ZSM-5分子筛膜的研究进展

本文分析了ZSM-5分子筛膜的主要合成方法和研究现状,总结了ZSM-5分子筛膜的缺陷与修饰方法,指出了ZSM-5分子筛膜的表征手段是以XRD、SEM、TEM和单组分气体渗透等为主,对ZSM-5分子筛膜的应用和前景进行了展望。     

SYNTHESIS OF CROSS-CONJUGATED （p-PHENYLENE）S-POLY（p- PHENYLENEVINYLENE）S HYBRIDS WITH LOW CONTENT OF STRUCTURAL DEFECTS

The novel shish-kebab-type liquid crystalline cross-conjugated （p-phenylene）s-poly（p-phenylenevinylene）s hybrid was synthesized through Gilch polymerization. Their structures and properties were characterized by NMR, GPC, DSC, X-ray diffraction and polarizing optical microscope （POM）. ^1H-NMR investigation of the polymers indicates that the shish-kebab-structure has a strong ability to suppress the structural defects in the polymers. The polymers are enantiotropic liquid crystals. The melting point （Tm） of the polymers decreases when the length of the alkoxy tails of the mesogenic units increases. The mesophase was identified by X-ray diffraction method. They showed not only a smectic LC phase, but also a strong green fluorescence in chloroform. The maximum absorption band of the ＂kebabs＂ of the two, 5-bis（4＇- alkoxyphenyl）benzene at 280 nm did not appear in absorption spectra of the polymers. The same phenomena were also observed in the fluorescence spectra. These results imply that the polymers have formed a cross-conjugated uniform structure and achieved an extended n-conjugation polymer.     

亚锰酸镧及其A位掺杂物的结构与缺陷

鉴于亚锰酸镧的结构和缺陷在理论和应用上的重要性,本文总结了近年来对LaMnO3及其A位掺杂物的结构与缺陷的研究.着重分析了其氧化学非计量性和La/Mn比与结构及缺陷的关系.并讨论了亚锰酸镧的各种缺陷模型.指出了目前研究中存在的一些争议和一些缺乏足够研究的方面.     

聚氯乙烯结构缺陷和热不稳定性之间关系的研究 2.各种结构缺陷含量和热脱氯化氢速率之间的关系

本工作采用溴加成法、酚解法、FTIR法及臭氧裂解法分别测定了五种不饱和蒸气压下聚合的PVC样品(u-PVC)和五种商品PVC样品(s-PVC)的总双键、总不稳定氯、孤立双键和内部双键的含量.通过研究结构缺陷和PVC的平均分子量及脱HCl速率的相互关系,揭示了不饱和总双键值,总不稳定氯和孤立双键含量彼此的相关性是建立在它们分别与1/M_n的相关性基础之上,从而得出了这三种定量值测得的主要都是端基烯丙基氯结构.根据三者对脱HCl速率的良好线性相关性,首次提出了端基烯丙基氯结构在HCl催化作用下异构化成内部烯丙基氯从而成为脱HCl速率主要原因的机理.     

用正电子湮没寿命谱法研究锡镀层缺陷

光亮镀锡工艺由于成本低、无毒、镀层稳定性好而广泛应用于电子元器件引线的电镀.但因锡镀层与基体之间会发生原子的相互扩散,致使产品在储存、焊接或使用期间因温度效应而使某些重要的物理和化学性能,如钎焊性、导电性和防腐性变差。金属界面原子的热扩散行为与金属晶体的结构缺陷密切相关,因此应用正电子湮没寿命谱法研究锡镀层在热处理过程中缺陷的运动规律,在理论和工艺方面都具有重要的意义。     

钐对锰激活的硼硅锌存储玻璃的影响

使用高温固相法合成了钐锰共激活的硼硅锌玻璃. 利用热释光谱研究了钐的掺入对锰激活的硼硅锌玻璃的陷阱能级的影响, 发现钐的掺入使后者的缺陷向浅能级方向移动, 表现为锰激活的硼硅锌玻璃的余辉和存储性能的相应变化.     

