LaB6-ZrB2共晶复合材料的组织特征及控制

用电弧炉和电子束悬浮区熔炉法制备了ＬａＢ６ＺｒＢ２共晶复合材料，并用ＳＥＭ和ＴＥＭ方法对其显微组织进行了研究。结果表明，ＬａＢ６ＺｒＢ２形成纤维状共晶组织，控制凝固条件可得到定向排列的组织，ＬａＢ６基体上均匀分布着直径为０２～１２μｍ的ＺｒＢ２纤维，纤维长度可达１００μｍ以上。对于固液界面为平面生长的试样，其结晶学取向关系为［００１］ＬａＢ６∥［００１］ＺｒＢ２，（１１０）ＬａＢ６∥（０１０）ＺｒＢ２。     

Tribological properties of ormosil coatings

Transparent plastics are not scratch resistant. The damage leads to a loss of optical properties. Coatings prepared using either tetraethoxysilane or colloidal silica particles embedded in glymo is a way to avoid these disadvantages. Tribological experiments are carried out to better understand the surface modification due to a sliding friction. It is shown that the wear track is not directly related to usual mechanical properties such as Young's modulus and the hardness of the coating. The different stages leading to material loss are discussed in term of particle removal and debris circulation (accumulation or elimination) through the friction track. The mechanical properties of the film combined with the film to substrate adhesion are expected to play an important role as it can be deduced from results obtained as a function of the coating composition.     

A scratch-resistant single-layer antireflective coating by a low temperature sol-gel route

A novel quarterwave-thick narrow-bandwidth antireflective coating has been developed for both plastic and vitreous substrates by a sol-gel route. This coating has revealed pronounced scratch- and climatic-resistance under adverse conditions. The single-layer coating consists basically of a composite material made of silica as the discontinuous phase and of a polytetrafluoroethylene-derived (Teflon¹) organic polymer as the continuous phase. This leads to fluorine-containing colloidal silica product, or a so-called Flucosil coating. The coating is applied by spinning or dipping from specific solutions at room temperature followed by a mild and short heat treatment. In addition to remarkable abrasion and environmental resistance properties, such coatings have displayed excellent laser-induced damage threshold levels, surpassing uncoated substrates.We hope such a product might open new perspectives concerning household articles, architectural optical thin-films, ophthalmic uses, and so on.     

复合Fe2O3纳米粒子的高分子微球的结构表征

近年来，复合有机、无机粒子的高分子微球及其特殊性质越来越引起人们的兴趣与关注［1］．获得有机、无机复合微球的方法很多，如在无机粒子存在下的乳液或无皂乳液聚会[2，3]，通过可聚合的表面活性剂在粒子表面形成胶囊化层[4]以及共沉淀法等[5]．这些无机粒子包括氧化钛、氧化铁、氧化铝及氧化硅等．Haga等[6]增发现包覆在聚合物粒子中的CdS与其本体的光电性质不同；单分散的聚合物微球可以在基片上被组装成二维乃至三维有序的结构[7]．这为信息存储、立体印刷等领域提供了新途径．因此，将无机粒子与聚合物复合成为功能化粒子是一项有…     

Optimization of the process variables for the synthesis of cardanol-based novolac-type phenolic resin using response surface methodology

Models capable of predicting the maximum extent of conversion (p) of cardanol-based novolac-type phenolic resin, have been developed using response surface methodology to determine the optimum reaction conditions. Three-dimensional response surface and their contour plot were drawn. The maximum extent of conversion (98.93%) was predicted when the cardanol was condensed with formaldehyde (molar ratio 1:0.652) at 119.84 °C for a time period of 3 h with the catalyst (e.g., citric acid) concentration of 1.988% of total volume of cardanol and formaldehyde. The pH of the reaction mixture was maintained at 3.0. These predicted values for optimum process conditions were in good agreement with experimental data.     

