Novel Gel—like Process for Synthesizing Submicron LiaNi0.8Co0.2O2 Powders Used in Lithium Ion Batteries

A novel gel-like process has been developed for synthesizing LiaNi0.8Co0.2O2 powders,using citric acid as a chelating agent. This process improves the homogeneity of constituent cation and enhances their reactivity in the obtained precursor. The results of electrochemical test demonstrated that these materials exhibited excellent electrochemical properties. Its initial capacity reached 181.6 mAh/g and reversible efficiency at the first cycle is about 88.6%.     

Oxidation of n-Butanol and 2-Pentanol with Molecular Oxygen in Supercritical CO2

Oxidation of n-butanol and 2-pentanol using molecular oxygen in supercritical (SC) CO2 with and without co-solvent is investigated. The results showed that the reaction selectivity is high when the reaction is carried out in SC CO2. It has been observed that co-solvent affects conversion and selectivity of the reaction considerably.     

纳米晶PbTiO3负载CuO催化NO分解

A large specific surface area perovskite-type mixed oxide PbTiO₃ supported cupric oxide was synthesized as a catalyst for NO decomposition and characterized by techniques such as XPS, XRD, H₂-TPR before and after NO decomposition reactions. The catalytic properties were tested with a fix-bed micro-reactor. The results showed that the PbTiO₃ was inactive for the reactions, but 1wt % Cu/PbTiO₃ catalyst gave fairly good activities for NO decomposition at temperature as low as 473 K. Copper species were found well-dispersed but weakly interacted with the support before NO decomposition, and the NO decomposition caused significant change in the environment of the copper species, which became Cu(Ⅰ) and most probably incorporated into surface crystal lattice of the nano-sized PbTiO₃. In NO reaction, a large amount of oxygen atoms from the decomposition of NO penetrated into the nano-sized PbTiO₃ support and caused small expansion of crystal lattice. The transport of oxygen between the copper species and the catalyst support may be helpful to speed up the kinetic regeneration of active metal sites from oxygen occupancy and resulted in good catalytic performance.     

聚苯撑的合成、性能及其应用

对直链型、树枝形聚苯撑的合成、性能及其应用作了介绍，并着重描述了聚苯撑的应用。     

TiO_2-CeO_2催化剂湿式氧化苯酚的活性研究

采用共沉淀法制备了湿式氧化降解苯酚的TiO2-CeO2催化剂,测定了反应过程中不同反应时间的COD去除率,结果表明,当Ti、Ce摩尔比为3∶1时,在150℃、总压5MPa(其中氧分压4.5MPa)时,所制备的催化剂活性最高,反应90分钟COD去除率可以达到71%.对催化剂进行了比表面积、XRD和XPS测试,结果表明,高效的催化剂具有较多的活性位、催化剂粉末体系Ce的变价特性以及大量的表面吸附氧.     

固体电解质La2-xCaxMo1.7W0.3O9-δ(0≤x≤0.2)的合成、表征及电性能

在氧离子导体La₂Mo_1.7W_0.3O₉的基础上，采用固相法合成了La位掺杂的Ca系列新型氧化物La_2-xCa_xMo_1.7W_0.3O_9-δ(0≤x≤0.2)。通过XRD、Raman和XPS等手段对化合物结构进行表征，交流阻抗谱测试其电性能。结果表明：掺杂离子Ca²⁺的半径小于基质离子La³⁺的半径导致晶格收缩；Ca的掺杂在La₂Mo_1.7W_0.3O₉自身内置氧空位的基础上增加了额外的氧空位，提高了氧离子导体的电导率，550 ℃电导率由0.79 × 10^-4 S·cm^-1 (x=0.0)增加到1.5 × 10^-4 S·cm^-1 (x=0.16，0.2)，电导率增加89.9%。     

苯并噁嗪中间体/蛭石插层纳米复合物热固化行为的研究

通过对双酚A型苯并嗪中间体 (BOZ A) 蛭石插层纳米复合物固化过程的分析表明长链烷基铵阳离子对BOZ A的热开环聚合反应没有表现出催化作用 ,也不影响纳米复合物的结构形态 .不同蛭石含量的插层纳米复合物 ,在形成不同纳米分散状态的纳米复合物的过程中 ,蛭石晶片对BOZ A的热开环聚合具有明显不同的阻碍作用 ,蛭石含量为 3%的插层纳米复合物 16 0℃的凝胶化时间较纯树脂延长约 7min ,活化能升高约8kJ mol,固化反应热焓降低约 14J g ,使得固化物的固化程度较纯树脂降低约 7%～ 10 % ,阻碍作用最大 ,其它含量的次之     

1，5-二甲基-2-（S）-（1′-苯基乙基）-2-氮杂-8-氧杂-双环[3．3．0]辛烷-3，7-二酮的合成及其结构表征

利用 2 ,3 丁二酮与丙二腈缩合形成双甲基双氰基环并内酰胺 ,经酸性水解得到双甲基环并内酯 ,然后和 (S) ( -) ( 1 苯基乙基 )胺反应生成 1,5 二甲基 2 (S) ( 1′ 苯基乙基 ) 2 氮杂 8 氧杂 -双环 [3 .3 .0 ]辛烷 3 ,7 二酮 ,通过元素分析、红外光谱、核磁共振氢谱和质谱对其结构进行了表征 .用X射线单晶衍射法测定了目标产物的晶体结构 ,结果表明 ,晶体属单斜晶系 ,P2 1 空间群 ,a =0 8777( 18)nm ,b =1 0 10 2 ( 2 )nm ,c =0 90 0 9( 18)nm ,β =118 75 ( 3 )° ,V =0 70 0 3 ( 2 )nm3 ,Dc=1 2 96g·cm-3 ,μ =0 0 89mm-1 ,F( 0 0 0 ) =2 92 ,Z =2 ,R1 =0 0 3 93 ,wR2 =0 0 95 5 .     

水中痕量钼(Ⅵ)的4-(2-吡啶偶氮)-间苯二酚螯合活性炭吸附富集分光光度法测定

提出了一种简单快速预富集水中痕量钼（Ⅵ）的新方法，方法的机理在于4－（2－吡啶偶氮）－间苯二酚（PAR）与钼（Ⅵ）螯合后被活性炭中附，然后用NaOH解吸下来，再用水杨基荧光酮与钼（Ⅵ）显色，分光光度法测定钼（Ⅵ）的含量；详细研究了影响Mo-PAR螯合物定量吸附于活性炭上的各种参数，找出了最佳吸附－解吸条件，包括吸附酸度、PAR用量、吸附时间、解吸酸度等；该法的主要优点是操作简单、快速，干扰小，避免了常规方法中用浓硝酸消化活性炭费时和污染大的解吸方法，该法已用于测定水中痕量钼（Ⅵ），加标回收率达到94％－97％。     

Synthesis of New Chiral C2-Symmetrical Bis(oxazoline )Compounds

New chiral C2-symmetrical bis(oxazoline)compounds bearing one isobutyl-,secbutyl-benzyl- or isopropyl-substituent at the 4-position have been prepared and characterized.