一种高岭土基多孔硅材料的制备及其对Ca2+和Mg2+的吸附

成功合成了一种高岭土基新型多孔硅材料（ASM）并以FTIR,XRD,FE-SEM和N₂吸附-脱附进行了系统的表征。ASM的制备过程涉及两步：SiO₃^2-提取和ASM的制备。SiO₃^2-提取的最优条件为煅烧温度为960℃,NaOH浓度为20%,反应温度为90℃,反应时间为90 min,在此条件下SiO₃^2-提取率为60.45%（w/w）。以此提取液为原材料,调整提取液中SiO₃^2-的浓度为12 g·L^-1,反应温度为90℃,反应时间为60 min,然后再搅拌2 h可制得ASM。以此ASM对Ca²⁺和Mg²⁺进行吸附研究,脱除率分别可达94.99%和62.32%。     

Yield stress measurements and microstructure of colloidal kaolin powders clusterized and dispersed in different liquids

Rheologicat measurements of four colloidal kaolin powders dispersed in water, paraffinic oil and liquid rubber have been done at solid concentration （9 （VS/VL） in the range 8-33%. In quasi-static conditions the yield stress τ° values were derived. An S-shaped relationship between τ° and （9 exists, that allows to evaluate the percolation threshold θc values. In water θc ranges between 29% and 33%, while it is between 17% and 21% in oil and in liquid rubber. In water the microstructure units, i.e. the primary clusters among kaolin crystallites, are denser and bigger than the ones in the two other liquids. Furthermore, in quasistatic condition, the aqueous microstructure units have less tendency to cling together to form a network that can span all over the liquid phase. The different kaolin dispersions at θ equal to 22% are characterized by yield stress ranging between 7.S Pa and 59 Pa in water, 66-250 Pa in oil and 230-770 Pa in liquid rubber. It has been found that for any kaolin types the log τ°/ θ evaluated near to the percolation threshold is a conservative parameter of the three different liquids. These results are useful to design colloidal dispersions with selected microstructure.     

Synthesis of Acrylic Acid／Kaoline Powder Superabsorbent Composite by Inverse-suspending Polymerization

An acrylic acid/kaoline powder superabsorbent composite with a water absorbency of the superabsorbentcomposite about 1/800 was synthesized by inverse-suspending polymerization reaction between acrylic acidmonomer and kaoline ultrafine powder. The influence of the dispersant agent on the configuration of theproducts in the inverse suspension polymerization is investigated. The influences of the kaoline powder.cross-linker, initiator, neutralization degree and the volume ratio of oil to water phase on the water absorben-cy of the superabsorbent composites are discussed in the paper.     

Mg-Al-MMH-高岭土分散体系触变性研究

触变性是分散体系流变学研究的重要内容之一,在外切力作用下,若体系的粘度随时间下降,静止后又恢复,即具有时间因素的切稀现象,称为正触变性（positive thixotropy);反之,若体系的粘度或切力上升,静止后又恢复,即具有时间因素的切稠现象,称之为负触变性（Negative thixotropy)^[1],若在外切力作用下,某个特定体系的粘度或切力随时间先后呈现出正触变性和负触变性特征,则称之为复合触变性（Complex thixotropy)^[2,3],目前,对各种触变性机理的认识尚不统一。     

洗涤助剂用硅铝酸盐制备

以苏州高岭土为原料,进行了新型高效无磷洗涤助剂硅铝酸盐活性体制备研究,确定了传统水热法合成硅铝酸盐活性体的适宜条件:高岭土在800℃焙烧活化2h,焙烧后的偏高岭土补加氢氧化钠、硅酸钠和水,调整SiO2:Al2O3:Na2O:H2O摩尔比为2:1:4.3:237,然后在60℃恒温水浴中老化3h,接着在95℃条件下晶化4h,最后所得固相即为钙镁离子交换性能优良的硅铝酸盐。该产品对钙镁吸附量均高于4A沸石和P型沸石,分别达到374.3mg/g和122.7mg/g;此外该产品对水溶液中铅离子也有很好的吸附性能。     

欧盟最新批准4种食品接触材料

<正>不久前,欧洲食品安全局(EFSA)食品接触材料组批准了4种新的食品接触材料,其中包括两种氧气吸收剂、一种添加剂以及一种塑化剂。具体的物质如下:铁(0)改性膨润土和铁(0)改性高岭土,用于吸收食品接触环境中的氧气;2,2,4,4-四甲基-1,3-环定二醇(CASNo3010–96–6),在聚酯生产过程中用作单体聚甘油(CASNo25618–55–7),用于塑化剂,要求脂肪族芳香聚酯共聚物中聚甘油不超过6.5%。随着食品生产技术的日益多元化,食品安全问题已经不仅仅限于食品本身,还包括与食品直接或间接接触的材料。     

悬浮物测定的质量控制方法

为完善现行国标法GB 11901–1989《水质悬浮物的测定重量法》中质量控制与质量保证相关内容,促进悬浮物标准品的研发,利用高岭土研制的标准溶液建立了悬浮物测定的质量控制方法。根据水样的属性,取样体积范围在50 m L~200 m L区间,采用水系0.45μm滤膜和三联抽滤装置对水样进行预处理操作,以重量法测定水样悬浮物的含量。确定方法的空白测定值稳定于上下警告线内波动,检出限为5 mg/L,样品6次测定结果的相对标准偏差小于10%,标准样品10次测定相对误差在±10%内,满足分析质量控制要求。     

高岭土磁性复合材料表面印迹聚合物选择性吸附分离环丙沙星

以氨基改性的磁性高岭土为基质材料,利用电子转移产生催化剂的原子转移自由基聚合法制备磁性高岭土表面印迹聚合物（MMIPs）。通过FTIR、TEM、TGA、XRD和VSM等方法对其物理化学性质进行表征,其比表面积112 m²·g^-1,且具有较好的热稳定性、超顺磁性（M_s=13.365 emu·g^-1）。吸附性能研究表明,准二级动力学模型能较好地描述MMIPs对环丙沙星（CIP）吸附动力学行为,Langmuir等温模型能较好地拟合MMIPs对CIP的吸附平衡数据,25℃时MMIPs的单分子层吸附容量为89.36 mg·g^-1。选择性实验研究表明,MMIPs对CIP具有较好地选择识别性。结合高效液相色谱分析技术,MMIPs已成功应用于鲜鱼样品中痕量CIP的分离、富集和回收,CIP的回收率为92.15%。     

焙烧高岭土的相变研究

对湿化学方法处理过的高岭土作不同温度焙烧得不同样品，对不同样品进行XRD研究表明，高岭土随焙烧温度的不同发生一系列相应。用DTA，TG，IR对其相变进行了印证，得到了一致的结果。     

Y型沸石和高岭土原位晶化产品的Tb／Tb同位素交换及NaTb,Tb／…

本文在前文＾［１］Ｙ型沸石和高岭土原位晶化产品上的Ｎａ／Ｔｂ离了交换平衡研究的基础上，进一步了这两种离了交换剂上Ｔｂ／Ｔｂ同位素交换及Ｎａ／Ｔｂ，Ｔｂ／Ｎａ正逆离子交换动力学，确定了反应机理，测得了铽的自扩散系数以及正逆交换的积分粒内互扩散系数。对这两种离交换剂所得结果进行了对比和讨论。