γ-Fe2O3/Ag/TiO2的制备与抗菌性能

采用两步法合成了γ-Fe₂O₃/Ag/TiO₂复合光催化剂, 以大肠埃希氏菌(E. coli)为目标菌, 对数去除率为评价指标评价了催化剂的抗菌性能, 优化了催化剂的最佳制备参数. 通过X射线衍射、 扫描电子显微镜、 X射线光电子能谱和紫外-可见漫反射光谱等手段对催化剂进行了表征. 结果表明, 当Ti/Ag摩尔比为1:0.05, 煅烧时间为3 h, 煅烧温度为350 ℃时, γ-Fe₂O₃/Ag/TiO₂表现出最佳抗菌活性. 复合催化剂具有介孔结构, 比表面积为89.1 m²/g; 光吸收边界达690 nm, 有良好的可见光响应能力; 磁性较强, 在水处理应用中可有效分离和重复使用. 反应条件不受光源限制, 在有/无光照下均具有良好的抗菌活性, 且太阳光辐照下对E. coli的对数去除率可达6.28.     

用于生物检测的链霉亲和素修饰γ-Fe2O3@Au复合颗粒的制备与表征

制备了粒径为30 nm左右的γ-Fe₂O₃磁性颗粒, 利用巯基硅烷(MPTES)的偶联作用最终制备了粒径约为35.9 nm的金磁复合颗粒. 用X射线粉末衍射仪(XRD)、透射电子显微镜(TEM)、紫外可见吸收光谱(UV-Vis)、傅里叶变换红外光谱(FT-IR)、振动样品磁强计(VSM)等方法对所得金磁颗粒的表面形貌、大小、结构、光学和磁学性质进行了表征. 结果表明: 金成功地包覆到了γ-Fe₂O₃颗粒的表面, 所得金磁颗粒具有超顺磁性. 利用静电吸附作用, 链霉亲和素有效修饰到了γ-Fe₂O₃@Au复合磁性颗粒表面. 通过扫描仪检测其捕捉Cy3标记寡核苷酸序列后的荧光信号, 证明了链霉亲和素修饰的γ-Fe₂O₃@Au复合磁性颗粒有生物活性, 且没有荧光背景, 在生物检测领域表现出了很大的应用前景.     

γ-Fe2O3纳米粉的低热固相制备及其电磁损耗特性(英)

The Fe(OH)₃ precursor was prepared by solid -state reaction with Fe(NO₃)₃·9H₂O, NaOH and dispersed poly-ethylene glycol at low heating temperature(25 ℃). Synthesis of iron oxide (γ-Fe₂O₃) nanoparticle was achieved by thermal decomposition of Fe(OH)₃·xH₂O precursor. The nanoparticle was characterized by TG-DTA, X-ray diffra-ction, TEM etc. The results showed that the nanoparticle was composed of γ-Fe₂O₃ and was a better absorber for electromagnetic wave within the low frequency band.     

准立方体纳米α-Fe_2O_3的制备及光催化活性研究

本文利用无表面活性剂条件,以氨水和醋酸锌为形貌调控剂,通过水热法合成了准纳米立方块结构的α-Fe2O3。并利用X射线衍射、透射电子显微镜、扫描电子显微镜对产物的形貌进行了的表征,对其形成机理进行了初步的解释。同时对其光催化降解活性进行了研究。     

高温高压方法合成碳包覆γ-Fe_2O_3纳米棒及其磁学性能

采用高温高压(HPHT)方法,以水热法制备的聚乙烯醇包覆FeOOH纳米棒为前驱体,合成了碳包覆γ-Fe2O3纳米棒.通过使用多种表征方法,研究了HPHT过程中合成温度对样品结构和形貌的影响,并对样品的生长机理进行了探讨.利用振动样品磁强计测量了样品的室温磁学性质.实验结果表明,反应温度为400?C,压强为1 GPa条件下制备的碳包覆γ-Fe2O3纳米棒具有较高的长径比(直径约为20 nm,长度约为150 nm),矫顽力可达到330 Oe(1 Oe=79.5775 A/m).该方法为制备具有核壳结构的一维纳米材料提供了新思路.     

一种新型纺锤状α-Fe_2O_3纳米晶的合成、表征及其表面性能(英文)

合成了一种新型的具有单晶结构的α-Fe2O3纳米晶(NFO-1).在我们的合成方法中,样品的形貌和结构在低反应浓度体系中运用无机盐和有机模板进行双重调控,同时用溶剂挥发诱导自组装(EISA)来加速反应和在不改变形貌结构的前提下获得高产率样品.所得α-Fe2O3纳米晶的形貌和结构对其表面修饰功能有明显的影响,NFO-1因其特殊的纺锤状形貌而与表面功能试剂(多巴胺)之间的化学作用有明显的增强.并且,本文所描述的合成方法同样适用于其他过渡金属氧化物纳米单晶的合成.我们预期,这种方法可为新型纳米材料的合成提供新的途径.     

