冲击波对结晶MgO晶体结构,表面性质和催化剂性能的影响

用ＸＲＤ，ＥＳＲ和ＴＰＤ等技术研究冲击波处理的结晶ＭｇＯ后发现，ＭｇＯ的晶格发生畸变，微应力值ε１／２Ｄ显著增大，有大量缺陷产生并形成Ｆ心，晶体的平均晶粒减小，且表现出各向异性，从而引起了催化剂表面碱中心强度增大，数目变化，在对乙烷氧化脱氢反应中表现出较高的活性和对乙烯的选择性，初步讨论了可能的结构模型和催化机理。     

Synthesis of Dimethyl Carbonate from CO2 , Methanol, and Epoxides Using Re（CO） 5 Cl/K2 CO3 as Catalyst System

IntroductionOver the past few years, dimethyl carbonate(DMC) has been proven to be an efficientmethylating,methoxylating, and methoxycarbonylating agent inorganic syntheses, in which DMC is used to replace thetoxic methyl halides, dimethyl sulfate or carb     

La1-xNdxSrCoO4催化剂的合成及其催化性能

采用聚丙烯胺溶胶-凝胶法制备了类钙钛矿La1-xNDxSrCoO4(x=0.1～0.9)复合氧化物催化剂,考察了其对CO和C3H8的催化氧化活性,并运用XRD、IR和TPR等手段对催化剂进行了表征.结果表明,所制备的样品均具有K2NiF4型结构,适量Nd2O3的加入增加了LaSrCoO4的催化活性,使LaSrCoO4催化剂粒度变小、晶格畸变率变大及与氧的结合能力减弱,从而有利于CO和C3H8氧化活性的提高.     

催化动力学光度法测定痕量铝

痕量铝在硝酸介质中能催化加速过氧化氢和高碘酸钾与二甲苯胺兰FF之间的褪色反应。研究了反应的最佳实验条件,建立了测定痕量铝的新方法。方法检出限为6.1×10-10gAl3+/mL,检测范围为0-1.0μgAl3+/25mL。本方法具有高灵敏度,选择性较好,操作简便,快速的特点。用以测定水样中的痕量铝,获得满意结果。     

催化荧光法测定痕量草酸

在硫酸介质中 ,草酸能催化重铬酸钾氧化罗丹明B褪色 ,使体系荧光猝灭 ,建立了催化荧光法测定草酸的新方法。催化反应在 50℃水浴中进行 1 0min ,为假零级反应。测定草酸的线性范围为 0 4～ 1 2 0mg·L- 1 ,其回归方程为ΔF =8 42c(mg·L- 1 ) 3 81 ,r=0 9983 ,检出限为 0 1 6mg·L- 1 。试验了 30种共存物质的干扰情况。此法用于生物样品中草酸含量的测定 ,结果满意。     

Pt-SDB疏水催化剂的研制

基于液相水-氢同位素催化交换的疏水催化剂研究已有近30年历史。从所报道的资料来看，目前用于重水提氚工艺中相转移的疏水催化剂主要集中在Pt-C-PTFE和Pt-SDB两类材料上。前者疏水性好，耐辐照稳定性好，后者催化活性好，但催化剂耐辐照稳定性稍差。拟在特制的SDB疏水材料上制备出催化活性好，性能稳定，满足使用要求的Pt-SDB疏水催化剂。     

SYNTHESIS OF MACROPOROUS COPOLYMER OF VCA AND DVB

The reactivity ratios of vinyl acetate(VAc) and divinyl benzene (DVB) were calculated from the Q and e values.The possibility of the copolymerization of these two monomers was predicted and the copolymerization was carried out by suspension polymerization technique in the presence of pore producing agent (toluene and gasoine).The relative ratio of acetoxy group and benzene ring in the copolymer were monitored by IR measurement during the polymerization.The variation of pore properties,such as spectific surface area,porosity and average pore diameter,with polymerization time were determined.The copolymers at various polymerization time were alcoholyzed and thus the variation of the hydroxyl group content with polymerization time was studied.     

超稳Y沸石制备技术对沸石铝分布的影响 Ⅱ.均匀铝分布的超稳Y沸石的制备

对水热处理后得到的USY沸石作进一步的酸处理以及采用改进的氟硅酸盐溶液骨架富硅工艺,分别得到了经XPS剖面分析证实为铝分布均匀的超稳Y沸石HAY-Ⅰ和HAY-Ⅱ。IR分析表明,在酸处理过程中从USY沸石中去掉的那部分非骨架铝类与3690cm~(-1)处羟基有关,仍残留在HAY-Ⅰ沸石中的那部分非骨架铝类与3670cm~(-1)和3600cm~(-1)处羟基有关。XRD和化学分析表明HAY-Ⅰ沸石仍含有约50％的非骨架铝类,而HAY-Ⅱ沸石则基本上不含非骨架铝类,HAY-Ⅱ沸石还显示更高的结晶保留度。DTA分析表明,HAY-Ⅰ和HAY-Ⅱ两种沸石的热稳定性均高于USY沸石。