It is proved that the variety of relevant disjunction lattices has the finite embeddability property. It follows that Avron's relevance logic RMI _min has a strong form of the finite model property, so it has a solvable deducibility problem. This strengthens Avron's result that RMI _min is decidable. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Novel,organosoluble, light‐colored fluorinated polyimides based on 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl or 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐1,1′‐binaphthyl

Two series of fluorinated polyimides were prepared from 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl ( 2 ) and 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐1,1′‐binaphthyl ( 4 ) with various aromatic dianhydrides via a conventional, two‐step procedure that included a ring‐opening polyaddition to give poly(amic acid)s, followed by chemical or thermal cyclodehydration. The inherent viscosities of the polyimides ranged from 0.54 to 0.73 and 0.19 to 0.36 dL/g, respectively. All the fluorinated polyimides were soluble in many polar organic solvents, such as N,N‐dimethylacetamide and N‐methylpyrrolidone, and afforded transparent and light‐colored films via solution‐casting. These polyimides showed glass‐transition temperatures in the ranges of 222–280 and 257–351 °C by DSC, softening temperatures in the range of 264–301 °C by thermomechanical analysis, and a decomposition temperature for 10% weight loss above 520 °C both in nitrogen and air atmospheres. The polyimides had low moisture absorptions of 0.23–0.58%, low dielectric constants of 2.84–3.61 at 10 kHz, and an ultraviolet–visible absorption cutoff wavelength at 351–434 nm. Copolyimides derived from the same dianhydrides with an equimolar mixture of 4,4′‐oxydianiline and diamine 2 or 4 were also prepared and characterized. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2416–2431, 2004     

功能性丙烯酸/MBAM体系共聚产物的研制

以丙烯酸和MBAM为主要原料，经聚合，合成了一种高性能的具有良好保水性能的聚合产物，其保水量达到750～1000倍．50℃以下有良好的保水性能，28℃以下有极好的保水性能，并研究了工艺条件对该产品性能的影响因素．     

Dynamic mechanical thermal analysis transitions of partially and fully substituted cellulose fatty esters

The main transitions of cellulose fatty esters with different degrees of substitution (DSs) were investigated with dynamic mechanical thermal analysis. Two distinct main relaxations were observed in partially substituted cellulose esters (PSCEs). They were attributed to the glass‐transition temperature and to the chain local motion of the aliphatic substituents. The temperatures of both transitions decreased when DS or the number of carbon atoms (n) of the acyl substituent increased. Conversely, all the transitions of fully substituted cellulose esters occurred within a narrow temperature range, and they did not vary significantly with n. This phenomenon was explained by the formation of a crystalline phase of the fatty substituents. The presence of few residual OH groups in PSCEs was responsible for a large increase in the storage bending modulus, and it eliminated the effect of n on damping. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 281–288, 2003     

Viscometric properties of dilute polystyrene/dioctyl phthalate solutions

We report viscometric data collected in a Couette rheometry on dilute, single‐solvent polystyrene (PS)/dioctyl phthalate (DOP) solutions over a variety of polymer molecular weights (5.5 × 10⁵ ≤ M_w ≤ 3.0 × 10⁶ Da) and system temperatures (288 K ≤ T ≤ 318 K). In view of the essential viscometric features, the current data may be classified into three categories: The first concerns all the investigated solutions at low shear rates, where the solution properties are found to agree excellently with the Zimm model predictions. The second includes all sample solutions, except for high‐molecular‐weight PS samples (M_w ≥ 2.0 × 10⁶ Da), where excellent time–temperature superposition is observed for the steady‐state polymer viscosity at constant polymer molecular weights. No similar superposition applies at a constant temperature but varied polymer molecular weights, however. The third appears to be characteristic of dilute high‐molecular‐weight polymer solutions, for which the effects of temperature on the viscosity curve are further complicated at high shear rates. The implications concerning the relative importance of hydrodynamic interactions, segmental interactions, and chain extensibility with increasing polymer molecular weight, system temperature, and shear rate are discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 787–794, 2006     

Thiol–norbornene materials: Approaches to develop high Tg thiol–ene polymers

The ability to prepare high T_g low shrinkage thiol–ene materials is attractive for applications such as coatings and dental restoratives. However, thiol and nonacrylated vinyl materials typically consist of a flexible backbone, limiting the utility of these polymers. Hence, it is of importance to synthesize and investigate thiol and vinyl materials of varying backbone chemistry and stiffness. Here, we investigate the effect of backbone chemistry and functionality of norbornene resins on polymerization kinetics and glass transition temperature (T_g) for several thiol–norbornene materials. Results indicate that T_gs as high as 94 °C are achievable in thiol–norbornene resins of appropriately controlled chemistry. Furthermore, both the backbone chemistry and the norbornene moiety are important factors in the development of high T_g materials. In particular, as much as a 70 °C increase in T_g was observed in a norbornene–thiol specimen when compared with a sample prepared using allyl ether monomer of analogous backbone chemistry. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5686–5696, 2007     

