Y2O2S：Eu,Mg,Ti,Tb红色长时发光材料的研究

利用高温固相反应法合成了一种新型的红色长时发光材料－Y2O2S：Eu,Mg,Ti,Tb.材料的XRD测试结果表明Eu掺杂引起Y2O2S，Eu,Mg,Ti,Tb晶胞增大，激发光谱，发射光谱和发光衰减曲线表明该材料是一种适合紫外线和可见光激发，并具有很好的长时发光性能的红色长时发光材料，热释光谱测试结果表明该材料可能具有两个较深的陷阱能级，研究了Eu,Mg,Ti,Tb的加入量对材料发光特性的影响。结果表明：Eu,Mg,Ti,Tb影响材料的初始亮度和发光时间，Eu决定材料的红色比。     

新型有机锗倍半氧化物及硫化物的合成

已先后合成的倍半氧化物类及倍半硫化物类化合物的前体,即有机锗三氯化物中只含1个锗原子。为了考查从含2个锗原子的前体合成的有机锗倍半氧化物及硫化物的药物活性,我们合成了1类化合物及相应的倍半氧化物(2类)及倍半硫化物(3类),并合成了酰基苯胺化合物1_e、2_e及3_e。结果见表1。     

2,4,6-三硝基苯酚改性锆铝复合氧化物固定相分离富勒烯的色谱性能研究

制备了用于分离C60和C70的2，4，6－三硝基苯酚改性锆铝复合氧化物高效液相色谱固定相，考察了流动相中甲苯的含量、柱温及流速对C60和C70分离的影响，同时比较了酸腐蚀前后锆铝复合氧化物基质对分离的影响，结果表明，2，4，6－三硝基苯酚改性酸腐蚀后锆铝复合氧化物填料对富勒烯表现出较强的分离能力，具有作为富勒烯制备分离的潜力。     

Ni(phen)(H2O)(V2O6)的水热合成和晶体结构（英）

A novel compound Ni(phen)(H₂O)(V₂O₆) has been hydrothermally synthesized and structurally determined to be a two-dimensional compound, which contains {V₂O₆}_n^2n- chains interconnected by nickel(Ⅱ) complexes via oxygen atoms. The crystallographic data measured by single-crystal X-ray diffraction analysis are as follows: C₁₂H₁₀N₂NiO₇V₂, M_r=454.81, monoclinic, space group P2₁/c, a=0.784 6(3), b=2.103 6(8), c=0.942 3(4) nm, β=112.872(5)°, V=1.433 0(10) nm³, Z=4, D_c=2.104 Mg·m^-3, μ(Mo Kα)=2.615 mm^-1, F(000)=904, T=298(2) K, 4 480 reflections collected, 2 470 independent (R_int=0.032 2), the final R=0.058 4 and wR₂=0.145 7 for 2 303 observed reflections with I>2σ(I). CCDC: 192520.     

A New Technique of Synthesizing 10—Hydroxy—5—methyl—5,10—dihydrophenophosphazine 10—Oxide

10-Hydroxy-5-methyl-5,10-dihydrophenophosphazine 10-oxide(1)was prepared by a new technique of treating 10-methoxy-5,10-dihydrophenophosphazine 10-oxide(2)with an equivalent of NaH in anhydrous DMF,and then at 120℃ for 3-4h,which not only avoided poisonous and expensive methyl iodide used in literature,but made the consumption of NaH greatly decrease as well.The possible reaction mechanism was also described.The chemical structure of 1 was confiremed by IR,NMR,and mass spectroscopy.     

BiPbSbSrCaCuO的超导电性

据报,在BiPbSrCaCuO中加Sb形成BiPbSbSrCaCuO体系的T_c可达130K。但其组成、结构、性质等均未见详细报道。我们合成了一系列BiPbSbSrCaCuO,发现了一个具有2212相结构、但T_c却为～110K的超导相。 试样制备包括将Bi_2O_3,PbO,Sb_2O_3,SrCO_3,CaO和CuO(AR级)混匀、碾磨、于     

CRYSTALLIZATION AND MELTING OF POLY（ETHYLENE OXIDE） CONFINED IN NANOSTRUCTURED PARTICLES WITH CROSS-LINKED SHELLS OF POLYBUTADIENE

Small fixed aggregates of a poly(ethylene oxide)-block-polybutadiene diblock copolymer(PEO-b-PB)in THFsolution were obtained by adding a selective solvent for PB blocks,followed by cross-linking the PB shells.Themorphologies of the nanostructured particles with a cross-linked shell were investigated by atomic force microscopy andtransmission electron microscopy.The average behaviors of the PEO crystallization and melting confined within thenanostructured particles were studied by using differential scanning calorimetry experiments.For the deeply cross-linkedsample(SCL-1),the crystallization of the PEO blocks was fully confined.The individual nanoparticles only crystallized atvery low crystallization temperatures(T_cs),wherein the homogenous primary nucleation determined the overallcrystallization rate.For the lightly cross-linked sample(SCL-2),the confinement effect was T_c dependent.At T_c(?)42℃,thecrystallization and melting behaviors of SCL-2 were similar to those of the pure PEO-b-PB diblock copolymer.At T_c>42℃,SCL-2 could form PEO lamellae thicker than those of the pure PEO-b-PB crystallized at the same T_c.     

希土元素与三甲胺氧化物配合物的制备及光谱性质

尽管文献报道了三甲胺氧化物与Mn、Co、Ni、Zn、Cd、Cu等多种离子在有机溶剂中形成较稳定的配合物。但对其金属配合物的研究远不如芳香族杂环化合物那样引起人们广泛的注意。本文研究了它与希土元素形成配合物的合成和光谱性质。     

铟锡氧化物(ITO)纳米颗粒的制备及表征

以金属In和SnCl₄·5H₂O为主要原料，加入保护剂PVP，利用化学共沉淀法合成了球形的铟锡氧化物(ITO)纳米颗粒。分别对PVP的用量、溶液的pH值、热处理温度等因素对ITO纳米颗粒粒径的影响进行了分析。并且借助透射电镜(TEM)、X射线衍射(XRD)对所合成的ITO纳米颗粒进行了表征。XRD分析说明本文合成了金刚砂型结构的铟锡氧化物纳米颗粒，并且其晶型结构随着热处理温度的升高而转变为铁锰矿型。     

SrCe0.9Yb0.1O3-α陶瓷的导电性

以高温固相反应法合成了质子导电性氧化物陶瓷SrCe0.9Yb0.1O3-α.粉末XRD结果表明,该陶瓷样品为单一斜方相钙钛矿型结构.以陶瓷样品为固体电解质、多孔性铂为电极,采用交流阻抗谱技术和气体浓差电池方法分别测定了样品在600～1000 ℃下、干燥空气及湿润氢气中的电导率及离子迁移数,研究了样品的离子导电特性.结果表明,在600～1000 ℃下干燥空气中,陶瓷样品的最大电导率为0.026 S·cm-1,氧离子迁移数为0.03～0.2,是一个氧离子与空穴的混合导体;在湿润氢气中,陶瓷样品的最大电导率为0.015 S·cm-1. 600～800 ℃时,陶瓷样品的质子迁移数为1,是一个纯的质子导体,而在900～1000 ℃时,陶瓷样品的质子迁移数为0.91～0.97,是一个质子与电子的混合导体,质子电导占主导.