SrTi0.9M0.1O3-δ钙钛矿型氧化物催化剂甲烷氧化偶联反应性能的研究

The structure and catalytic properties of SrTi_0.9M_0.1O_3-δ (M=Mg，Al， Zr) perovskite-type catalysts for ox-idative coupling of methane (OCM) have been studied by using X-ray diffraction (XRD)，X-ray photoelectron spectroscopy (XPS) and temperature-programmed desorption of oxygen(O₂-TPD) methods. It has been shown that doping the cations of lower valence (e.g. Mg²⁺， Al³⁺) to the B site of SrTi_0.9M_0.1O_3-δ perovskite-type catalysts results in the higher content of adsorbed oxygen species on the surface of catalysts and thus higher C₂-selectivity for OCM reaction. It is suggested that the oxygen vacancies of SrTi_0.9M_0.1O_3-δ (M=Mg， Al， Zr) perovskite-type catalysts are the sites responsible for oxygen activation， and the adsorbed oxygen species on the surface of SrTi_0.9M_0.1O_3-δ catalysts are the main active species for OCM reaction.     

O2在MgO(001)完整和缺陷表面上的吸附

在密度泛函理论的框架下， 采用嵌入点电荷簇模型研究了O2在MgO(001)完整和缺陷表面上的吸附.用电荷自洽的方法确定了点电荷的值.计算结果表明， O2倾向吸附在低配位的角Mg2＋端.并且发现， 当O2为平躺吸附时，键长有较大的拉伸，将有利于O2的解离.同时，分别计算了使用裸簇和嵌入表观±2.0 e点电荷簇模型时的吸附能，并与采用电荷自洽方法的计算值进行了比较.结果表明，电荷自洽方法更能有效反映簇周围的环境，得到的计算结果能够较好地与实验值吻合.最后，分别计算了不同吸附情况下O2的振动频率.     

ZnO荧光粉中的紫外发射和绿色发射之间的关系

通过在低氧分压和真空中热处理ZnO粉末, 获得了ZnO荧光粉. ZnO荧光粉有两个发射谱带, 分别位于380 nm(紫外)和510 nm(绿色). 紫外谱带对应于ZnO中的激子发射, 是一个单中心发光过程；绿色谱带是一个复合发光过程, 与ZnO中的本征缺陷相关, 如氧空位、锌空位等. 实验表明, 高密度的激发条件有利于紫外发射, 而低氧分压下的热处理有利于提高绿色发射谱带的强度. 研究结果还表明, 与紫外发射相联系的激子可向与本征缺陷相联系的绿色发光中心传递能量, 这种传递可能是通过激子扩散实现的.     

柠檬酸溶胶-凝胶法制备的Ce1-xZrxO2: 结构及其氧移动性

采用 XRF、XRD、Raman、XPS、H₂-TPR 以及与氩离子刻蚀相结合的XPS等表征技术对柠檬酸溶胶-凝胶法制备的Ce_1-xZr_xO₂ (0≤x≤1)样品的结构及其氧移动性进行了研究. 结果表明, Ce_1-xZr_xO₂ 样品的晶型结构对其中氧的移动性有明显影响. 当x≤0.15 时, Ce_1-xZr_xO₂ 以立方CeO₂相 Ce-Zr-O 固溶体存在, 随着Zr含量的逐渐增加, CeO₂晶胞体积减小、氧空位浓度增加, 氧移动性逐渐增强; 当x＞0.15时, 形成四方ZrO₂相和立方CeO₂相Ce-Zr-O固溶体的混合物, 随着Zr含量的逐渐增加, 四方ZrO₂相的含量增加、氧空位浓度减小, 氧移动性逐渐减弱. 因此, Ce_0.852Zr_0.152O₂样品具有最高的氧移动性.