Giant Magneto-Impedance of Co50Ni22Ga28 Alloy with High Chemical Ordering

The microstructure of CosoNi22Ga28 ribbon with the L10 structure is examined. The band-like morphology is observed. These bands with the width in a range of 40-200 nm appear along the transverse direction of the ribbon. The giant magnetoimpedance （GMI） effect in this alloy is measured. The results show that Co5oNi22Ga28 exhibits a sharp peak of the GAI effect. The maximum GAH ratio up to 360% is detected. The GMI effect measured versus temperature shows large jumps of the magnetoimpedance amplitude at the reversal martensitic transformation temperature 240℃ and Curie temperature 375℃C respectively. The jump ratios of the magnetoimpedance amplitude examined at these temperatures are about 5 and 10, respectively.     

Nano-tribological study on a super-hydrophobic film formed on rough aluminium substrates

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166^o was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer. The project supported by the National Natural Science Foundation of China (50375151, 50323007, 10225209) and the Chinese Academy of Sciences (KJCX-SW-L2)     

密封容器中后处理制备Tl2Ba2CaCu2Oy高温超导薄膜及其性能研究

以铝酸镧（001）单晶为基片，采用两步法制备Tl2Ba2CaCu2Oy（Tl 2212）高 温超导薄膜.首先，利用脉冲激光沉积（PLD）工艺沉积Ba2CaCu2Ox非晶前驱体薄膜；然后，前驱体薄膜在高温（720—850℃）下密封钢容器里铊化结晶形成Tl 2212薄膜.XRD结果表明Tl2212 薄膜是沿c轴方向生长的，其相组成为Tl 2212，摇摆曲线（0012）的半高宽为0.72° ，SEM图像显示其表面光滑平整，其零电阻温度为106.2K. 关键词： Tl 2212超导薄膜 脉冲激光沉积     

离子束增强沉积VO2多晶薄膜的温度系数

用改进的离子束增强沉积方法和恰当的退火从V2O5粉末直接制备了VO2多晶薄膜.实验测试表明，薄膜的取向单一、相变特性显著、结构致密、界面结合牢固、工艺性能良好，薄膜的电阻温度系数（TCR）最高可达4.23%/K.从成膜机理出发，较详细地讨论了离子束增强沉积 VO2多晶薄膜的TCR高于VOx薄膜的TCR的原因.分析认为，单一取向的VO2结构使薄膜晶粒具有较高的电导激活能，致密的薄膜结构减少了氧空位和晶界宽度，使离子束增强沉积 VO2多晶薄膜结构比其他方法制备的VOx薄膜更接近于单晶VO2是其具有高TCR的原 关键词： VO2多晶薄膜 离子束增强沉积 热电阻温度系数     

多壁碳纳米管膜湿敏特性的研究

研究了多壁碳纳米管(MWNTs)薄膜的湿敏特性，实验所用的多壁碳纳米管是用热灯丝化学气相沉积法(CVD)合成的.分别对未修饰和修饰的多壁碳纳米管膜温度和湿度特性进行研究后发现，修饰的多壁碳纳米管对温度和湿度非常敏感，且对湿度的响应时间和恢复时间短，重复性好.而未修饰的多壁碳纳米管对温度和湿度不太敏感.对修饰多壁碳纳米管的湿敏特性进行了理论分析，给出了其理论表示式. 关键词： 多壁碳纳米管 化学修饰 湿敏特性 物理吸附     

步进扫描时间分辨光谱及其在太阳电池光电导上的应用

建立傅里叶变换步进扫描时间分辨光电导光谱，并研究太阳电池中与转换效率密切相关的少数载流子寿命.实验选取三种典型的硅太阳电池(单晶硅样品1、多晶硅样品2和多晶硅样品3 )，发现其瞬态光电导的上升和衰退曲线可以分别用两个简单的指数函数描述.由于有复合中心的参与，复合过程中少数载流子的寿命比产生过程中的寿命短.为验证实验结果的可靠性，采用了提取样品少数载流子的体寿命和计算其有效扩散长度两种方法.通过与太阳电池暗伏安特性和负载特性研究相结合，进一步分析和讨论了少数载流子寿命与短路电流、开路电压和转换效率的关系.同时探讨了步进扫描时间分辨光谱实验的其他用途. 关键词： 步进扫描 时间分辨 硅太阳电池 瞬态光电导     

TiN和Ti1-xSixNy薄膜的微观结构分析

使用x射线衍射(XRD)、x射线光电子谱(XPS)、高分辨透射电子显微镜(HRTEM)和原子力显微镜(AFM)多种观测手段分析了TiN薄膜和Ti1-xSixNy纳米复合薄膜的微观结构.实验分析证明Ti1-xSixNy薄膜是由直径为3-5nm的纳米晶TiN和非晶Si3N4相构成,并且Ti1-xSixNy薄膜的表面粗糙度小于相同条件下制备的TiN薄膜,在Ti1-xSixNy薄膜体系的自由能中引入界面能的概念,在此基础上分析了体系中TiN晶粒的取向问题.     

走近纳米科技

 纳米科技于20世纪70年代兴起,进入21世纪越来越被大家耳熟。纳米科技在促进科技进步,提高社会文明程度,改善人类生存质量,更新对物质世界的认知及观念上扮演了举足轻重的角色。纳米是长度单位。一纳米为一米的十亿分之一,如果你的拇指指甲盖宽14毫米,这个比例就相当于拇指指甲盖宽度与地球直径间的比例。纳米科技所接触、研究、开发的是100纳米～0.1纳米范围内物质的性质和应用。一个分子或一个原子大小的数量级大致在10纳米。因此,纳米科技也可以说是在分子水平上观察、分析、研究物质的物理、化学性质并加以开发利用。