四苯硼钠-甲苯胺蓝缔合物纳米微粒体系减色效应研究

在PH4.0醋酸-醋酸钠介质中，甲苯胺蓝在600nm处有一个吸收峰，随着四苯硼钠浓度的增大甲苯胺蓝在600nm处吸收峰降低，颜色减弱，这是由于甲苯胺蓝-四苯硼钠缔合物分子间存在较强的疏水作用及分子间作用力，聚集形成纳米微粒所致，甲苯胺蓝-四苯硼钠纳米微粒体系亦在600mm处有1个吸收峰，在400mm、470mm和580mm处产生3共振散射峰，其中400mm和580mm为甲苯胺蓝-四苯硼钠复合纳米微粒产生的特征共振散射峰，这也表明有纳米微粒存在，丙酮浓度的影响实验结果等表明，纳米微粒的形成是产生其减色效应的原因。     

Determination of degree of conversion as a function of depth of a photo-initiated dental restoration composite—III application to commercial Prodigy Condensable™

In this third work, we evaluated the degree of conversion (DC) versus depth of dental filling composite named Prodigy Condensable™ using infrared spectroscopy. Confirming previous results, there was a gradual reduction of DC with increasing depth but the composite exhibited extreme values of DC, an upper value (45.9%) on the surface and a lower one (6.1%) at a depth of 5 mm. The composite presented the worst performance among materials studied. The composite formulation was 80% of inorganic fillers and BisfenolA/dimethacrylate (BisGMA) (18%)/triethyleneglycoldimethacrylate (TEGDMA) (2.0%) as monomers. As stated before, type/ratio/viscosity of monomers and type, amount, size and size distribution of fillers all together had an important role in the cure reaction contributing to the final performance of the composite.     

A study of the formation of silica-supported mixed magnesium-manganese spinel oxides from multicomponent gels

The effects of thermal treatment on composite materials prepared by the gelation of sols comprising large concentrations of metal oxide precursor salts have been investigated, in order to determine the compositional and thermal requirements for forming spinel magnesium manganates in such systems. The preparative technique has been found to give rise to derived gel materials in which the metal oxide phase, in the form of regular spherical particles, is dispersed throughout a continuous silica matrix. Silica-supported mixed magnesium and manganese spinel oxide phases were obtained for systems comprising at least 30 wt% metal nitrate after heating to temperatures between 700 and 850°C, but not without concomitant formation of Mn₂O₃ and modification of the silica network by magnesium.     

Determination of dopamine in synthetic cerebrospinal fluid by SWV with a graphite–polyurethane composite electrode

This work describes an electroanalytical investigation of dopamine using cyclic voltammetry (CV) and the graphite–polyurethane composite electrode (GPU). In CV studies, well-defined redox peaks characterize the oxidation process at the GPU electrode, which is indicative of electrocatalytic effects associated with active sites on the GPU electrode surface. A new analytical methodology was developed using the GPU electrode and square wave voltammetry (SWV) in BR buffer solution (0.1 mol L^–1; pH 7.4). Analytical curves were constructed under optimized conditions (f=60s^–1, E_a=50 mV, E_I=2 mV) and detection and quantification limits of 6.4×10^–8 mol L^–1 (12.1 g L^–1) and 5.2×10^–6 mol L^–1 (0.9 mg L^–1), respectively, were achieved. The precision of the method was checked by performing ten successive measurements for a 9.9×10^–6 mol L^–1 dopamine solution. For intra-assay and inter-assay precisions, the relative standard deviations were 1.9 and 2.3%, respectively. In order to evaluate the developed methodology, the determination of dopamine was performed with good sensitivity and selectivity, without the interference of ascorbic acid in synthetic cerebrospinal fluid, which indicates that the new methodology enables reliable analysis of dopamine.     

负载型TiO2-聚酰亚胺亲水复合膜的制备与分离性能

采用溶解－流涎法，湿相转换法和干湿相转换法制轩了负载型ＴｉＯ２－聚酰亚胺亲水复合膜，采用扫描电镜，红外光谱，压汞和透气性实验等手段对该膜的孔径分布，表面结构及扩散性能进行了表征，并讨论了制备亲水对膜孔结构的影响，实验结果表明，三种膜均具有很好的亲水性能，而干湿相转换膜具有良好的孔径分布和分离性能。