Effect of reaction conditions on the molecular weight and polydispersity of linear poly(arylene ether phosphine oxide)s prepared from an AB monomer

A thorough study of the polymerization behavior of 4‐fluoro‐4′‐hydroxytriphenyl‐phosphine oxide, 2 , under nucleophilic aromatic substitution reactions has been carried out. The synthesis of 2 was achieved in excellent yields by the reaction of bis(4‐fluorophenyl)phenylphosphine oxide, 1 , with one equivalent of potassium hydroxide in DMSO/water. The structure and purity of 2 were confirmed via ¹H, ¹³C, and ³¹P NMR spectroscopy along with elemental analysis. Polymerization reactions of 2 in NMP or DMSO at 180 °C provided the corresponding linear poly(arylene ether phosphine oxide)s, PAEPOs, with number average molecular weights, M_n, ranging from 11,700 to 36,500 Da. All of the polymer samples were completely soluble in chloroform, tetrahydrofuran, DMSO, NMP, and DMAc. The polymerization reactions were accompanied by a competing intramolecular process that resulted in the formation of cyclic oligomeric species that were removed via a final precipitation from methanol. Analysis using ³¹P NMR spectroscopy and size exclusion chromatography (SEC) confirmed that the majority of the lower molecular weight cyclic species were removed via this process. The polymer samples formed tough films when chloroform solutions were slowly evaporated on a glass slide. The PAEPO samples prepared in this study exhibited excellent thermal stability with T_d (5%) values between 503 and 542 in air while the glass transition temperatures ranged from 223 to 237 °C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2099–2106, 2006     

Preparation and properties of isobutylene–isoprene rubber–clay nanocomposites

Isobutylene isoprene rubber (IIR)‐clay nanocomposites have been prepared successfully by melt intercalation with maleic anhydride‐grafted IIR (Ma‐g‐IIR) and organophilic clay. In IIR‐clay nanocomposites, the silicate layers of the clay were exfoliated and dispersed into the monolayer. The nanocomposites exhibited greater gas barrier properties compared with those of Ma‐g‐IIR. When 15 phr clay was added, gas barrier properties were 2.5 times greater than those of Ma‐g‐IIR. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1182–1188, 2006     

Lithographic design of photosensitive polyarylates based on reaction development patterning

The factors affecting pattern‐forming properties in reaction development patterning were examined with polyarylates with various bisphenol moieties. The developability of the photosensitive polyarylates was dependent on the properties of the subtituent (R) in the bisphenol moieties. The development time decreased in the following order: R?C(CH₃)₂ > fluorenyl unit ? phenolphthalein unit > C(CF₃)₂ > SO₂. This order agreed with that of the reactivity between the polyarylates and ethanolamine, and these orders can be explained by pK_a of the bisphenol used to prepare the polyarylates. The development with NH₂? R′? OH resulted in successful positive‐tone pattern formation. However, pattern formation with the developers containing NH₂? R′? OCH₃ was unsuccessful. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2694–2706, 2006     

Preparation and characterization of rigid poly(vinyl chloride)/MMT nanocomposites. II. XRD,morphological and mechanical characteristics

A Haake torque rheometer equipped with an internal mixer is used to study the influence of the amount of sodium montmorillonite (Na⁺‐MMT) and organically modified MMT (O‐MMT) on X‐ray diffraction (XRD), morphology, and mechanical characteristics of rigid poly (vinyl chloride) (PVC)/Na⁺‐MMT and PVC/O‐MMT nanocomposites, respectively. Results of XRD and transmission electron microscopy (TEM) indicate that MMT is partially encapsulated and intercalated in the rigid PVC/Na⁺‐MMT nanocomposites. However, results of XRD and TEM show MMT is partially intercalated and exfoliated in the rigid PVC/O‐MMT nanocomposites. Tensile strength, yield strength, and elongation at break of the rigid PVC/MMT nanocomposites were improved simultaneously with adding 1–3 wt % Na⁺‐MMT or O‐MMT with respect to that of pristine PVC. However, the addition of Na⁺‐MMT or O‐MMT should be kept as not more than 3 wt % to optimize the mechanical properties and the processing stability of the rigid PVC/MMT nanocomposites. SEM micrographs of the fractured surfaces of the rigid PVC/Na⁺‐MMT and PVC/O‐MMT nanocomposites both before and after tensile tests were also illustrated and compared. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2145–2154, 2006