碳质颗粒添加物对渣油热反应生焦的影响

在高压反应釜中研究了三种不同碳质颗粒添加物对克拉玛依常压渣油420℃氮气气氛下热反应生焦的影响。实验结果表明，反应初期碳质颗粒在一定程度上抑制渣油的热反应生焦。碳质颗粒抑制生焦的能力与其表面对极性组分的润湿吸附能力有直接关系，表面易被极性组分润湿的颗粒吸附沥青质的能力强，其抑制渣油生焦的能力也强。碳质颗粒对沥青质的吸附能力和抑制生焦的能力与其比表面积没有直接关系。生焦量随反应时间的变化表明，碳质颗粒在生焦的初期有抑制生焦的作用，后期有促进作用。对甲苯不溶物（TI）的扫描电子显微镜（SEM）和热重（TG）分析表明，和不含添加物的TI相比，含添加物的TI中，小球状甲苯不溶物的数量少、直径小。沥青质和生焦前驱相在碳质颗粒添加物表面的吸附和铺展作用是抑制渣油生焦的主要原因，该作用可以限制生焦前驱相的融并长大，在反应的初始阶段减少生焦量。     

葡萄糖、果糖和蔗糖在甲酰胺溶液中的体积性质

报导了含葡萄糖、果糖和蔗糖的甲酰胺溶液的密度数据，无限稀释表观摩尔体积和体积第二维里系数．利用改进的定标粒子理论、基团几何模型和基团加合方法，求解了溶质的空腔生成体积，溶质-溶剂间的氢键作用对体积性质的影响，并和水溶液中的情况进行了比较．     

Influence of fused deposition modeling parameters on the mechanical properties of ABS parts

This work aims to determine the influence of fused deposition modeling (FDM) printing parameters on the mechanical properties of parts fabricated on an Ultimaker2 printer with acrylonitrile butadiene styrene (ABS). The effect of several parameters such as interlayer cooling time (ILCT), nozzle diameter, infill density, raster angle and layer thickness on the ultimate tensile strength, yield strength, and elastic modulus of produced parts was evaluated. Two independent studies were conducted: a first study dedicated to the ILCT and a second study where the influence of other parameters was evaluated through a design of experiments (DoE) approach. Both studies were carried out through the execution of standard tensile tests. The statistical analysis of tensile tests results was processed with the ANOVA methodology. The obtained results indicate that a reduced ILCT improves the tensile strength of parts. It is shown that nozzle diameter and infill density are the parameters that most influence the mechanical properties of ABS, with the upper range selected values improving the studied mechanical properties. The raster angle configuration of (?45^o/45^o) benefits UTS and yield strength of ABS samples. Interactions of nozzle diameter on layer thickness were detected. It was observed that smaller layer thickness promotes a higher elastic modulus and UTS; however, for thinner layers (0.06‐0.10 mm), no significant differences were found on strength of samples due to potential high distortion levels.     

碳酸酯类电解液中Mg(NO3)2添加剂抑制锂枝晶生长的研究

在锂-硫化聚丙烯腈电池体系中,负极锂枝晶的形成和生长严重恶化了电池充放电性能,并给电池带来了安全隐患。而在更有利于稳定正极硫化聚丙烯腈材料的碳酸酯类电解液中,锂枝晶生长尤为严重。本文通过将硝酸镁添加到碳酸酯类电解液中,研究硝酸根和镁离子对锂金属表面改性的共同作用。实验数据发现,在硝酸根和镁离子共同作用下,锂枝晶生长被有效抑制。当硝酸镁浓度为100 mmol·L^-1时,锂铜半电池的库仑效率明显提高,并显著改善了锂-硫化聚丙烯腈电池的循环性能。300次循环后容量保持率为71%,远高于硝酸锂的61%和无添加剂的50%。     

A hierarchical porous carbon membrane from polyacrylonitrile/polyvinylpyrrolidone blending membranes:Preparation,characterization and electrochemical capacitive performance

Novel hierarchical porous carbon membranes were fabricated through a simple carbonization procedure of well-defined blending polymer membrane precursors containing the source of carbon polyacrylonitrile （PAN） and an additive of polyvinylpyrrolidone （PVP）, which was prepared using phase inversion method. The as-fabricated materials were further used as the active electrode materials for supercapacitors. The effects of PVP concentration in the casting solution on structure feature and electrochemical capacitive performance of the as-prepared carbon membranes were also studied in detail. As the electrode material for supercapacitor, a high specific capacitance of 278.0 F/g could be attained at a current of 5 mA/cm2 and about 92.90% capacity retention could be maintained after 2000 charge/discharge cycles in 2 mol/L KOH solution with a PVP concentration of 0.3 wt% in the casting solution. The facile hierarchical pore structure preparation method and the good electrochemical capacitive performance make the prepared carbon membrane particularly promising for use in supercapacitor.     

