负载杂多酸催化剂H4SiMo12—nWnO40／SiO2的表征

合成H4SiMo12-nWnO40(n=0,6,12)的SiO2负载样品，XRD、TEM、LRS测定结果表明杂多酸在低负载量时在载体表面高度分散，但仍保持Keggin 单元结构，然后随负载量的增加逐渐聚集成较大的晶粒。XPS结果显示杂多酸同载体之间有一定的相互作用，但负载化对杂多酸的热稳定性影响不大。负载化使杂多酸在载体表面分散而提高其对异丙醇脱水的催化能力，当杂多酸在载体表面聚集形成较大晶粒后活性不再上升。吡啶吸附红外光谱结果显示负载样品同时具有B酸和L酸中心，异丙醇脱水催化反应发生在B酸位上。     

磺化聚醚醚酮／二氧化硅／磷钨酸导电复合膜的制备

1引言 直接甲醇燃料电池（DMFC）被认为是最适合发展可移动电源的选择之一，目前困扰DMFC发展的主要问题之一是所使用的质子交换膜（主要是杜邦公司的Nation膜）的阻醇性能较低。磺化聚醚醚酮膜（SPEEK）特有的微观结构使其阻醇性能明显的优于Nation膜，而较低的质子传导率、较差的机械性能以及溶胀等缺点限制了它的应用；本文通过在其中加入二氧化硅（SiO2）和磷钨酸（PWA）制备磺化聚醚醚酮／二氧化硅／磷钨酸导电复合膜，并考察了二氧化硅及磷钨酸对复合膜溶胀性能、质子传导率及机械性能的影响。     

甲酰胺对有序介孔二氧化硅形貌的影响

At room temperature and in acidic solution, ordered mesoporous silicas with particular morphology were synthesized using cetylpyridinium chloride as the template and formamide as the cosolvent. Scanning electron microscope (SEM), small angle X-ray diffraction (SXRD), and nitrogen adsorption techniques were used to characterize the as-synthesized and calcined samples. Results showed that the samples had hexagonal mesostructure analogous to MCM-41 and relatively narrow pore-size distributions (BJH). Besides, BET surface areas of the samples were in the range of 1 000～1 250 m²·g^-1 and high total pore volumes were up to 1.367 cm³·g^-1. Addition of formamide affected obviously mesostructures and the morphology of the mesoporous silica. Furthermore, with the increase of the concentration of formamide, the unit-cell constant decreased and particle shape changed from gyroids to fibers.     

Deposition of Layer－by－layer Inorganic－organic Nano－hybrid Ultrathin Films onto SBA－15

Deposition of inorganic-organic nano-hybrid ultrathin films onto mesoporous silicate materials has been proven possible by using layer-by-layer assembly method. In combination with sol-gel method, titania, subsequently dye molecules (or polymer) were successfully fabricated onto the inner wall of SBA-15. Their structures were preliminarily characterized by FTIR and solid-state UV-Vis spectroscopy, thermal analysis, and BET surface area measurements,respectively.     

Rapid Fabrication of Hollow SiO2 Spheres with Novel Morphology

The hydrolysis of tetraethoxysilane (TEOS) occurred on the surface of poly(methyl methacrylate) (PMMA) microshperes immediately after these microshperes were prepared in TEOS. Micron-sized hollow SiO2 spheres were obtained by calcination of the coated PMMA microshperes. It was found that the final hollow spheres were constituted by small SiO2 particles.     

醋酸十二铵的吸附和SiO2悬浮液的稳定性

（1）测定了醋酸十二烷基铵（DAA）在CAB－O－SIL上的吸附，其等温线属双平台或LS型[1－3，5]；（2）NaCl的存在使DAA的吸附增加．但不影响其低浓度下第一平台的吸附量；HCl的存在则在全浓度范围内抑制了DAA的吸附，（3）测定了CAB－O－SIL颗粒在上述各溶液中的悬浮液的稳定性；（4）根据表面形成小胶团的吸附理论（即二步模型产）[2，3，5，]，并借助电导跟踪溶液中发生的变化，满意地解释了吸附和聚沉的实验结果．