QCM Detection of Adhesion, Spreading and Proliferation of Human Breast Cancer Cells （MCF-7） on a Gold Surface

The quartz crystal microbalance (QCM) was used to monitor the one-day incubation of human breast cancer cells (MCF-7) on the gold electrode. In combination with an optical microscope simulation experiment, the cell-population pictures at various stages, the QCM responses to the cells' adhesion, spreading and proliferation on the electrode surface were discussed. The △f0 and △R1 responses were found mainly from mixed effects of viscodensity and surface stress, and in proportion to the cell coverage, rather than to the number of cells at the electrode. The significant fore-and-aft changes in cyclic voltammetry and electrochemical impedance spectroscopy of the ferri-ferrocyanide redox couple also proved that the cells were adhesion to the gold surface.     

PEO与Li1.3Al0.3Ti1.7(PO4)3络合的离子导体聚合物电解质

将实验室经固相反应的精细Li1．3Al0．3Ti1．7(PO4)3盐与聚氧化乙烯(PEO)按照不同，nEO／nLi摩尔比，通过溶液浇铸法制备了固态聚合物电解质。红外光谱分析表明Li1．3Al0．3Ti1．7(PO4)3盐与PEO之间有络合产生。SEM照片显示PEO晶体外层为无定形相所包覆形成的胞状结构。经电化学阻抗(简称EIS)法测试发现聚合物电解质膜的室温阻抗谱图是由高频处一压缩的半圆和低频下一条直线组成，而高温时的阻抗谱主要为一条直线。离子电导率的测试结果得到：当nEO／nLi=16时，聚合物电解质室温下电导率约为10^-6／cm，343K时达到10^-4s／cm。离子迁移率的数据表明聚合物电解质为离子和电子共混的导体，但在聚合物电解质体系中电荷的迁移主要是由离子作为载流子导电造成的，由测试结果可得此电解质为离子导体。     

正极材料LiNi0.5C0.5O2的电化学性能研究

以聚丙烯酰胺（PAM）为分散剂用微波—固相复合加热技术合成了层状锂离子电池正极材料LiNi0.5C0.5O2。通过扫描电子显微镜（SEM）和X—射线粉末衍射（XRD）分析技术对材料的微观形貌和相结构进行了表征。恒电流充放电循环测试表明：材料的放电比容量高达154mAh／g，且有良好的循环性能。重点利用循环扫描伏安、计时电量和电化学交流阻抗测试技术，对材料在循环前后的电化学性能变化规律进行了探讨。结果表明，经过循环后材料的导电能力以及锂离子扩散能力都有了很大的提高。另外，材料中的锂含量对材料的导电能力也有很大的影响。     

贮氢电极电化学阻抗谱及其数学模型

从分析贮氢电极的放电过程着手，建立了具有明显物理意义贮氢电极电化学阻抗谱的数学模型，以该数学模型为基础，讨论了与电极材料性质和电极荷电状态相联系的一些参数。     

VA族元素对阳极铅(II)氧化物膜半导体性质的影响(I)

用交流阻抗法研究了铅、铅砷、铅锑和铅铋金在4.5 mol·L~(-1) H_2SO_4溶液(20 ℃)中，以0.9 V(vs．Hg/Hg_2SO_4)极化2 h而形成的阳极膜的半导体性质．根据Mott-Schottky图，此种膜为n型半导体．pb，pb-lat％As，Pb-lat％Sb和Sb-lat％Bi上膜的平带电位分别为-0.95，-1.1, -1.0，-1.1 V(vs. Hg/Hg_2SO_4)；相应的施主密度分别为0.82×10~(16)，2.6×10~(16)，1.2×10~(17)和0.71×10~(16) cm~(-3).     

Zn/V2O5水相二次电池的交流阻抗研究

The dependence of charge transfer resistances of electrodes in the aqueous Zn/V 2O 5 secondary battery on the Zn 2+ amount intercalated was studied by means of AC impedance experiments. The results showed that the electrode reaction on cathode was controlled by the diffusion of Zn 2+ at the beginning of the discharge process. With the increase of Zn 2+ amount intercalated into the cathode, the reaction became a kinetic controlled process, i.e.a process controlled by intercalation of Zn 2+ in V 2O 5.     

新型AB5储氢合金表面修饰方法及机理研究

探索了一种储氢合金表面修饰的新方法. 在HF和CuSO₄的混合溶液中对MH/Ni电池负极材料AB₅型储氢合金进行表面处理, 研究了HF含量对反应的影响；考察了铜颗粒沉积量对表面修饰的影响；测试了修饰后合金电极的电化学性能；应用交流阻抗分析了表面修饰对合金性能影响的作用机理. 电化学测试结果表明, 表面修饰后合金电极具有更好的高倍率放电能力和循环稳定性. EIS分析结果表明, 表面修饰使合金的活性增强, 导电性提高, 欧姆阻抗及电化学阻抗显著降低. 因此, 这种新型表面修饰方法可以有效地改善合金的电化学性能, 使之更好地满足电动车用动力型电源的要求.     

TiO_2光电化学电池催化氧化甲基红

以钛基TiO2薄膜为光阳极,研究了光电化学电池中阳极光催化降解偶氮染料甲基红的动力学.结果表明,短接光电化学电池分隔了光催化过程的阴、阳极反应,有利于抑制光生载流子的复合,提高光催化氧化速率.相同实验条件下短路光电流越大,则甲基红降解速率越高.在基底和TiO2薄膜之间夹层SnO2得到组装电极Ti/SnO2/TiO2,进一步提高了光生载流子的分离效率;同时采用电化学阻抗谱(EIS)评价了电极的光催化性能.     

铜在低电导溶液中扩散机理的研究

双水内冷发电机空芯铜导线的腐蚀问题直接影响到火电厂发电机的安全经济运行．其腐蚀体系为纯铜和低电导水溶液（pH＝7．3，空气饱和，电导率＜10μS·cm－1）．我们已经用交流阻抗法对该体系进行了一些研究．由于该体系溶液电导率低，在交流阻抗谱的高频区出现高频半圆；低频区为一条文于实轴Z约45°的直线（不加缓蚀剂时）．如果在该体系中MABTA、MBT等缓蚀剂，低频区直线变为半圆．所以，低频区的阻抗代表了电极表面的特征，而高频区（如10k～100kHz范围）半圆是由于参比回路（包括参比电极、盐桥、鲁金毛细管等）中存在太大的电阻…     

钙调素修饰金电极的交流阻抗行为研究

利用交流阻抗方法, 以氧化还原对为探针，对自组装到金电极表面的钙调素 (CaM)膜的成膜过程、不同pH值的影响以及与钙离子的结合情况进行了较系统的研究.实验结果表明, 钙调素可以自组装到金电极表面并且其自组装过程较为明显地分为快、慢两个步骤；还发现钙调素膜的性能结构随体系不同的pH值发生有规律的变化，在其等电点，膜的结构最致密；而且钙调素膜与钙离子的结合也分为较明显的三个阶段.