本文首次报道了利用电泳技术在铁和不锈钢基底上制备MgB2超导带材.电阻测量表明,沉积在铁和不锈钢基底上MgB2带材的超导零电阻转变温度分别为37.5K和31K,超导转变宽度分别为0.3K和1K.磁测量表明,(5K,OT)时不锈钢基底上带材的临界电流密度为6×105(A/cm2).X射线衍射谱和扫描电子显微镜图象表明样品结晶良好,晶粒生长致密.本工艺制备MgB2带材时不受系统真空度的限制,生长迅速,成本低廉,并且可以根据不同的需要任意选择基底的形状和大小.     

Moessbauer Investigation of the Ferromagnetic Coupling in Copper-Iron Polycyanides

One of the Prussian blue analogs, molecular magnet Cu3^Ⅲ [Fe^Ⅲ (CN)6]2.11.6H2 O, was investigated by Moessbauer spectroscopy. It was found that transition temperature was around Tc = 18.5 K from paramagnetic phase to ferromagnetic phase. The β value of the critical exponent is around 0.338 at magnetic ordering temperature.Therefore, the ferromagnetic coupling interaction of Cu-Fe cyanide could be clearly explained by spin wave theory.     

A Mossbauer study of the magnetic coupling in iron phosphorous trisulfides

The polycrystalline sample of layered compound FePS_3 has been investigated by using M?ssbauer spectroscopy (12K to 300K), magnetic susceptibility measurements, x-ray diffraction and FTIR spectroscopy. The antiferromagnetic order exists below T_N=120.5±1K. The M?ssbauer spectra below T_N indicate that the magnetization axis is perpendicular to the layer of FePS_3, and the divalent iron cations are in their high spin configurations. By fitting the hyperfine field parameters near the Néel temperature, we obtain information on the nature of magnetic interactions in the material. The results show that the magnetic coupling can be treated by the two-dimensional Ising model, and it can be interpreted on the basis of a crystal-field effect.     

后退火温度对溅射沉积Pb(Zr0.52Ti0.48)O3铁电薄膜结构和性能的影响

在具有Ti缓冲层的Pt(111)底电极上,用射频溅射工艺在较低的衬底温度(370℃)和纯Ar气氛中沉积Pb(Zr0.52Ti0.48)O3(PZT)薄膜,沉积过程中基片架作15°摇摆以提高膜厚的均匀性。然后将样品在大气中进行5min快速热退火处理,退火温度550-680℃。用XRD、SEM分析薄膜的微结构,RT66A标准铁电测试系统测量样品的铁电和介电性能。结果表明,所沉积的Pt为(111)取向,仅当后退火温度高于580℃,沉积在Pt(111)上的PZT薄膜才能形成钙钛矿结构的铁电相,退火温度在580-600℃时结晶为(110)择优取向,退火温度高于600℃时结晶为(111)择优取向。PZT薄膜的极化强度随退火温度的升高而增加,但退火温度超过650℃时漏电流急剧上升,因此退火处理的温度对PZT薄膜的结构和性能有决定性的影响。     

Formation Mechanism and Orderly Structures of an Iron Film System Deposited on Silicone Oil Surfaces

A new iron film system,deposited on silicone oil surfaces by vapour phase deposition method,has been fabricated and its formation mechanism as well as orderly structures has been studied,It is found that the formation mechanism of the films obeys a two-stage growth model,which is similar to that to the other metallic films on liquid substrates,Large and orderly structures are observed in the continuous iron films.The experiments show that the orderly spatial structures result from the local material gathering in these nearly free sustained films.