硅胶负载磷钼杂多酸催化氧化糠醛制顺丁烯二酸酐

采用浸渍法制备负载型磷钼杂多酸催化剂,分析了催化剂的比表面积、分散性、结构特征、稳定性以及再生温度等性质.通过固定床微反应器考察杂多酸催化剂催化氧化糠醛生成顺丁烯二酸酐的催化性能.研究了焙烧温度、负载量对催化剂性能的影响,以及反应温度对顺丁烯二酸酐收率的影响.结果表明:通过浸渍制备的杂多酸催化剂具有杂多酸催化剂的Keggin结构,具有较好的稳定性和酸性;活性组分能较好的分布于载体SiO2上;催化剂的再生温度和活化温度均为400℃;在钼磷原子比为0.85,负载量为48.6%时催化性能较好,催化剂的表面酸量为0.646 mmol/g;反应温度控制在365℃附近时,顺丁烯二酸酐收率可达到57.2%,选择性为62.7%.     

MgO/NaY催化糠醛和丙酮合成航空燃料中间体的性能研究

采用"机械混合-焙烧"方法制备了负载型固体碱催化剂MgO/NaY,研究了糠醛与丙酮在水-乙醇体系中的羟醛缩合反应,考察了催化剂负载量、原料配比、反应温度、反应时间等因素对催化剂性能的影响。结果表明,20%MgO/NaY催化剂表现出最佳的催化性能,在85℃条件下反应8 h后,糠醛转化率达到99.6%,亚糠基丙酮(FA)和二亚糠基丙酮(F₂A)选择性分别达到42.2%和57.1%,缩合产物的总收率为98.6%。高温促进反应中间体向产物的转化,有利于提高产物的总选择性。改变糠醛/丙酮的摩尔比可调控两种缩合产物的选择性,较高的糠醛/丙酮摩尔比有利于提高F₂A的选择性,但会降低整体反应速率。重复性评价表明,催化剂具有较好的再生性能。     

含氨基酸单元Schiff碱的合成与表征

以谷氨酸为原料合成了四个新型的含糠醛或苯甲醛Schiff碱的氨基酸衍生物,并通过红外光谱、质谱和核磁共振氢谱对化合物的组成及结构进行了表征．     

A New Solid Sorbent System for Rapid Monitoring of Dehydrogenated Nicotine by Using Furfural-hydrochloric Acid

Nicotine is one of the highly toxic chemicals, belonging to tobacco alkaloid. Nicotine appears to be a promising tracer for environmental tobacco smoke (ETS) because of its specificity for tobacco and it presents relatively high concentrations in tobacco …     

复合载体及其制备方法对非晶态Ni-B合金催化剂性能的影响

采用浸渍法及溶胶-凝胶法制备了TiO2-Al2O3复合载体,采用浸渍还原法制备了负载型非晶态Ni-B合金,以糠醛液相加氢制糠醇为探针反应考察了不同载体及复合载体的不同制备方法对非晶态Ni-B合金催化性能的影响.采用等离子发射光谱(ICP)、差示扫描量热法(DSC)、透射电镜(TEM)、H2化学吸附法、程序升温还原(TPR)和程序升温脱附(TPD)等技术研究了负载型非晶态Ni-B合金的负载量、合金组成、热稳定性、粒子大小和形态、活性表面积、还原性能以及吸附性能等.用N2吸附法测定了催化剂及载体的比表面和孔径.研究结果表明,与单一氧化铝载体相比,复合载体负载的Ni-B合金催化活性和选择性明显提高,浸渍法制备的TiO2-Al2O3复合载体负载Ni-B合金的催化性能优于溶胶-凝胶法.主要的原因为复合载体负载的催化剂中Ni含量更高,Ni-B粒子细化导致活性表面积更大,以及催化剂的还原及吸附性能发生改变.     

Hydrogenation of Furfural to Furfuryl Alcohol over Co-B Amorphous Catalysts Prepared by Chemical Reduction in Variable Media

Five Co-B amorphous alloy catalysts were prepared by chemical reduction in different media, including pure water and pure ethanol as well as the mixture of ethanol and water with variable ethanol content, Their catalytic properties were evaluated using liquid phase furfural hydrogenation to furfuryl alcohol as the probe reaction. It was found that the reaction media had no significant influence on either the amorphous structure of the Co-B catalyst or the electronic interaction between metallic Co and alloying B. This could successfully account for the fact that all the as-prepared Co-B catalysts exhibited almost the same selectivity to furfuryl alcohol and the same activity per surface area （ Rs ）, which could be considered as the intrinsic activity, since the nature of active sites remained unchanged. However, the activity per gram of Co （ R^mH ） of the as-prepared Co-B catalysts increased rapidly when the ethanol content in the water-ethanol mixture used as the reaction medium for catalyst preparation increased. This could be attributed to the rapid increase in the surface area possibly owing to the presence of more oxidized boron species which could serve as a support for dispersing the Co-B amorphous alloy particles.     

高效液相色谱法同时检测黄酒中的5-羟甲基糠醛和9种多酚

建立了黄酒中5-羟甲基糠醛和9种多酚(儿茶素、表儿茶素、绿原酸、芦丁、咖啡酸、原儿茶酸、丁香酸、阿魏酸、p-香豆酸)的高效液相色谱检测方法。采用Diamonsil C18柱(150mm×4.6mm,5μm)分离,柱温为42℃,检测波长为280nm,流动相为乙腈和3%乙酸水溶液,梯度洗脱,20min内10种物质得到了较好的分离。各化合物回归方程的相关系数r为0.9911～0.9995,检出限为0.2～0.5mg/L;相对标准偏差RSD≤2.4%;10种组分的平均回收率为89.4%～98.3%;能够满足定量分析要求。实验结果表明,本方法适用于不同种类和年份黄酒中5-羟甲基糠醛和9种多酚的检测。     

Fe_2O_3/聚糠醛纳米复合材料的制备及光催化性能

以Fe(NO3)3·9H2O和糠醛(FD)为原料,通过聚合-热转化两步法制备了Fe2O3/聚糠醛(PFD)纳米复合材料,用TEM、XRD、XPS和UV-Vis等技术对其尺寸、结构及吸光特性等进行了表征。在自然光、室温条件下,以亚甲基蓝(MB)溶液的催化脱色降解为模型反应,考察了其光催化性能以及热转化温度对催化性能的影响。结果表明,利用该法可以得到纳米级的、相间以强相互相用结合的有机-无机复合材料Fe2O3/PFD,该纳米材料对紫外-可见区的全程光波有强的吸收;热转化条件对复合材料的结构、催化性能等有很大影响,在300℃下处理35min所得的纳米复合材料在自然光条件下具有最佳的催化性能,25min即可使MB溶液完全脱色,并且重复使用3次仍可使MB溶液的脱色率保持在75.0%以上。而在相同条件下,纳米Fe2O3仅能使MB的脱色率达到5.8%。