Sulfonated poly(aryl ether ketone)s containing naphthalene moieties obtained by direct copolymerization as novel polymers for proton exchange membranes

A series of sulfonated poly(aryl ether ketone)s (SPAEKs) were prepared by aromatic nucleophilic polycondensation of 2,6‐dihydroxynaphthalene with 5,5′‐carbonyl‐bis(2‐fluorobenzenesulfonate) and 4,4′‐difluorobenzophenone. The structure and degree of sulfonation (DS) of the SPAEKs were characterized using ¹H NMR spectroscopy. The experimentally observed DS values were close to the expected values derived from the starting material ratios. The thermal stabilities of the SPAEKs were characterized by thermogravimetric analysis, which showed that in acid and sodium salt forms they were thermally stable in air up to about 240 and 380 °C, respectively. Transparent membranes cast from the directly polymerized SPAEKs exhibited good mechanical properties in both dry and hydrated states. The dependence of water uptake and of membrane swelling on the DS at different temperatures was studied. SPAEK membranes with a DS from 0.72 to 1.60 maintained adequate mechanical properties after immersion in water at 80 °C for 24 h. The proton conductivity of SPAEK membranes with different degrees of sulfonation was measured as a function of temperature. The proton conductivity of the SPAEK films increased with increased DS, and the highest room temperature conductivity (4.2 × 10^?2 S/cm) was recorded for a SPAEK membrane with a DS of 1.60, which further increased to 1.1 × 10^?1 S/cm at 80 °C. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2866–2876, 2004     

UV‐ignited frontal polymerization of an epoxy resin

By combining frontal polymerization and radical‐induced cationic polymerization, it was possible to cure thick samples of an epoxy monomer bleached by UV light. The effect of the relative amounts of cationic photoinitiator and radical initiator was thoroughly investigated and was related to the front's velocity and its maximum temperature. The materials obtained were characterized by quantitative conversion also in the deeper layers, not reached by UV light. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2066–2072, 2004     

Functionalization of polyethylene/silane copolymers in posttreatment reactions

7‐Octenyldimethylphenylsilane was copolymerized with ethylene via Et(Ind)₂ZrCl₂ methylaluminoxane catalyst system without loss of catalyst activity or decrease in molar mass. The comonomer contents in the polymer samples were at a level of 0.15–1.0 mol % and the reactive phenylsilane groups were posttreated to different alcoxy‐ and halosilane groups, for example, Si? F, Si? Cl, Si? OCH₃, and Si? OCH₂CH₃. The posttreatment reactions had no major effect on the molar masses or on the thermal properties (measured with differential scanning calorimetry) of the copolymers. The reaction pathways were nearly independent of the comonomer contents and the reactions reached 70–100% conversions. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1461–1467, 2004     

Dielectric relaxation analysis of starch oligomers and polymers with respect to their chain length

Starch belongs to the polyglucan group. This type of polysaccharide shows a broad β-relaxation process in dielectric spectra at low temperatures, which has its molecular origin in orientational motions of sugar rings via glucosidic linkages. This chain dynamic was investigated for α(1,4)-linked starch oligomers with well-defined chain lengths of 2, 3, 4, 6, and 7 anhydroglucose units (AGUs) and for α(1,4)-polyglucans with average degrees of polymerization of 5, 10, 56, 70, and so forth (up to 3000; calculated from the mean molecular weight). The activation energy (E_a) of the segmental chain motion was lowest for dimeric maltose (E_a = 49.4 ± 1.3 kJ/mol), and this was followed by passage through a maximum at a degree of polymerization of 6 (E_a = 60.8 ± 1.8 kJ/mol). Subsequently, E_a leveled off at a value of about 52 ± 1.5 kJ/mol for chains containing more than 100 repeating units. The results were compared with the values of cellulose-like oligomers and polymers bearing a β(1,4)-linkage. Interestingly, the shape of the E_a dependency on the chain length of the molecules was qualitatively the same for both systems, whereas quantitatively the starch-like substances generally showed higher E_a values. Additionally, and for comparison, three cyclodextrins were measured by dielectric relaxation spectroscopy. The ringlike molecules, with 6, 7, and 8 α(1,4)-linked AGUs, showed moderately different types of dielectric spectra. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 188–197, 2004     

Heterochain model for simultaneous long‐chain branching and crosslinking. III. Multicomponent polymerization

The matrix formula developed in the context of heterochain theory, M?_w = M?_wp + WF ( I ? M )^?1 S , was applied to describe the molecular weight development during free‐radical multicomponent polymerization. All of the required probabilistic parameters are expressed in terms of the kinetic‐rate constants and the various concentrations associated with them. In free‐radical polymerization, the number of heterochain types, N, needs to be extrapolated to infinity, and such extrapolation is conducted with only three different N values. This matrix formula can be used as a benchmark test if other approximate approaches can give reasonable estimates of the weight‐average molecular weights. The moment equations with the average pseudo‐kinetic‐rate constants for branching and crosslinking reactions may provide poor estimates when the copolymer composition drift during polymerization is very significant. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2801–2812, 2004     

