纳米晶掺钇硬质合金粉末的制备

采用高能球磨法制备了纳米晶掺Y硬质合金粉末。用XRD，SEM和DTA等分析检测手段，研究了纳米晶掺Y硬质合金粉末的结构、形貌和相的变化。结果表明：高能球磨45h，可获得晶粒尺寸约为8nm的掺Y硬质合金粉末；微量Y的加入，有利于硬质合金粉末晶粒的细化；在25～45h范围内，随着高能球磨时间的延长，粉末晶粒尺寸减小，且掺Y硬质合金粉末的晶粒尺寸比未掺Y的硬质合金粉末晶粒尺寸要细一倍；高能球磨25h，粉末中Co的X射线衍射峰消失。高能球磨掺Y硬质合金粉末的DTA曲线在626℃出现了1个尖锐的放热峰。高能球磨掺Y硬质合金粉末固结之后，其合金晶粒细小，机械性能较好。     

Copper Promoted Au/ZnO-CuO Catalysts for Low Temperature Water-gas Shift Reaction

IntroductionThe water-gas shift(WGS)reaction is an impor-tant step in many important chemical processes[1].Re-cently,the renewed interest in the removal of CO bythe WGS reaction has grown significantly because of theincreasing attention to pure hydrogen p…     

含金属纳米粒子的层层自组装及单壁碳纳米管的催化生长

利用层间的静电吸附作用，重氮树脂和不同种类的含金属纳米粒子被依次吸附到硅片表面形成层层自组装膜。通过改变自组装膜的层数可以控制纳米粒子在表面吸附的量，同时利用重氮树脂的光敏特性可以实现纳米粒子在表面的图案化排布。以这些纳米粒子为催化剂，研究了单壁碳纳米管在硅片表面的化学气相沉积生长。     

负载型纳米非贵金属催化剂上一氧化碳的氧化 Ⅲ.纳米Cu/γ-Al_2O_3催化剂预处理对催化剂活性的影响

以电弧等离子体法制备纳米铜活性组分．将物理法制备的负载型纳米Ｃｕ／γ－Ａｌ２Ｏ３催化剂用于催化一氧化碳氧化反应，发现在催化过程中其催化活性呈规律性变化，即初始活性较低；空气中焙烧预处理易使纳米粒子长大．催化剂的氧化与一氧化碳还原实验表明，铜氧化物活性高于零价铜     

Electrooxidation Mechanism of Methanol at Pt-Ru Catalyst Modified GC Electrode in Electrolytes with Different pH Using Electrochemical and SERS Techniques

The electrochemical and in-situ surface-enhanced Raman spectroscopy （SERS） techniques were used to investigate the electrooxidation behavior of methanol in acidic, neutral and alkaline media at a Pt-Ru nanoparticle modified glassy carbon （Pt-Ru/GC） electrode. The results showed that methanol could be dissociated spontaneously at the Pt-Ru/GC electrode to produce a strongly adsorbed intermediate, CO. It was found that CO could be oxidized more easily in the alkaline medium than in the acidic and neutral media. The peak potential of methanol oxidation was shifted from 0.663 and 0.708 V in the acidic and neutral media to -0.030 V in the alkaline medium, which is due to that the adsorption strength of CO on the Pt surface in the alkaline medium is weaker than that in the acidic and neutral media. The final product of the methanol oxidation is CO2. However, in the alkaline medium, CO2 produced would form CO3^2- and HCO3^- resulting in the decrease in the alkaline concentration and then in the decrease in the performance of DMFC. Therefore, the performance of the alkaline DMFC is not Stable.     

Amperometric Determination of lndole-3-acetic Acid Based on Platinum Nanowires and Carbon Nanotubes

Platinum nanowire （PtNW） can be grown by electrodeposition in polycarbonate membrane, with the average diameter of the nanowires about 250 nm. The PtNW and multiwalled carbon nanotubes （CNT） are then dispersed into chitosan （CHIT） solution. The resulting PtNW-CNT-CHIT material brings new capabilities for electrochemical devices by using the synergistic action of the electrocatalytic activity of PtNW and CNT. By dropping the PtNW-CNT-CHIT film onto the glassy carbon （GO） electrode surface, and after evaporation an amperometric sensor for the determination of indole-3-acetic acid （IAA） was developed. The oxidation current of IAA increased significantly at the PtNW-CNT-CHIT film coated GC electrode, in contrast to that at the CNT-CHIT modified GC. The linear response of the sensor is from 50 ng/ml to 50 μg/ml with a detection limit of 25 ng/mL.     

等离子体引发原位聚合制备凹凸棒土/聚苯乙烯纳米复合物

用阳离子表面活性剂处理凹凸棒土（Attapulgite),通过超声分散的方法将其均匀分散到苯乙烯单体中，并采用等离子体引发的方法制备出凹凸棒土／聚苯乙烯纳米复合物。通过透射电子显微镜（TEM）和X－射线衍射（XRD）观察了凹凸棒土及其纳米复合物的微观结构。对复合物的GPC测试表明，采用等离子体引发聚合反应可以显著提高树脂的分子量。XRD结果表明聚苯乙烯不是嵌入到凹凸棒土的层间，而是通过离子吸附接枝在凹凸棒土的棒状晶束上。     

溶剂萃取法制备Co(PO_3)_2超细微粉

本文用溶剂萃取法成功地制备了偏磷酸钴超细微粉并通过ＸＲＤ，ＩＲ，ＴＧ，ＤＴＡ，ＴＥＭ等实验对超细微粉的组成、结构进行了表征。     

微孔分子筛纳米晶的控制合成及其催化应用

纳米分子筛因具有高的外表面积和短的孔道结构而显示了独特的催化活性和选择性, 近年来已成为催化界的研究热点.本文就分子筛纳米晶的控制合成、催化基础研究,特别是当前分子筛纳米晶在自组装分级多孔材料和分子筛基纳米复合材料方面的新方向进行了系统的综述,分析了纳米分子筛研究中的机会和应用前景.     

液相合成方形PbS纳米晶的光学特性

采用一种简单、温和的液相合成方法制备了PbS纳米晶，利用透射电镜和高分辨透射电镜对PbS纳米晶的形貌与晶型结构进行了表征．研究了PbS纳米晶的光学吸收和光致发光特性，并比较分析了包覆剂聚乙烯吡咯烷酮(PVP)和回流时间对产物光学特性的影响．结果表明：PVP分子链中的O原子与纳米晶表面吸附的游离态Pb原子形成Pb-O配位键，使产物的激子吸收大为减弱，同时引起了表面浅束缚态能量的升高，最终导致了荧光淬灭现象．