Coupled perpendicular magnetization in Fe/Cu/Fe trilayers

Ultrathin epitaxial Fe films on Cu(1 0 0) with perpendicular magnetization have been used as templates for the preparation of FCC Fe/Cu/Fe trilayers. The magnetic anisotropy and the coupling of these films have been studied by in-situ magneto optical Kerr effect measurements and Kerr microscopy. The magnetic coupling of both Fe layers is found to be dominated by magnetostatic interaction. Adsorbate-induced spin reorientation in the top layer also causes spin reorientation in the bottom layer. The governing role of the Fe-vacuum interface for the magnetism of the whole trilayer is demonstrated.     

Hard magnetic properties in Pr2Fe14B/α-Fe nanocomposite magnets with a combined addition of V and C

Nanostructured Pr₈Fe_86−xV_xB_6−yC_y (x=0, 1; y=0, 1) ribbons composed of Pr₂Fe₁₄B and α-Fe phases with a high coercivity are fabricated by direct melt spinning. The effects of a single addition of V and a combined addition of V and C on the structures and magnetic properties of melt-spun Pr₈Fe₈₆VB_6−xC_x (x=0 and 1) ribbons have been investigated. Compared with addition-free ribbons, 1 at% V addition is found to reduce the grain sizes of the samples and improve their magnetic properties due to a strong exchange coupling between the hard and the soft phase. A remanence ratio of 0.82, a coercive field of 6.2 kOe and a maximum energy product of 23.4 MGOe in melt-spun Pr₈Fe₈₅VB₆ ribbons are obtained at room temperature. The combined addition of V and C is found to lead to the formation of an intermediate phase of VC at grain boundaries, which appears as a pinning barrier during magnetization and results in an increase of the coercivity value to 6.9 kOe for melt-spun Pr₈Fe₈₅VB₅C ribbons.     

Cr,Mo,Ni在$lt;i$gt;α$lt;/i$gt;-Fe（C）中占位、键合性质及合金化效应的第一性原理研究

基于密度泛函理论第一性原理方法,采用广义梯度近似下的PW91泛函形式,计算了合金元素Cr,Mo,Ni固溶于α-Fe（C）的电子结构,从晶格畸变、结合能、态密度、重叠布居及差分电荷密度等计算结果出发探讨了合金元素在α-Fe（C）中占位、键合性质及其合金化效应,结果表明：Cr优先占据铁素体晶胞顶角位置,而Mo,Ni 优先占据体心位置;Cr与晶胞的结合能最大,晶胞最稳定,Ni次之,Mo最低;Cr,Mo,Ni 在晶胞中都存在金属键、共价键和微弱离子键的共同作用,成键轨道主要是Cr3d与Fe3d,Mo4d与Fe3d,Ni3d与Fe3d,C2p的交互作用形成的;Cr与晶胞原子间的键合作用强,晶胞的稳定性好,对增强钢材的机械性能帮助较大,Ni的键合作用较弱,但还是能保持晶胞的稳定性,Mo虽然键合作用强,但反键作用也非常强,使晶胞的稳定性大大降低,对钢材的机械性能危害较大. 关键词： 第一性原理 α-Fe（C）')" href="#">α-Fe（C） 键合性质 合金化效应     

γ-Fe2O3纳米纤维的丙酮敏感特性

采用静电纺丝法制备了PVP/FeC₆H₅O₇复合纳米纤维, 并将复合纤维在500 ℃高温烧结3 h, X射线衍射分析(XRD)表明, 烧结后的产物为正尖晶石结构的γ-Fe₂O₃晶体. 扫描电子显微镜(SEM)观测结果表明, 制得了直径均匀、 连续的复合纳米纤维, 其平均直径约为1000 nm; 烧结后的γ-Fe₂O₃纳米纤维保持了其连续性, 但纤维发生了收缩, 直径较烧结前小, 平均约为600 nm. 比表面积分析表明, γ-Fe₂O₃纳米纤维比表面积为57.18 m²/g. 气敏性能测试结果表明, 230 ℃为γ-Fe₂O₃纳米纤维检测丙酮气体的最佳工作温度. 在此温度下, γ-Fe₂O₃纳米纤维对丙酮气体表现出高响应度[S=6.9, c(Acetone)=7.88×10⁴ mg/m³]和线性度(7.88×10²~1.58×10⁵ mg/m³浓度范围内). 同时, γ-Fe₂O₃纳米纤维气体传感器件还表现出良好的长期稳定性.