锆英粉中二氧化锆测定方法的探讨

锆英粉是冶金铸造中大型钢件和各种合金铸件的抗粘砂涂料 ,具有很高的耐火度和导热性及低热膨胀性 ,锆英粉中二氧化锆含量直接影响到铸件表面的质量。随着锆英粉生产技术的进步 ,二氧化锆的含量可高达 65 % ,而锆英粉的分析报道很少 ,传统的分析方法通常采用铂金坩埚熔样的系统分析方法。用此方法对 5 5 %以上二氧化锆的锆英粉试样检测中 ,常常出现试样不易全部熔解且因二氧化硅中易夹杂二氧化锆而使分析结果偏低的问题。本法对系统分析方法中二氧化锆夹杂量进行了定量分析 ,并对改进熔剂、避免夹杂进行了试验研究。1　试验部分1.1　主要试…     

改性ZrO2-MnO2基整体式催化剂上NH3选择性催化还原NO

采用共沉淀法制备了ZrO2-MnO2催化剂,考察了CeO2,MoO3和WO3的添加对ZrO2-MnO2整体式催化剂上NH3选择性催化还原(NH3-SCR)NOx的影响,并利用低温N2吸附-脱附、X射线衍射、X射线光电子能谱、NH3和NO程序升温脱附等方法对催化剂进行了表征,结果表明催化剂物相为Mn0.2Zr0.8O1....     

Wideband Antireflection Film Fabricated by Glancing Angle Deposition

Graded-index ZrO2 films has been fabricated on K9 glass by glancing angle deposition. Because the index mismatch at the interface has been reduced, the film results in wideband high-transmission antireflection. From 400nm to 1200nm, the film reflection is lower than 0.8% and the lowest value is 0.2% at 432nm.     

ICP—AES法测定高纯二氧化锆中痕量杂质

介绍了高纯二氧化锆中痕量杂质元素Ｆｅ，Ｎａ，Ｓｉ，Ｔｉ的ＩＣＰ－ＡＥＳ测定方法。样品以浓Ｈ２ＳＯ４及（ＮＨ４）２ＳＯ４溶解，采用空白背景校正法消除基体Ｚｒ的光谱干扰，以基体匹配法补偿基体效应。各元素平均回收率为９５％－１０６％，相对标准偏差为１．３％－３．０％。     

纯ZrO_2纳米粒子结构的拉曼光谱研究

本文对粒径在５８～１０ｎｍ范围内不同粒度的纯ＺｒＯ＿２粒子进行了拉曼散射光谱研究。结果表明，粒子的点阵结构受表面效应的影响，粒径的减小，粒子表面层结构严重畸变，但仍是有序的结构。同时，表面效应将进一步引起ＺｒＯ＿２粒子点阵结构变化，在室温下，使单斜相的粒子自发地转变为四方相结构。ＺｒＯ＿２粒子由单斜相向四方相转变的临界直径为１５ｎｍ。     

在织构Ni衬底上用电子束蒸发沉积YSZ阻挡层

用轧制及再结晶方法制备了高度立方织构的金属Ni(镍）基带。采用电子束蒸发的方法在几个厘米长的Ni基带表面上生长YSZ（钇稳定二氧化锆）阻挡层。X射线衍射分析表明，YSZ层具有纯c轴取向和良好的平面内取向及立方织要。扫描电镜观察表明，YSZ阻挡层连续致密无裂纹。     

Autothermal reforming of methane over Ni catalysts supported over ZrO2-CeO2-Al2O3

Ni catalysts supported on Al2O3, ZrO2-Al2O3, CeO2-Al2O3 and ZrO2-CeO2-Al2O3 were prepared by coprecipitation method, and their catalytic performances for autothermal reforming of methane to hydrogen were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS. The relationship between the structures and catalytic activities of the catalysts was discussed. The results showed that the catalytic activity and stability of the Ni/ZrO2-CeO2-Al2O3 catalyst was better than those of other catalysts with the highest CH4 conversion, H2/CO and H2/COx ratio at 750 ℃. The catalyst showed a little deactivation along the reaction time during its 72 h on stream with the mean deactivation rate of 0.08%/h. The catalytic performance of the Ni/ZrO2-CeO2-Al2O3 catalyst was also affected by reaction temperature, no2 ： nCH4 molar ratio and nH2O ： nCH4 molar ratio. TPR, XRD and XPS measurements indicated that the formation of ZrO2-CeO2 solid solution could improve the dispersion of NiO, and inhibit the formation of NiAl2O3, and thus significantly promoted the catalytic activity of the Ni/ZrO2-CeO2-Al2O3 catalyst.     

Ni在ZrO2(111)薄膜表面的生长、电子结构及热稳定性

利用X射线光电子能谱、紫外光电子能谱和低能电子衍射研究了Ni纳米颗粒在ZrO₂(111)薄膜表面的生长模式、电子结构及热稳定性. ZrO₂(111)薄膜外延生长于Pt(111)单晶表面,厚度约为3 nm.结果表明,当Ni气相沉积到ZrO₂(111)薄膜表面上时,遵循Stranski-Krastanov生长模式,即先二维生长至0.5 ML(monolayer),然后呈三维岛状生长.随着覆盖度的减小, Ni 2p_3/2峰逐渐向高结合能位移.利用俄歇参数法分析发现,引起该峰向高结合能位移的主要原因来源于终态效应的贡献,但在低的Ni覆盖度时,也有部分初态效应的贡献,说明Ni在ZrO₂表面初始生长时,两者存在较强的界面相互作用, Ni向ZrO₂衬底传递电荷,形成带部分正电荷的Ni_δ+.两种不同覆盖度(0.05和0.5 ML)的Ni/ZrO₂(111)模型催化剂热稳定性研究表明,当温度升高时, Ni逐渐被氧化成Ni₂₊,并伴随着向ZrO₂衬底的扩散.本文从原子水平上认识了Ni与ZrO₂表面的相互作用和界面结构,为理解实际ZrO₂担载的Ni催化剂结构提供了重要的依据.     

共掺杂的二氧化锆纳米材料中Yb3+和Tm3+上转换发光

用共沉淀法制备了二氧化锆掺Yb3 和 0 2 (0 4 ,1)mol%Tm3 的纳米材料 ;用发射波长为 980nm的激光激发样品 ,测量了掺 0 2mol%Tm3 的纳米材料在不同退火温度下的上转换光谱 ;测量了在相同退火温度、不同泵浦电流下的上转换发射光谱 ;并研究了蓝色上转换发射的过程。