Self-bonding in an amorphous polymer below the glass transition: A T-peel test investigation

Films of amorphous polystyrene (PS) with a weight-average molecular weight (M_w) of 225 × 10³ g/mol were bonded in a T-peel test geometry, and the fracture energy (G) of a PS/PS interface was measured at the ambient temperature as a function of the healing time (t_h) and healing temperature (T_h). G was found to develop with (t_h)^1/2 at T_h = T_g-bulk − 33 °C (where T_g-bulk is the glass-transition temperature of the bulk sample), and log G was found to develop with 1/T_h at T_g-bulk − 43 °C ≤ T_h ≤ T_g-bulk − 23 °C. The smallest measured value of G = 1.4 J/m² was at least one order of magnitude larger than the work of adhesion required to reversibly separate the PS surfaces. These three observations indicated that the development of G at the PS/PS interface in the temperature range investigated (<T_g-bulk) was controlled by the diffusion of chain segments feasible above the glass-transition temperature of the interfacial layer, in agreement with our previous findings for fracture stress development at several polymer/polymer interfaces well below T_g-bulk. Close values of G = 8–9 J/m² were measured for the symmetric interfaces of polydisperse PS [M_w = 225 × 10³, weight-average molecular weight/number-average molecular weight (M_w/M_n) = 3] and monodisperse PS (M_w = 200 × 10³, M_w/M_n = 1.04) after healing at T_h = T_g-bulk − 33 °C for 24 h. This implies that the self-bonding of high-molecular-weight PS at such relatively low temperatures is not governed by polydispersity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1861–1867, 2004     

Determination of the degree of cure under dynamic and isothermal curing conditions with electrical impedance spectroscopy

This article presents a new methodology for the quantitative determination of the progress of the curing reaction of a thermosetting resin, using the results of electrical impedance spectroscopy. The method is an extension of the use of the imaginary impedance maximum as a reaction progress indicator and is based on the demonstration of a close correlation between the reaction rate, as measured by conventional differential scanning calorimetry, and the rate of change of the value of the imaginary impedance spectrum maximum. Tests on a commercial aerospace epoxy resin under both isothermal and dynamic heating conditions with calorimetry and impedance spectroscopy have demonstrated the validity of the method and set the accuracy limits involved. This technique can be used as a real-time online control tool for thermoset composite manufacturing. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 146–154, 2004     

Novel fixed‐site–carrier polyvinylamine membrane for carbon dioxide capture

Fixed‐site–carrier membranes were prepared for the facilitated transport of CO₂ by casting polyvinylamine (PVAm) on various supports, such as poly(ether sulfone) (PES), polyacrylonitrile (PAN), cellulose acetate (CA), and polysulfone (PSO). The cast PVAm on the support was crosslinked by various methods with glutaraldehyde, hydrochloric acid, sulfuric acid, and ammonium fluoride. Among the membranes tested, the PVAm cast on polysulfone and crosslinked by ammonium fluoride showed the highest selectivity of CO₂ over CH₄ (>1000). The permeance of CO₂ was then measured to be 0.014 m³ (STP)/(m² bar h) for a 20 μm thick membrane. The effect of the molecular weight of PVAm and feed pressure on the permeance was also investigated. The selectivity increased remarkably with increasing molecular weight and decreased slightly with increased pressure in the range of 1 to 4 bar. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4326–4336, 2004     

Statistical thermodynamics evaluation of polymer–polymer miscibility

The Simha and Somcynsky (S–S) statistical thermodynamics theory was used to compute the solubility parameters as a function of temperature and pressure [δ = δ(T, P)], for a series of polymer melts. The characteristic scaling parameters required for this task, P*, T*, and V*, were extracted from the pressure–temperature–volume (PVT) data. To determine the potential polymer–polymer miscibility, the dependence of δ versus T (at ambient pressure) was computed for 17 polymers. Close proximity of the δ versus T curves for four miscible polymer pairs: PPE/PS, PS/PVME, and PC/PMMA signaled the usefulness of this approach. It is noteworthy, that the tabulated solubility parameters (derived from the solution data under ambient conditions) propounded the immiscibility of the PVC/PVAc pair. The computed values of δ also suggested miscibility for polymer pairs of unknown miscibility, namely PPE/PVC, PPE/PVAc, and PET/PSF. In recognizing the limitations of the solubility parameter approach (the omission of several thermodynamic contributions), these preliminary results are auspicious because they indicate a new route for estimating the miscibility of any polymeric material at a given temperature and pressure. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2909–2915, 2004     

A note on the necessary conditions for the algebraic Riccati equation

We derive some useful and easily computable necessary conditionsfor the existence of a positive semi-definite solution to thealgebraic Ricatti equation (ARE). A motivating example is givento highlight the usefulness of the conditions for controllerand observer designs for nonlinear systems. Further, an upperbound on the trace of the solution to the ARE is also derived.