Electrooxidation Mechanism of Methanol at Pt-Ru Catalyst Modified GC Electrode in Electrolytes with Different pH Using Electrochemical and SERS Techniques

The electrochemical and in-situ surface-enhanced Raman spectroscopy （SERS） techniques were used to investigate the electrooxidation behavior of methanol in acidic, neutral and alkaline media at a Pt-Ru nanoparticle modified glassy carbon （Pt-Ru/GC） electrode. The results showed that methanol could be dissociated spontaneously at the Pt-Ru/GC electrode to produce a strongly adsorbed intermediate, CO. It was found that CO could be oxidized more easily in the alkaline medium than in the acidic and neutral media. The peak potential of methanol oxidation was shifted from 0.663 and 0.708 V in the acidic and neutral media to -0.030 V in the alkaline medium, which is due to that the adsorption strength of CO on the Pt surface in the alkaline medium is weaker than that in the acidic and neutral media. The final product of the methanol oxidation is CO2. However, in the alkaline medium, CO2 produced would form CO3^2- and HCO3^- resulting in the decrease in the alkaline concentration and then in the decrease in the performance of DMFC. Therefore, the performance of the alkaline DMFC is not Stable.     

三维有序大孔杂化材料SiW11O8-39-SiO2和γ-SiW10O8-36-SiO2的制备与表征

通过溶胶-凝胶和聚苯乙烯模板等方法制备了含缺位Keggin阴离子SiW11O8-39和γ-SiW10O8-36的三维有序大孔杂化氧化硅复合材料, 并通过紫外漫反射光谱(UV/DRS)、傅里叶变换红外光谱(FTIR)、固体核磁共振波谱(MAS NMR)等手段对其结构进行了表征. 结果表明, 杂化材料中的Keggin阴离子仍保留其基本骨架结构, 但其与氧化硅基体之间存在化学作用. 杂化材料的孔道结构用扫描和透射电子显微镜(SEM和TEM)进行表征, 其平均孔径为(335±50) nm. 对杂化材料孔壁的微孔性通过氮气吸附进行了测定. 此类材料对水溶液中羟基丁二酸的降解反应具有活性, 光催化过程中未发现Keggin阴离子自载体中脱落的现象.     

新型高活性催化剂乙烯气相聚合的研究（Ⅱ）——改性剂,预聚…

研究了新型高活性乙烯气相聚合催化剂ＴｉＣｌ４／ＭｇＣｌ２／ＺｎＣｌ２／ＳｉＣｌ４醇／Ａｌ（ｉ－Ｂｕ）３体系中不同醇、不同Ｃ２Ｈ５ＯＨ／Ｔｉ摩尔比和正丁醚对聚合反庆及产物颗粒形态的影响，研究了预聚合反应及乙烯气相聚合反应规律，用扫描电镜和图象分析对催化剂、预聚物和聚合产物的形态和颗粒分布的研究表明：新型高活性催化剂和经预聚合制得的乙烯气相聚合物的颗粒形态类似球形，颗粒长短轴比值和大小粒径比值相近。     

聚苯乙烯乳胶球三维有序体的制备及其显微形貌表征

A three-dimensional (3D) ordered structure was achieved by self-organization of monodisperse polystyrene latex about 250nm in diameter after being ambient dried. The stacked morphology was investigated by scanning electron microscopy(SEM) observation. It is shown that the face-centered cubic(FCC) phase dominantly exists. This finding presents a potential template for preparing an inverse FCC structure as a photonic crystal of full band gap if the index contrast is higher than 2.8.     

颗粒性甲烷单加氧酶的电子供体研究

从甲基弯菌M ethylosinus trichosporium IMV3011的膜中分离出颗粒性甲烷单加氧酶（Particulate MMO,Pmmo）t和NADH脱氢酶，只有当两者同时存在，并添加去垢剂解离膜组分时，NDAH才能为pMMO提供还原当量，对苯二酚能够在整细胞和膜水平代替NADH作为PMMO的电子供体，对于纯化的PMMO，对苯二分配仍是有效的电子供体，而NADH却是无效的电子供体。在NADH脱氢酶存在下，NADH可将对苯醌还原为对苯二酚，纯化过程中，采用对苯二酚作为PMMO活性分析时的电子供体，不必共纯化NADH脱氢酶，且有利于对PMMO活性中心进行深入研究。     

反相微乳液法制备棒状羟基磷灰石纳米粒子

在(Tritonx-100 Tween 80)，环己烷，(正己醇 正丁醇)，0．5mol／L Ca(NO3)2水溶液反相微乳液体系中，采用滴加0．3mol／L(NH4)2HPO4水溶液的加料方式成功制备出直径在20～25nm，长度在28～64nm的棒状羟基磷灰石纳米粒子。通过对(Triton X-100 Tween 80)，环己烷，(正己醇 正丁醇)／0．5mol／L Ca(NO3)2水溶液三元相图及水溶液反应机理的分析，确定了最佳反相微乳液组成；研究了HLB值和表面活性剂用量对羟基磷灰石颗粒大小的影响。实验结果表明，最佳反相微乳液组成为：47．6(wt)％的环己烷、37．4(wt)％的表面活性剂和助表面活性剂、15(wt)％0．5mol／L的Ca(NO3)2水溶液。     

一种N-酰肌氨酸在四氧化三铁纳米颗粒表面的吸附特征

根据表面活性剂固液界面吸附理论和表面改性颗粒亲水疏水特性及红外光谱分析,提出了不同四条件和表面活性剂用量下不同的吸附模型。     

纳米银掺杂二氧化硅复合颗粒的制备及表征

0引言金属纳米颗粒因其粒子尺寸小(1￣100nm),比表面积大,表面原子数多,表面能和表面张力随粒径的下降急剧增大而具有量子尺寸效应[1]、小尺寸效应[2]、表面效应[3]及宏观量子隧道效应[4]等,从而出现了不同于常规固体的新奇特性,如:光学性质、磁性质以及电磁学性质[5],使其在催化、信息存储及非线性光学等领域展示了广阔的应用前景[6]。虽然制备金属纳米颗粒的方法有很多[6],但是由于纳米尺寸的金属颗粒具有较高的表面能,容易发生聚集,所以如何保持其稳定性依旧是比较困难的问题。随着纳米科技的发展,人们正尝试用各种方法来解决这个问题:如…     

铟锡氧化物(ITO)纳米颗粒的制备及表征

以金属In和SnCl₄·5H₂O为主要原料，加入保护剂PVP，利用化学共沉淀法合成了球形的铟锡氧化物(ITO)纳米颗粒。分别对PVP的用量、溶液的pH值、热处理温度等因素对ITO纳米颗粒粒径的影响进行了分析。并且借助透射电镜(TEM)、X射线衍射(XRD)对所合成的ITO纳米颗粒进行了表征。XRD分析说明本文合成了金刚砂型结构的铟锡氧化物纳米颗粒，并且其晶型结构随着热处理温度的升高而转变为铁锰矿型。