Bola型阴离子表面活性剂与溴化十二烷基三乙铵混合体系的表面性质与聚集行为

研究了具有简单结构的bola型阴离子表面活性剂二十酸二钠（C_(20)Na_2)与 阳离子型普通表面活性剂溴化十二烷基三乙铵（C_(12)Et_3）混合体系的表面性质 ，发现混合体系的cmc和γ_(cmc)比C_(12)Et_3单一体系未有显著降低。以负染色 ，FF-TEM，动态光散射（DLS）及粘度方法研究了混合体系的聚集行为，发现混合 体系中同时形成球形囊泡和管状聚集体，提出了产生这种聚集行为的机制。     

丁腈羟增韧环氧树脂形态与力学性能

研究了丁腈羟增韧环氧树脂的力学性能和形态结构，丁腈羟的用量、丁腈羟中丙烯腈的含量、固化条件对所形成的微区尺寸都有较大影响，并进一步影响固化物的力学性能。     

A Cyclic and Polymeric Phosphazene as Solid State Template for the Formation of RuO<Subscript>2</Subscript> Nanoparticles

Pyrolysis of the organometallic polymer: {{[N=P(R₁)]_0.8[N=P(OC₆H₄CH₂CN[Ru])₂]_0.15[N=P((OC₆H₅)(OC₆H₄CH₂CN[Ru]]_0.05}{Cl}_0.31} _n , [Ru]=CpRu(PPh₃)₂, R₁ = O₂C₁₂H₈ (1) as well of the cyclic specie {N₃P₃ (OC₆H₅)₅(OC₆H₄CH₂CN[Ru])}{PF₆} (2) under a flow of air at 800°C affords nanostructured RuO₂. Nanoparticles near to 10 nm were observed. The differences in the use of cyclic or polymeric phosphazenes, as solid state template, influence strongly the morphology and slightly the composition of the pyrolytic product. Temperature variable (SQUID) measurements in the range of 5–300 K of the material obtained from the polymer, indicate an antiferromagnetic interaction between the Ru atoms, although lower than that found for the crystalline ruthenium oxide, probably due to some amorphous product present in the pyrolytic material. The possible formation mechanism is discussed and the differences in using the cyclic or the polymeric compound as precursor is analyzed in terms of the relative content of Ru to P, N. A general formation method of nanostructured metal oxides is proposed.     

混合价四核锰配合物[Mn4O2(ClCH2COO)7(bipy)2]•H2O的合成、晶体结构及性质研究

在乙腈溶液中, 由混合价三核锰配合物[Mn₃O(ClCH₂COO)₆(py)₂]•(H₂O) (py为吡啶)与2,2′-联吡啶(bipy)反应合成了混合价(Mn₃^IIIMn^II)四核锰配合物[Mn₄O₂(ClCH₂COO)₇(bipy)₂]•H₂O. 采用元素分析、红外光谱、热分析和X射线单晶衍射法确定了其组成和结构. 标题化合物晶体属于三斜晶系, 空间群P-1, 晶胞参数: a＝0.89854(13) nm, b＝1.4027(2) nm, c＝1.9037(3) nm, α＝93.518(3)°, β＝96.736(3)°, γ＝94.875(3)°, V＝2.3680(6) nm³, Z＝2, D_c＝1.734 g/cm³, F(000)＝1238, GOF＝1.036, R₁＝0.0592, wR₂＝0.1162 [I＞2σ(I)]. 在标题化合物中, 配位结构单元中心为一蝶型[Mn₄(μ₃-O)₂]^7＋多核簇, 含有2个Mn₃(μ₃-O)单元, 具有近似C₂对称轴. 4个Mn离子均为六配位, 外围配体为7个氯乙酸根和2个2,2′-联吡啶, 处于变形的八面体环境. 变温磁化率研究表明标题化合物在整体上表现为反铁磁性耦合作用, 但在低温下的磁相互作用较为复杂.     

