MECHANICAL PROPERTIES OF OZONIZED HDPE FILLED WITH SERICITE-TRIDYMITE-CRISTOBALITE

The mechanical properties of ozonized high density polyethylene (HDPE) blended with sericite-tridymite-cristobalite (STC) were studied in this paper. The experimental results show that some oxygen containing polar groups are introduced on the molecular chain of HDPE through ozonization, the compatibility between HDPE and STC is thus improved, the mechanical properties of the blend are markedly enhanced. Compared with untreated HDPE/STC (60/40) blend, the yield strength and notched impact strength of ozonized HDPE/STC (60/40) blend are increased from 27.0MPa to 29.5MPa and from 2.8kJ/m^2 to 13.3kJ/m^2, respectively, the notched impact strength is close to that of HDPE (13.6kJ/m^2),the yield strength is in excess of 3.9MPa of that of HDPE. The yield strength and notched impact strength will be further increased to 30.7MPa and 32.4kJ/m^2 in case the ozonized HDPE is blended with STC pretreated with silane coupling agent.     

过(氧)硫酸根中硫和氧及臭氧中氧的氧化数与相应的氧化还原电对

提出了氧族元素教学中有关S2O2-8(SO2-5)中硫和氧及O3中氧的氧化数、氧化性本质以及这两种物质与其还原产物所构成的电对的表示问题。对与S2O2-8和O3相关的元素电势图和氧化态-吉布斯自由能图的表示提出了建议,并建议将过二硫酸(以及过一硫酸)及其盐归属于氧系列,放在过氧化氢之后讨论。     

Pd/MnOx+Pd/γ-Al2O3整体式催化剂降解地表臭氧

用高锰酸钾与硝酸锰氧化还原反应制备了高活性的氧化锰(MnO_x)催化组分,用胶溶法制备了高比表面积的γ-Al₂O₃载体,分别用等体积浸渍法制备了Pd/MnO_x和Pd/γ-Al₂O₃催化剂,然后将两者机械混合涂覆于堇青石上制得Pd/MnO_x+Pd/γ-Al₂O₃整体式催化剂。采用X射线衍射(XRD)、X射线光电子能谱(XPS)、程序升温还原(H₂-TPR)和低温N₂吸附-脱附对催化剂进行了表征。考察了在300至700℃焙烧MnO_x对催化剂降解地表O₃活性的影响。结果表明,Pd和MnO_x之间存在协同作用;MnO_x焙烧温度对催化剂活性有一定的影响,其中以600℃焙烧时催化剂的活性最高,O₃的起始(12℃)转化率达到88%,完全转化温度为18℃。MnO_x的物相和催化剂表面的吸附氧物种对催化活性影响较大,适当比例的MnO₂和Mn₂O₃共存有利于O₃分解,表面吸附氧为O₃分解的活性氧物种。     

空间中心紫外臭氧总量探测仪成功监测雾霾天气

前不久,我国中东部大部分地区持续出现雾霾天气。由国家空间科学中心自主研制的紫外臭氧总量探测仪利用吸收性气溶胶指数AAI（The Absorbing Aerosol Index）成功对雾霾进行监测。中国气象局正是利用“风云三号”气象卫星紫外臭氧总量探测仪实现了对雾霾事件的全过程监测。     

CH_2CH(~2A')自由基与臭氧反应机理的理论研究

用量子化学MP2（full）方法，在6－311+ +G~(**)基组水平上研究了CH_2CH (~2A~＇)自由基与臭氧反应的机理，全参数优化了反应过程中反应物、中间体、过 渡态和产物的几何构型，在QCISD（T,full）/6-311+ +G~(**)水平上计算了它们的 能量，并对它们进行了振动分析，以确定中间体和过渡态的真实性，研究结果表明 ：CH_2CH(~2A~＇)自由基与臭氧反应有两条可行的反应通道，分别为：CH_2CH (~2A~＇)+O_3→TS1→M1→TS2→O_2+OCH_2CH→TS4+O_2→O_2(~3∑_g)+CH_2CHO (~2A~＂)和CH_2CH(~2A~＇)+O_3→M2→TS3→O_2(~3∑_g)+CHO(~2A~＂),后一个反 应通道较容易发生，而且反应活化能小（2.97kJ/mol），说明CH_2CH(~2A~＇)自由 基与臭氧之间的反应活性很强。     

