对磁弹耦合在决定纳米晶软磁合金宏观磁性中的作用进行了探讨,高场磁化规律以及正电子湮没测量表明:对Fe_73.5Cu₁Nb₃Si_13.5B₉合金,准位错偶极子造成的应力场对畴壁的钉扎效应是造成纳米晶软磁合金矫顽力的重要原因;结构缺陷造成的应力场与磁致伸缩的耦合作用对纳米晶软磁性能有重要的影响.在结构各向异性和磁弹耦合能共同作用下可解释纳米晶合金表现出最佳软磁性能.     

Si1－xGex/Si量子阱发光材料的分子束外延生长及其结构研究

采用固源Si分子束外延,在较高的生长温度于Si(100)衬底上制备出Si1－xGex/Si量子阱发光材料。发光样品的质量和特性通过卢瑟福背散射、X射线双晶衍射及光致发光评估。背散射实验中观察到应变超晶格的反常沟道效应;X射线分析表明材料的生长是共度的、无应力释放的,结晶完整性好。低温光致发光主要是外延合金量子阱中带边激子的无声发射和横光学声子参与的激子复合。并讨论了生长温度对量于阱发光的影响。     

NaNO3掺杂Y2O3材料的制备及电流变性质

利用NaCO3和Y（NO3）3做主要原料，合成了一系列用稀土氧化物（Y2O3）作为基础材料的新型电流变材料——NaNO3掺杂Y2O3材料。对于这些材料的介电性质、微观结构和电流变性能的研究结果表明，NaNO3的掺杂可以明显地提高Y2O3材料的电流变活性。材料在二甲基硅油中的悬浮液的剪切应力随NaNO3在Y2O3中的掺杂程度有明显变化，当Na／Y（物质的量的比）为0．6时材料的电流变性能最好，     

Dextran-modified iron oxide nanoparticles

Dextran-modified iron oxide nanoparticles were prepared by precipitation of Fe（Ⅱ） and Fe（Ⅲ） salts with ammonium hydroxide by two methods. Iron oxide was precipitated either in the presence of dextran solution, or the dextran solution was added after precipitation. In the second method, the iron oxide particle size and size distribution could be controlled depending on the concentration of dextran in the solution. The nanoparticles were characterized by size-exclusion chromatography, transmission electron microscopy and dynamic light scattering. Optimal conditions for preparation of stable iron oxide colloid particles were determined, The dextran/iron oxide ratio 0-0,16 used in precipitation of iron salts can be recommended for synthesis of nanoparticles suitable for biomedical applications, as the colloid does not contain excess dextran and does not coagulate.     

第一讲中子散射与散裂中子源

中子散射是研究物质微观结构和动态的理想工具之一,广泛地应用于凝聚态物质研究和应用的众多学科领域.散裂中子源能是新一代的加速器基脉冲中子源,能为中子散射提供高通量的脉冲中子.文章简明地介绍了中子散射的特点和它作为物质结构和动态探针的优越性,以及散裂中子源的基本原理、发展状况和多学科的应用优势.我国计划建设的散裂中子源CSNS中,靶站将由多片钨靶、铍/铁反射体和铁/重混凝土生物屏蔽体组成.质子束功率100kW下,脉冲中子通量约为2.4×1016n/cm2/s.第一期将设计建造高通量粉末衍射仪、高分辨粉末衍射仪、小角散射仪、多功能反射仪和直接几何非弹性散射仪等五台典型的中子散射谱仪,以覆盖大部分的中子散射研究领域.     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

浅谈高中物理单元结构“自学—质疑—讨论—小结”式教学

介绍以物理单元结构“自学—质疑—讨论—小结”式的教学模式的实施过程,并对其优越性及缺点都予以分析并提出改进方案。     

MORPHOLOGY OF BLACK CARBON AEROSOLS AND UBIQUITY OF 50-NANOMETER BLACK CARBON AEROSOLS IN THE ATMOSPHERE

Different-sized aerosols were collected by an Andersen air sampler to observe the detailed morphology of the black carbon （BC） aerosols which were separated chemically from the other accompanying aerosols, using a Scanning Electron Microscope equipped with an Energy Dispersive X-ray Spectrometer （SEM-EDX）. The results indicate that most BC aerosols are spherical particles of about 50 nm in diameter and with a homogeneous surface. Results also show that these particles aggregate with other aerosols or with themselves to form larger agglomerates in the micrometer range. The shape of these 50-nm BC spherical particles was found to be very similar to that of BC particles released from petroleum-powered vehicular internal combustion engines. These spherical BC particles were shown to be different from the previously reported fullerenes found using Matrix-Assisted Laser Desorption/Ionization Time-Of-Flight Mass Spectrometry （MALDI-TOF-MS）.     

HI-13串列加速器上核结构在束γ谱学研究：现状及展望

主要介绍HI-13串列加速器的现状, 升级工程BRIF以及计划中的BRIFF-Ⅱ, 在束γ谱学研究的现状与将来核结构研究的展望.