新型含二茂铁有机配合物的合成及其电化学性质

以二茂铁为起始原料,经氯汞化反应、溴代反应、Suzuki偶联反应、水解反应和取代反应等5步反应合成了一种新型的含二茂铁结构单元的有机配合物(7),其结构经1H NMR、13C NMR、IR和HR-MS(ESI-TOF)表征。电化学研究结果表明:化合物6的E1/2小于化合物7,具有较高的氧化还原活性。     

Carbon-Supported Silver Catalysts for CO Selective Oxidation in Excess Hydrogen

Carbon materials were used as supports for Ag catalysts that are prepared using the conventional wet impregnation method, and their catalytic properties for CO selective oxidation in excess hydrogen at temperatures below 483 K were tested. A variety of techniques, e.g. N2 adsorption, XPS, TPD, UV-Vis DRS, TEM and SEM, were used to determine the influence of physical and chemical properties of the carbon on the properties of Ag catalyst. It was found that defects on the carbon surface served as nucleation sites for silver ions, while functional groups on carbon surface induced their reduction to the metallic form. The formation of silver particles on carbon was governed by homogeneous and/or heterogeneous nucleation during the impregnation and subsequent activation processes. The best catalytic performance was obtained with a Ag/carbon black catalyst with a uniform size distribution of silver nanoparticles (about 12 nm), moderate BET surface area (with a mesoporous structure), and a limited amount of carbon-oxygen groups. The research indicates that carbon materials are potentially good supports for silver catalysts for preferential oxidation of CO in excess hydrogen.     

A Novel Carbon Nanotube-Supported NiP Amorphous Alloy Catalyst and Its Hydrogenation Activity

A carbon nanotube-supported NiP amorphous catalyst (NiP/CNT) was prepared by induced reduction. Benzene hydrogenation was used as a probe reaction for the study of catalytic activity. The effects of the support on the activity and thermal stability of the supported catalyst were discussed based on various characterizations, including XRD, TEM, ICP, XPS, H2-TPD, and DTA. In comparison with the NiP amorphous alloy, the benzene conversion on NiP/CNT catalyst was lower, but the specific activity of NiP/CNT was higher, which is attributed to the dispersion produced by the support, an electron-donating effect, and the hydrogen-storage ability of CNT. The NiP/CNT thermal stability was improved because of the dispersion and electronic effects and the good heat-conduction ability of the CNT support.     

加氢处理催化剂载体中Y型分子筛组分对催化剂表面性质和催化性能的影响

应用ＸＲＤ，ＸＰＳ，ＩＲ－ＴＰＤ，ＣＯ２和ＮＯ吸附及正庚烷裂解和噻吩加氢脱硫脉冲微反等方法，研究了加氢处理催化剂载体经Ｙ型分子筛改性前后各种性质的变化，结果表明，载体经Ｙ型分子筛改性后，催化剂的Ｂ酸、正庚烷裂解活性和异构选择性明显提高，Ｙ型分子筛以分散的形式分布于γ－Ａｌ２Ｏ３表面，减少了载体表面的空位铝，该催化剂中有盯当一部分金属组分进入Ｙ型分子筛孔道与３其Ｂ酸位作用，与ＮｉＱ／γＡｌ２Ｏ３相比     

配合物型非线性光学材料的晶体工程

以分子基材料为目标的功能配合物的设计合成是近年来材料化学研究的重要领域，传统的分子设计尽管在分子水平上获得了很大的成功，但在由分子到晶体，由微观性质到宏观功能的晶体工程研究中遇到了极大的困难。因为宏观功能不仅要求分子本身具有良好的性能，同时还要求分子按照一定的方式堆积和排列犤１～３犦。例如二阶非线性光学材料不但要求分子具备较大的非线性超极化率和非对称中心，而且还要求分子在堆积过程中形成无心空间群的晶体。而自然界中大约超过７０％的手性分子在结晶时都形成有心的空间群，因此，如何实现分子的无心堆积是非…