硫酸溶液中Ag+离子对Mn2+离子阳极氧化的催化作用

Anodic oxidation of Mn2+ and Ag+ ions and anodic oxidation of Mn2+ ion on platinum electrode in H2SO4 solution catalyzed by Ag+ ion are studied by using RRDE and triangle voltammetry techniques. Mn2+ ion is oxidized on the anode surface with adsorped OH group to form a certain compound containing Mn3+, which causes Mn2+difficult to be oxidized directly on anode. Near the potential of oxygen evolution from H2O decomposition, Ag+ ion is oxidized to form Ag2+ ion. This is the main reaction on anode because of its reversability. At higher potential silver oxide is formed on the anode. The oxide catalyzes the decomposition of H2O strongly. The anodic oxidation of Mn2+ion catalyzed by Ag+ takes place and Ag2+ ion and silver oxide are no longer the product of Ag+ anodic oxidation when Mn2+ exists in solution at the potential for Ag+ anodic oxidation. It is confirmed that the catalysis reaction is homogeneous and very fast.     

Selection of Anodic Material Used in Electrolytic Process for Producing Hypophosphorous Acid

Black lead, Ti-Ru and Ti-PbO2 were used as anode and stainless steel was used as cathode The electrolytic process of producing hypophosphorous acid with four-compartment electrodialytic cell was studied. The comparison of some factors, such as anodic voltage, product concentration and current efficiency, of black lead, Ti-Ru, and Ti-PbO2 electrodes was conducted. As a result, theTi-PbO2 electrode is the optimal anode material used, it can be in electrolytic process for producing hypophosphorous acid.     

Ti基IrO2＋Ta2O5阳极在H2SO4溶液中的电解时效行为

研究了450 ℃制备所得Ti/70％IrO2 30％Ta2O5（摩尔分数）高寿命阳极在H2SO4溶液电解过程中电极的物理、化学及电化学性能的时效行为.结果发现，整个电解过程可分为“活化”、“稳定”及“失效”三个阶段.在“活化”及“稳定”区内主要发生电极表面活性氧化物的溶解，涂层中IrO2金红石相的（110）、（101）晶面择优取向随电解时间延长而减弱，而（002）晶面择优增强.但是在“失效区”内，各晶面的择优程度却不随电解时间的变化而变化，这表明在“失效区”内氧化物的损失机制发生了变化.电化学阻抗谱测试表明，电极的析氧电化学反应电阻随电解时间的延长发生缓慢而连续的上升，而整个电极的物理阻抗在“失效区”内却发生突升现象.X射线衍射分析（XRD）表明，随电解时间的延长TiO2金红石相的衍射强度增大，达“失效区”时衍射强度发生突升.根据实验现象特别是“失效区”内阳极的时效行为提出高寿命Ti基氧化物涂层阳极的失效机制.     

离子液体中电沉积制备钴纳米线阵列

Porous anodic alumina (PAA) was used as a template to prepare Co nanowires array from 1-ethyl-3-methylimidazolium chloride ionic liquid by direct current method. The surface morphology of porous anodic alumina template was observed by field emission-scanning tunneling microscopy (FE-SEM) before and after the electrodeposition of Co nanowires. The electrodeposition of Co nanowires was characterized by transmission electron microscopy (TEM) and X-ray powder diffraction (XRD). TEM results indicate that the Co nanowire surface is coarse and porous when aqueous solution was used as electrolyte， and the Co nanowire deposited from the ionic liquid is uniform and smooth. XRD results show that the electrodeposition of Co is a mixture of crystal and microcrystal phase.     

镧对V2O5/γ-Al2O3催化剂在异丁烷脱氢中活性的影响

V2O5／γ-Al2O3是用于异丁烷脱氢的新型催化剂，引入适量的镧不仅可改善活性组分的分散度，提高催化脱氢活性，而且还增强了催化剂的抗积炭能力，通过FTIR，BET，TG，TPR和TEM等手段研究了镧对催化剂性能的影响。     

溶胶-凝胶法制备纳米氢氧化铝溶胶

研究了利用铝酸钠溶液碳酸化产生的沉淀, 经胶溶作用制备出纳米氢氧化铝溶胶的过程. 分析了铝酸钠溶液滴加到大量碳酸氢钠溶液中时发生的反应. X射线衍射研究结果表明, 在纳米氢氧化铝溶胶制备过程中, 从无定形氢氧化铝沉淀到拟薄水铝石的晶型转变过程是氢氧化铝沉淀胶溶时溶解再析出的过程. 将碳酸氢钠加入到苛性比为1.7的铝酸钠溶液中, 中和至苛性比为1.3后, 溶液诱导期中的紫外光谱显示270 nm处的Al(OH)3-6吸收增强. 经与含铝原子六配位的晶体紫外光谱对比后表明, 在铝酸钠分解生成氢氧化铝的过程中, 其铝的配位结构从四配位转化为六配位. 拟薄水铝石溶胶粒子的形貌与胶溶所用的酸和分散剂有关.     

纳米氧化铝微柱富集-等离子体发射光谱法测定植物中痕量稀土元素

以负载了1-苯基-3-甲基-4-苯甲酰基-吡唑酮[5](PMBP)的纳米氧化铝为微柱吸附材料，采用等离子体原子发射光谱法(ICP-AES)，系统地研究了其在动态条件下对稀土离子Sc^3 、Y^3 和La^3 的吸附性能，并确定了最佳吸附及解脱条件。实验结果表明：在pH为4．5时，分析物均可被上述吸附材料定量吸附；用0．5moL／L盐酸溶液可将吸附在微柱上的稀土离子完全解脱。本法对Sc^3 、Y^3 和La^3 的检出限分别为0．16、0.19和0．39μg／L；相对标准偏差(RSD)分别为2．7％、3．2％和1．6％(n=9，C=0．5mg／L)。方法应用于植物标样中痕量Sc、Y和La的测定，其测定值与标样值吻合很好。     

微波辐射下苯偶姻的干法氧化反应

研究了微波辐射下干法氧化苯偶姻生成苯偶酰的反应。结果表明，硅胶和酸性氧化铝是本反应的良好载体，空气是良好的氧化剂。在较短时间内(8～15min)即可获得很高的产率(92%～98%)，为一种有效的苯偶姻氧化反应新方法。     

Pd—Pt／Al2O3燃烧催化剂的活性和热稳定性

研究了Ｐｄ－Ｐｔ／Ａｌ２Ｏ３ 催化剂对有机物的完全氧化活性和热稳定性。结果表明：Ｐｄ－Ｐｔ双给分催化剂的活性高于单组分催化剂。在实验范围内，催化剂的氧化活性与Ｐｄ、Ｐｔ负载量无关，热稳定性受Ｐｄ、Ｐｔ负载量影响而与Ｓｌ２Ｏ３的表面积关系不大８呶麓硪鸫呋帘砻妫校洹ⅲ校艉康慕档褪窃斐苫钚韵陆档闹饕颉８么呋炼杂谢锞哂泻芨叩难趸钚裕匝醯睦寐屎芨撸视糜诠ひ涤谢掀木换?     

孔性氧化铝模板与一维纳米新材料的制备

纳米材料尤其是以碳纳米管有序阵列为代表的一维纳米阵列材料的重要价值,促进了人们对模板合成方法的研究。本文简要回顾和总结了近年来有关孔性氧化铝模板的制备及其应用的研究进展,结合我们实验室的部分相关研究工作,揭示了孔性氧化铝模板在合成与组装一维纳米新材料方面的重要作用,以进一步活跃和促进该重要领域的研究和发展。