纳米SrTiO3对高铁酸盐电化学性能影响研究

Two ferrates, K₂FeO₄ and BaFeO₄, had been prepared and characterized by XRD, IR and SEM. The electrochemical tests of the samples were carried out in the voltage range of 0.8～2.0 V and current density of 0.5～3.0 mA·cm^-2. The results indicated that performance of Zn-BaFeO₄ battery was superior to that of Zn-MnO₂ and Zn-K₂FeO₄ batteries. Nanometer SrTiO₃ prepared by Sol-gel methode with different ratio was added to the BaFeO₄ cathode in order to improve the discharge performance. The discharge capacity of the BaFeO₄ cathode was increased from 224 mAh·g^-1 to 246 mAh·g^-1 by addition of 5% nanometer SrTiO₃. The reason of enhancing BaFeO₄ electrochemical performance was discussed.     

固定化辣根过氧化物酶在有机/水混合溶液中的电化学

用魔芋多糖(KGM)将辣根过氧化物酶(HRP)固定在玻碳电极(GCE)表面, 制备了HRP-KGM膜修饰电极. 在乙醇等亲水性有机溶剂与水的混合溶液中, 包埋在KGM中的HRP 可以与电极发生直接电子传递, 且能催化还原过氧化氢、氢过氧化异丙基苯、氢过氧化叔丁基、过氧化丁酮等过氧化物. HRP-KGM膜修饰电极具有较好的稳定性和重现性, 可用于这些物质的定量检测.     

无机胶体法制备Pt/C催化剂及其性能表征

采用无机胶体法制备用于质子交换膜燃料电池(PEMFC)的Pt/C催化剂。研究了影响PtO₂胶体生成和稳定性的因素(溶液的pH值、浓度和温度条件等)以及不同还原剂浓度对Pt/C催化剂性能的影响。透射电子显微镜测试结果表明，采用经优化的工艺条件所制备的Pt/C催化剂平均粒径为3 nm，且分散性好、粒度均匀。X-射线衍射分析表明，催化剂中Pt(111)晶面的相对含量较高，有利于加速氧还原反应。单体PEMFC的电压/电流密度曲线测试表明，所制备的Pt/C催化剂具有良好的电化学性能。     

水相锌二次电池正极材料V2O5/C的电化学性能研究

采用溶胶－凝胶法合成了一种V₂O₅/C复合材料.扫描电镜（SEM）和红外光谱（FTIR）分析表明,这是一种外层V₂O₅胶体包覆内层乙炔分子的多孔复合材料.以V₂O₅/C作正极,锌片为负极,Zn(ClO₄)₂溶液为电解质组成水相锌二次电池,采用循环伏安（CV）和电化学阻抗谱（EIS）等方法研究发现:V₂O₅:C质量比为1:1时电极具有最好的电化学性能,电池开路电压达1.64 V; Zn^2＋能分别在1.01 V和1.26 V处分步嵌入V₂O₅/C结构中A、B两种位置,其嵌入电流密度峰值最高可达70 mA•g^－1,并且具有较好的循环充放电性能;在一定放电深度下,V₂O₅/C电极反应速率受Zn^2＋的扩散过程控制.     

苯胺类化合物的电化学氧化及随后化学反应

利用循环伏安法研究了二取代对苯二胺(1),四取代对苯二胺(2)和二取代氨基酚(3)三类化合物以及它们的衍生物的电化学行为及其氧化产物的随后不可逆脱氨反应。 1类化合物在任何pH下的电化学氧化均为一步双电子转移反应,2类化合物为二步单电子转移反应;3类化合物在酸性和中性范围为一步双电子氧化在碱性溶液中为二步单电子转移反应。文中定量求算了不可逆随后化学反应的表观水解速率常数k_f,并进行了讨论。     

NdOx作为助催化剂对PtRu/C电催化氧化甲醇活性的影响

采用沉积-还原法制备了PtRu-NdOx/C催化剂, 借助TEM、EDS和XRD等测试手段对其进行了微结构和组成的表征. 结果表明, 催化剂中Pt与Ru以合金形式存在, 而Nd的氧化物则以无定形形态存在. 催化剂粒子的平均粒径在2 nm左右, 晶胞参数为0.3896 nm, Nd氧化物的加入对PtRu合金的晶体结构影响不明显. 采用循环伏安法和计时电流法, 比较了PtRu-NdOx/C催化剂和PtRu /C催化剂对甲醇氧化的电催化活性, 结果表明, 加入Nd的氧化物作为助催化剂能明显提高PtRu /C催化剂对甲醇氧化的电催化性能.     

A Home-made Simple Set-up for Measurement of Electrochemical Surface Tension Spectrum on a Mercury Drop Electrode

A setup for recording surface tension curves at a mercury drop during potential scanning is designed based on photo-sensitive detection system. Surface tension spectrum at Hg drop can be recorded by voltammetric study. A Yb(III)-NO2- catalytic reduction system was used for characterization. The simple, sensitive technique can be expected to provide fresh information on molecular interactions at electrode surfaces.     

电化学检测在流动注射分析中的应用

评述了近几年来电化学检测在流动注射分析中的应用，展望了流动注射电化学分析法的发展动向。     

四核钼簇合物Mo4S4（μ—OAc）2（dtp）4在一些非水溶剂中的电化学研究

利用循环伏安法测定了四核钼簇合物Ｍｏ４Ｓ４（μ－ＯＡｃ）２（ｄｔｐ）４在ＣＨ４ＣＮ，ＤＭＦ，ＤＭＳＯ等溶剂中的氧化还原半波电位（Ｅ１／２），对其氧化还原进行了归属，结果表明在ＣＨ３ＣＮ中存在一个单电子的氧化过程和二个单电子的还原过程，而在ＤＭＦ和ＤＭＳＯ中只存二个单电子的还原过程，同时还探讨了溶剂的ＤＮ数对该簇合物电化学性质的影响。     

铬(Ⅵ)与谷胱甘肽作用及其中间态配合物形成的电化学表征

本文采用电化学方法，对谷胱甘肽(GSH)与重铬酸钾的相互作用及其中间态配合物的形成过程进行研究。结果表明：在pH=5.6的HAc-NaAc缓冲溶液中，GSH浓度为Cr(Ⅵ)浓度5倍以上时，Cr(Ⅵ)与GSH作用完全并形成一新的中间态配合物，该中间态配合物于+0.21 V和+0.36 V(vs SCE)处产生一对新的氧化还原峰，UV-Vis的吸收光谱进一步证明了中间态配合物的形成。该配合物不稳定，在一定时间内缓慢分解，其电化学与UV-Vis光谱动力学信息同步。进一步探讨了GSH与Cr(Ⅵ)作用的电极反应机理。当Zn(Ⅱ)存在于该体系时，Zn(Ⅱ)对中间态配合物的生成和分解过程起着双向催化作用。