微波等离子体化学气相沉积合成掺氮金刚石薄膜的缺陷和结构特征及其生长行为

Diamond film was deposited in CH₄ and H₂ gas mixture with a small amount of N₂ by microwave plasma assisted chemical vapor deposition (MPCVD). Scanning electron microscopy, Raman spectroscopy and transmission electron microscopy were applied to characterize the film. The results showed that the growth of grains are different the central region and the edge. In the central region, diamond grains nucleated with a density as high as 4.8×10⁸ cm^-2 and were preferential in 〈001〉 orientation. The inner grains formed an area without stacking faults,which was surrounded by a rim with a high density of stacking faults. A growth model was suggested to interpret the morphological feature and the behavior of preferential growth. At the edge, the grains were identified to be 6H polytypes of diamond and a new twin relationship of grains was found. Besides, the effect of the N dopant on the growth behavior of the diamond film deposited by MPCVD was discussed in connection with the growth rate of the film. 关键词： 金刚石 结构表征 透射电子显微镜 多型金刚石     

乙炔气体流量对纳米TiC类金刚石复合膜的化学结构及力学性能影响

采用离子注入与反应磁控溅射相结合的方法在钛合金及硅片基体表面上制备了纳米TiC类金刚石(DLC)复合膜.通过纳米压痕技术检测了薄膜的纳米硬度，显微划痕试验评估了薄膜的结合力.通过X射线光电子能谱及X射线衍射表征了薄膜的化学结构.结果表明，通过改变C₂H₂气体流量，可以达到控制薄膜中钛原子含量的目的，合适的C₂H₂气体流量可以在DLC膜中形成较多的纳米TiC晶粒，形成DLC包覆TiC晶粒的复合结构，使DLC膜力学性能得到明显提高.另外，划痕试验表明掺钛、先注入后沉积工艺都使薄膜的结合力得到了较大提高. 关键词： 纳米TiC类金刚石复合膜 类金刚石膜 力学性能     

含氮氟化类金刚石(FN-DLC)薄膜的研究：(Ⅳ)氮掺杂对薄膜结构的影响

不同条件下，在单晶硅基片上沉积了含氮氟化类金刚石(FN-DLC)薄膜.原子力显微(AFM)形貌显示，掺N后，薄膜变得致密均匀.傅里叶变换吸收红外光谱(FTIR)表明，随着r(r=N₂/［N₂+CF₄+CH₄］)的增大薄膜中C—H键的逐渐减少，C〖FY=,1〗N和C≡N键含量逐渐增加.X射线光电子能谱(XPS)的C1s和N1s峰拟合结果发现，N掺入导致在薄膜中出现β-C₃N₄和a-CN_x(x=1,2,3)成分.Roman散射谱的G峰向高频方向位移和峰值展宽等证明：随着r的增大，薄膜内sp²键态含量增加. 关键词： 氟化类金刚石膜 键结构 氮掺杂     

CVD金刚石薄膜探测器性能研究

通过实验测量和理论分析, 从载流子动力学角度研究了用于脉冲辐射探测的CVD金刚石薄膜探测器的适用结构、电荷收集效率和时间响应性能. 结果表明, CVD金刚石薄膜可以制成均匀型结构的探测器; 薄膜中的缺陷会降低探测器的电荷收集效率, 探测器的电荷收集效率随场强增大而增大直至饱和. 已研制的CVD金刚石探测器电荷收集时间可达719ps, 在2.5V/μm场强下达到饱和, 电荷收集效率 达60.5%; 晶格散射是影响探测器时间响应的主要因素, 选用大晶粒甚至单晶金刚石薄膜可以提高探测器时间响应.     

双离子(40Ar+,C2H6+)辐照合成金刚石纳米晶颗粒

用双离子(40Ar+,C1H6+)辐照实验完成了从多壁碳纳米管向金刚石纳米晶颗粒的转变.对转变机理进行了初步探讨.这一探索有望能成为一种金刚石纳米晶合成的新途径.由此可知,多重荷能离子辐照用于其他材料纳米结构的制备也不是凭空设想.     

类金刚石薄膜的制备、特性及应用

利用射频等离子分裂碳氢气体制备的类金刚石膜,具有硬度高、耐蚀和良好的透红外光等特性.本文研究了类金刚石膜的红外、机械、结构及电学特性,给出该膜应用于红外装置中镀膜元件的光谱性能.并结合文中所用的制备方法,讨论了类金刚石膜在低温低压下的形成机制.     

用显微金刚石池测试高分子弹性材料的红外光谱

本文论述了用显微金刚石池研究高分子弹性材料，方法简便、快速和精确。