔剂的预处理方法。方法已用于实际样品。对含氧0．43％、含氮0.018％的试样,分析精密度为氧4．3％,氮5.9％,加标回收率氧为93％～104％,氮为92％～110％。     

Effects on the evolution of microstructure and properties of low-silicon cast aluminum alloys in service

ABSTRACT

The microstructure evolution and property change of four kinds of low silicon cast aluminum alloy exposed to heat for 0–50?h at 200°C were studied by means of Brinell hardness test, tensile property test, friction and wear property test and XRD analysis. The results show that with increasing thermal exposure time, the tensile strength of each group of samples decreased and the amount of wear increased. The tensile strength of samples with more Si content decreased slowly. When the time increased to 50?h, the increase of wear loss was the largest. The hardness of samples after thermal exposure increases compared with that before thermal exposure. The residual stress of (311) diffraction crystal surface of AlSi3.5Mg0.66 under different thermal exposure time was measured. The type of residual stress changed from residual tensile stress to residual compressive stress after thermal exposure. There is an abnormal phenomenon that the hardness of the sample increased and the amount of wear increased, and it is evident that the distribution of residual stress was inhomogeneous after thermal exposure. It is found that with increasing thermal exposure time to 50?h, the average lattice distortion ε of the low-index crystal plane and the high-index crystal plane in the aluminum alloys gradually increased.     

快凝Pd82Si18合金原子团簇的演化特性及遗传机制

采用分子动力学(MD)模拟计算,对Pd82Si18合金快凝过程中基本原子团簇的遗传特性、演化趋势和结构稳定性进行了研究.团簇类型指数法(CTIM)分析表明:非晶固体中Si原子为中心的(102/14418/1551)双帽阿基米德反棱柱(BSAP)团簇数目占据优势.快凝过程中,BSAP结构团簇具有最大的遗传分数,并且其他以Si原子为中心的Kasper团簇大多都会向BSAP结构团簇转变.通过对Si原子为中心的Kasper基本团簇电子性质第一性原理计算发现,体系中BSAP团簇的结合能最低,结构稳定性较高,与分子动力学计算结果一致.     

锆系Laves相储氢合金电极的性能研究

Ｚｒ（Ｖ０．２Ｍｎ０．２Ｍｏ０．０６Ｎｉ０．５４）２．４合金经ＨＦ溶液处理后，合金表面由富Ｚｒ和富Ｍｎ层转变成富Ｎｉ层，从而使电极初期活化周期明显缩短，电极表面氢吸附性能改善。表面反应电阻减小。本文探讨了上述电极表面反应机理，即表面Ｎｉ的催化、氢吸附和氢转移机理，对阻抗谱进行拟合，给出了相应的电极反应等效电路。     

碱性电镀光亮锌镍合金研究

在总结镀液的电化学特性和锌镍合金镀层的晶体结构与性能等实验结果的基础上,提出碱性电镀光亮锌镍合金的工艺规范和直接把锌酸盐镀锌液转化为碱性电镀光亮锌镍合金镀液的方法。生产实践证明,该工艺稳定,镀层光亮、耐腐性好、硬度较高、无氢脆,镍含量可在９～２０ｗｔ％范围内随意控制。