聚（对羟基苯甲酸／6—羟基萘—2—酸）纤维结晶结构的研究

用X－射线衍射和热分析的方法对聚（对羟基苯甲酸／6－羟基萘－2－酸）共聚芳酯纤维结构及其在热处理中的变化进行了研究。结果表明，尽管沿分子链方向共聚单体呈无规分布，但共聚组分仍能形成共晶，纤维具有一定的空间规整性，经强化热处理后，纤维结晶结构发生了变化。     

活性炭纤维电极电解法处理墨绿B染料废水

将铁丝缠绕在活性炭纤维(简称ACF)上制成电极,并在阴极鼓入空气,用电解生成的Fenton试剂处理墨绿B染料模拟废水.研究了电压、pH值、温度、空气流量、支持电解质的浓度等因素对染料脱色率的影响.结果表明,pH值越低,温度越高,处理效果越好,气流量的改变对于处理效果影响不大.室温时处理浓度为50mg·L-1的活性染料墨绿B,在实验电压为11V,中性条件下,无水硫酸钠的浓度为20g·L-1,通入空气流量为60L·min-1时,处理60min,色度去除率达到95%左右.55℃时,电解30min色度去除率就达到96%,60min时达到100%.     

高密度聚乙烯/全同立构聚丙烯共混物超拉伸纤维的热行为与力学行为

用热拉法制备了高密度聚乙烯(HDPE)/全同立构聚丙烯(iPP)共混物超拉伸纤维,研究了拉伸比对其热行为及力学行为的影响,随拉伸比增加,纤维中HDPE与iPP的结晶度增大,熔融温度升高、熔程变宽;纤维中HDPE与iPP的结晶度低于其纯组分,熔融湿度与熔程基本不受组分比的影响,随拉伸比增加,纤维的模量增高,以HDPE为主的纤维的拉伸强度增大,以iPP为主的纤维拉伸强度增至一定值后,不再随拉伸比增加而增大,并有下降趋势。     

ZrO2纳米粉末复合羊毛纤维研究

ＺｒＯ_２纳米粉末复合羊毛纤维研究陈代荣，樊悦朋（山东大学化学系济南２５０１００）关键词ＺｒＯ_２纳米粉末，羊毛纤维，复合纤维由陶瓷粉末和天然纤维形成的复合纤维的强度、织品的保暖性、抗起球性及防缩性能等均有所提高，报道较多的是微米级陶瓷粉末（粒径０．５...     

Electrospun nanofibers of poly（vinyl pyrrolidone）/Eu^3＋ and its photoluminescence properties

Nanofibers of poly（vinyl pyrrolidone） （PVP）/Eu^3＋ with diameters of 300-900 nm were prepared by using sol-gel processing and electrospinning technique. The products were characterized by scanning electron microscope （SEM）, Fourier transform infrared spectroscopy （FT-IR）, and photoluminescence （PL）. The results indicated that, Eu^3＋ was successfully embedded in the onedimensional hybrid nanofibers, and the PVP/Eu^3＋ hybrid nanofibers had favorable photoluminescence properties.     

硫化锌掺锰/聚乙烯醇复合纳米纤维的制备与表征

利用静电纺丝法与气固反应相结合, 成功地制备了硫化锌掺锰/聚乙烯醇复合纳米纤维, 并对所制备的复合物进行了表征, 探讨了复合物的结构及其性能.     

PET导电纤维的制取及研究

以过氧化二苯甲酰为引发剂,使丙烯睛在涤沦(PET)纤维上接枝共聚。接枝纤维在含铜化合物,含硫还原剂溶液中反应,制备PET导电纤维。讨论了影响接枝共聚的各种因素,选择出最佳聚合条件。对该纤维的导电成份和结构以及性能进行了研究。     

STRUCTURE EVOLUTION OF POLYMER CHAINS FOR NECKING FORMATION IN HIGH-SPEED FIBER SPINNING PROCESS

Finite element method is used to simulate the high-speed melt spinning process,based on the equation system proposed by Doufas et al.Calculation predicts a neck-like deformation,as well as the related profiles of velocity,diameter, temperature,chain orientation,and crystallinity in the fiber spinning process.Considering combined effects on the process such as flow-induced crystallization,viscoelasticity,filament cooling,air drag,inertia,surface tension and gravity,the simulated material flow behaviors are consistent with those observed for semi-crystalline polymers under various spinning conditions.The structure change of polymer coils in the necking region described by the evolution of conformation tensor is also investigated.Based on the relaxation mechanism of macromolecules in flow field different types of morphology change of polymer chains before and in the neck are proposed,giving a complete prospect of structure evolution and crystallization of semi-crystalline polymer in the high speed fiber spinning process.     

Pt微粒修饰纳米纤维聚苯胺电极对甲醇氧化电催化

以脉冲电流法制备的纳米纤维状聚苯胺(PANI)为Pt催化剂载体，用它制备了甲醇阳极氧化的催化电极Pt/（nano-fibular PANI）.研究结果表明, Pt/（nano-fibular PANI）电极对甲醇氧化具有很好的电催化活性,并有协同催化作用.在相同的Pt载量条件下， Pt/（nano-fibular PANI）电极比Pt微粒修饰的颗粒状聚苯胺电极Pt/(granular PANI)具有更好的电催化活性.此外， Pt的电沉积修饰方法同样影响Pt/（nano-fibular PANI）电极对甲醇氧化的催化活性.脉冲电流法沉积Pt形成的复合电极较循环伏安法电沉积得到的Pt复合电极具有更优异的催化活性.     

酚醛基活性炭纤维孔结构及其电化学性能研究

利用水蒸汽活化法制备了酚醛基活性炭纤维(ACF-H2O), 对其比表面积、孔结构与在LiClO4/PC(聚碳酸丙烯酯)有机电解液中的电容性能之间的关系进行了探讨. 用N2(77 K)吸附法测定活性炭纤维的孔结构和比表面积, 用恒流充放电法和交流阻抗技术测量双电层电容器(EDLC)的电容量及内部阻抗. 研究表明, 在LiClO4/PC有机电解液中, ACF-H2O电极的可用孔径(d)应在0.7 nm以上. 随着活化时间的延长, ACF-H2O的孔容和比表面不断增大, 但微孔(0.7 nm ＜ d ＜ 2.0 nm)和中孔(d ＞ 2.0 nm)率变化很小, 活化过程中孔的延伸和拓宽同步进行, 但过度活化则造成孔壁塌陷, 孔容和比表面迅速下降. 因此, 除活化过度的样品外, 电容量随比表面积呈线性增长, 最高达到109. 6 F•g-1. 但中孔和微孔的孔表面对电容的贡献不同, 其单位面积电容分别为8.44 μF•cm-2和4.29 μF•cm-2, 中孔具有更高的表面利用率. ACF-H2O电极的电容量、阻抗特性和孔结构密切相关. 随着孔径的增大, 时间常数减小, 电解液离子更易于向孔内快速迁移, 阻抗降低, 电极具有更好的充放电倍率特性. 因此, 提高孔径和比表面积, 减少超微孔(d ＜ 0.7 nm), 是提高 EDLC能量密度和功率密度的重要途径. 然而仅采用水蒸汽活化, 只能在小中孔以下的孔径范围内进行调孔, ACF-H2O电极电容性能的提高受限.