表面修饰ZrO_2纳米微粒的结构表征及摩擦学行为研究(英文)

采用XPS,FTIR,DSC,TGA等多种现代分析手段表征了硬脂酸修饰ZrO2 纳米微粒的结构.在四球摩擦磨损试验机上,首次评价了表面修饰ZrO2 纳米微粒用作润滑油添加剂的摩擦学性能,结果表明ZrO2 纳米微粒具有良好的抗磨减摩性     

采用一体化燃煤添加剂的燃烧中固硫作用研究

针对五个不同煤种 ,研制出与之相匹配的催化燃烧及固硫一体化添加剂 ,采用高温定硫仪对其燃烧固硫效果进行了评价 ,考察了温度、Ca S摩尔比等影响因素 ,并着重讨论了一体化添加剂中催化燃烧组分的协同固硫作用。结果表明 ,一体化添加剂中的金属催化组分对CaO固硫具有较大的协同促进作用 ,固硫作用适宜的Ca S摩尔比因而可适当降低 ,一体化添加剂在燃烧固硫方面比传统单一组分固硫剂更具优越性 ,从而使催化燃烧和燃烧固硫两个过程有机地结合在一起。     

氢化物发生–原子荧光光度法测定食品和食品添加剂中的砷、汞和铅

建立氢化物发生–原子荧光光度法测定食品和食品添加剂中砷、汞和铅元素的方法。对茶叶、方便面、精料与二氧化硅样品的前处理方法进行了研究,讨论了酸介质与酸度、还原剂浓度、铁氰化钾与草酸浓度等因素对样品测定的影响。当还原剂质量浓度为20 g/L、载流酸度为5%、铁氰化钾和草酸质量浓度分别为4 g/L和2 g/L时,砷、汞和铅的方法检出限分别为0.024,0.008,0.066μg/L,方法的回收率为85%~105%,测量结果的相对标准偏差分别为0.7%,0.7%,1.8%。该方法简便、快速、结果准确可靠,能满足食品和食品添加剂中砷、汞、铅的测定。     

过充保护添加剂1,2-二甲氧基-4-硝基苯和1,4-二甲氧基-2-硝基苯在锂离子电池中的应用

在锂离子电池电解液1 mol·L^-1 LiPF₆/(碳酸乙烯酯(EC)+碳酸二乙酯(DEC)+碳酸甲乙酯(EMC) (1:1:1,体积比))中分别添加1,2-二甲氧基-4-硝基苯(DMNB1)和1,4-二甲氧基-2-硝基苯(DMNB2)作为防过充添加剂.采用循环伏安(CV)、恒流充放电、过充测试、电化学阻抗谱(EIS)、扫描电子显微镜(SEM)等手段研究了DMNB1和DMNB2 的防过充效果, 以及添加剂与LiNi_1/3Co_1/3Mn_1/3O₂材料的相容性. 结果表明: DMNB1 和DMNB2 的氧化电位都在4.3 V (vs Li/Li⁺)以上, 且均能显著提高电池的过充保护性能. 100%过充和5 V截止电压过充测试表明, DMNB1 的防过充性能优于DMNB2. 采用基础电解液、添加0.1 mol·L^-1 DMNB1 和添加0.1 mol·L^-1DMNB2 电解液的LiNi_1/3Co_1/3Mn_1/3O₂/Li 电池, 0.2C 倍率下循环100 次, 容量保持率分别为98.4%、95.9%和68.1%. 证明硝基在添加剂苯环上的取代位置和其电化学性能之间有着密切联系.     

阴离子表面活性剂聚二硫二丙烷磺酸钠的合成

利用硫化钠与硫磺反应制备二硫化钠,然后将二硫化钠与1,3-丙磺酸内酯反应,合成了一种可作为电镀添加剂的阴离子表面活性剂——聚二硫二丙烷磺酸钠(SPS)。采用核磁共振氢谱对合成产物进行结构表征,确认了产物结构及产率。通过正交试验研究了产物产率与反应物配比、反应温度、溶剂加入量等因素之间的关系,找出了最优合成条件:第一步合成二硫化钠的反应中,硫化钠/硫磺物质的量比为1∶1.3,温度55℃,加水量18 mL;第二步合成SPS的反应中,1,3-丙磺酸内酯/硫化钠物质的量比为1.7∶1,温度40℃,溶剂量75 mL,产物的最高产率可达到95.8%。