本文利用对苯二甲酰氯（ＴＰＣ），对苯二胺（ＰＰＤ）和亚甲基数为２和６的两种脂肪族二元胺（ＡＤＡ）合成了具有不同序列结构的芳香一脂肪族共聚酰胺．研究了共聚酰胺的序列结构参数──无规度Ｂ和数均序列长度Ｌｎ与液晶临界浓度Ｃ＊和中介相的类型之间的关系．     

Zr柱撑蒙脱土上负载稀土铈及铜铈催化剂的制备与表征

The Zr-pillaraed montmorillonite supported Ce and Cu-Ce catalysts were prepared by impregnation method. The performance of the catalysts was evaluated via the catalytic oxidation of volatile organic compounds (acetone, ethyl acetate, and toluene). The results showed that after supporting with Ce and Cu-Ce, the catalysts had a better reducibility. Moreover, the surface areas of the samples were increased. In addition，it was found that the Zr-pillared montmorillonite supported Cu-Ce catalysts had a higher activity and the reaction temperature decreased by 150～200 ℃ compared with the sample without Cu-Ce modification.     

气体法低温稀土多元共渗的研究

从自制的多种渗剂中,筛选了含稀土的最佳渗剂,实现了气体法低温稀土、硼、碳、氮、氧多元共渗。获得了组织、性能和层深远优于其它低温化学热处理的渗层。用金相、扫描电镜、光电子能谱和正电子湮没等技术,对渗层进行了较系统的分析,对稀土的催渗等基本理论问题进行了探讨。     

C_(60)离子束撞击固体表面的坍塌沉积(Ⅰ)共焦显微拉曼光谱研究

为了研究C60的结构特性，我们最近在实验中将加这后的C60离子束沉积在固体表面，对其沉积后的形态进行了共焦显微拉曼光谱的表征．在记录的光谱中已检测不出C60原有的特征谱问，说明C60离子在高速憧击固体表面后，已经完全失去了原有的球状构型．C60的t）［R实验在自制的串级飞     

甲基丙烯酸缩水甘油酯/苯乙烯固相接枝聚丙烯

以苯乙烯(St)为共单体，过氧化苯甲酰(BPO)为引发剂，采用固相接枝反应将甲基丙烯酸缩水甘油酯(GMA)接枝到聚丙烯(PP)大分子链上。研究了反应时间、单体用量、引发剂用量等因素对接枝率的影响。采用凝胶渗透色谱(GPE)测定了PP和接枝物PP-g-(GMA-St)的分子量和分子量分布。结果 表明固相接枝PP反应条件为[GMA／[St]=2，反应3．5h，加入GMA 10份，BPO 5份。St的加入有助于GMA与PP的接枝，同时在一定程度上抑制了PP的降解。     

沥青—重油共炭化反应机理的研究 Ⅰ.原料沥青和共炭化沥青的结构

使用一种工业重质油和中温煤焦油沥青进行共炭化反应，改善了煤历青的炭化性质。利用核磁共振（ＮＭＲ）手段详细研究了共炭化反应前后沥青ＴＳ（甲苯可溶）组分的结构变化，发现共炭化反应使沥青中的环烷及链烷烃含量增加，烷烃结构尤其是环烷结构的丰富是导致沥青改性的主要原因。     

热处理及与KOH共炭化对深度脱除煤中无机矿物质的促进作用

研究了煤经热处理（炭化）以及煤与ＫＯＨ共炭化对酸洗脱灰的影响。结果表明，煤经炭化再用盐酸洗涤，可以在缓和的条件下大幅度提高酸洗脱灰率；煤与ＫＯＨ共炭化后再酸洗，不仅对煤中的粘土、黄铁矿等无机矿物质有很好的效果，还特别适于脱除在一般情况下都难以除去的石英矿物。     

Fe3+/V5+/TiO2复合纳米微粒光催化性能的研究

采用溶胶凝胶法制备了Fe^3 /V^5 /TiO2复合纳米微粒作为光催化剂。光降解反应结果表明，其掺杂催化剂Fe^3 /V^5 /TiO2的光催化活性明显提高。光电化学研究显示，铁离子可以成为电荷陷阱，促进空穴的界面传递反应。适量钒离子掺杂使TiO2电极的光电流升高，导带中电子浓度的增大，加快了界面的电子传递反应。共掺杂催化剂中，Fe^3 、V^5 分别提供了空穴与电子的陷阱，同时加快了电子与空穴的界面传递反应，从 更有效地提高光催化活性。双组份共掺杂为提高TiO2光催化活性提供新的途径。     

A MORPHOLOGICAL STUDY OF POLY（DIVINYLBENZENE-co-ACRYLIC ACID） IN CROSSLINKING PRECIPITATION POLYMERIZATION

Divinylbenzene-80 （DVB-80） and polar monomer acrylic acid （AA） having hydrogen bonding at a total monomer loading of 5 vol% were precipitated-copolymerized in a variety of organic solvents with 2,2＇-azobis（isobutyronitrile） （AIBN） as initiator. The experiments were investigated from a two-dimensional matrix, i.e., the actual crosslinking degree of DVB varying from 0 to 80% and the solvent composition varying from 0 to 100% of toluene mixture with acetonitrile, when the mixture of acetonitrile and toluene was used as the reaction solvent. Under various reaction conditions, six distinct morphologies including soluble polymers, swellable microgels, coagulum, irregular microparticles, and nano-/micrometer microspheres were formed and the structures of these polymer architectures were described. A morphological map was utilized to discuss the effects of both crosslinking degree of DVB and composition of solvent on the transitions between morphology domains. The results demonstrated that the microspheres are formed by an internal contraction due to the marginal solvency of the continuous phase and the crosslinking of the polymer network through the covalent bonding from DVB as well as the interchain hydrogen-bonding between the carboxylic acid units.     

α-Al2O3纳米粒子对Co-Ni合金异常共沉积电化学行为的影响

为了研究在电化学复合共沉积过程中,惰性纳米粒子和金属离子、电极表面的相互作用,以及由此产生的对合金电化学共沉积行为的影响.本文从两个吸附过程出发: 电解液中的金属离子和H＋在纳米粒子表面的吸附；纳米粒子迁移到阴极表面,在电极表面的吸附.采用Zeta电势和稳态极化以及电化学交流阻抗（EIS）研究了纳米Al2O3粒子和电解液中的金属离子，和电极表面的相互作用,进而分析了纳米粒子对Co2＋和Ni2＋还原沉积的影响规律.通过对阻抗数据的拟合,讨论了Al2O3纳米粒子对等效电路中各物理参数的影响.在H＋和不同金属离子在纳米粒子上发生竞争吸附的基础上,提出了纳米粒子和合金共沉积的可能反应历程.