SnO2的制备及催化臭氧氧化活性

采用沉淀法制备了SnO2催化剂,以SnO2催化臭氧氧化降解糖蜜酒精废水脱色为探针反应,对催化剂的活性进行了评价.采用X射线衍射、红外光谱及热分析(TG-DSC)等技术对催化剂进行表征,研究了沉淀剂及焙烧温度等制备参数对SnO2催化臭氧氧化活性的影响.结果表明,SnO2催化剂对臭氧氧化降解糖蜜酒精废水脱色具有较高的催化活性,反应60 min后,糖蜜酒精废水的脱色率从单独臭氧氧化的43.04%提高到60.24%.沉淀剂对SnO2催化剂的活性影响很大,其中以氨水为沉淀剂制备的SnO2催化剂去羟基化反应程度高,所制得的催化剂活性最大.催化剂适宜的焙烧温度为723 K.SnO2吸附吡啶的红外光谱表明,催化剂表面存在L酸中心.臭氧在SnO2表面吸附的红外光谱表明,通过臭氧的末端氧原子与表面羟基及L酸中心成键,生成的活性氧可氧化降解糖蜜酒精废水.     

Au/TiO2光催化分解臭氧

 采用沉积-沉淀法制备了Au/TiO2催化剂,用透射电子显微镜、紫外-可见漫反射光谱和X射线光电子能谱进行了表征,结果表明,样品在空气中于200 ℃处理后,金以金属态Au0的形式沉积在TiO2表面. 与TiO2相比,担载金的TiO2具有明显的光催化分解O3的活性. 黑光灯光照20 h后, 1%Au/TiO2催化剂对O3的分解率仍达98%以上. TiO2上的Au簇作为电子的捕获中心,能够促使电子与空穴的有效分离. 而Au簇和载体TiO2的周界处作为O3新的吸附活性中心,促进了O3的分解.     

室温水汽对Au/TiO2上光催化分解臭氧的影响

 采用沉积-沉淀法制备了Au/TiO2光催化剂,并用紫外-可见漫反射光谱和X射线光电子能谱对其进行了表征,详细考察了室温水汽的引入对Au/TiO2光催化分解臭氧活性的影响. 结果表明,同干燥状态时相比,室温引入水汽后催化剂活性较低,并且较快地达到了稳定值. 催化剂的O 1s和Au 4f的XPS分析结果表明,水汽的存在导致TiO2的表面结构发生变化,进而使金-载体之间的相互作用力减弱. 这是导致催化剂活性下降的主要原因.     

Al2O3催化剂结构对催化臭氧化活性的影响

以Al₂O₃为催化剂催化臭氧化处理邻苯二甲酸二甲酯. 通过XRD、比表面积、孔结构、FTIR和活性评价等方法对催化剂的物化性质及催化活性进行了研究, 考察了焙烧温度、成型粒径对催化剂活性的影响. 结果表明, Al₂O₃催化剂对臭氧化降解邻苯二甲酸二甲酯具有很高的催化活性, 反应120 min后, 总有机碳(TOC)的去除率从单独臭氧氧化的23.9%提高到55.1%; 焙烧温度对催化剂的活性具有很大的影响, 600 ℃催化剂催化活性最高; 随着焙烧温度的升高, Al₂O₃晶型经历了从γ-Al₂O₃到θ-Al₂O₃到α-Al₂O₃的转变, 催化剂的比表面积、焙烧得到的孔容逐渐变小, 晶体粒径变大, 表面•OH数量减少, 催化活性下降. Al₂O₃成型粒径的减小, 提高了催化剂的外比表面积, 减小了内部传质扩散的影响, 从而提高了催化活性.     

活性炭负载金催化分解空气中低浓度臭氧

采用等体积浸渍法制备了以煤质活性炭为载体的负载金催化剂,并运用N2吸附-脱附法和X射线光电子能谱对样品进行了表征.考察了该催化剂催化分解低浓度臭氧的活性,并研究了载体预处理方法和催化剂后处理方法对催化剂活性的影响.在常温,相对湿度为60%,臭氧浓度为45 mg/m3,空速为60 000 h-1的条件下,1.6 g活性炭经HNO3和NaBH4处理后负载金再经H2还原后的催化剂在反应最初的16 h内臭氧去除率稳定在100%,反应100 h后对臭氧的去除率仍在97%以上.表征结果表明,NaBH4还原处理使得活性炭比表面积、孔体积及石墨碳含量增加,含氧官能团下降,从而提高了催化剂的活性.载金后,催化剂比表面积和孔体积进一步增大,但石墨碳含量下降,C-O和COO-等含氧官能团增加.经臭氧氧化后,催化剂的比表面积和孔体积减小,石墨碳含量下降,C-O,COO-和C=O等含氧官能团增加,而金的粒径和价态并未改变,表明活性炭在金催化下被臭氧氧化.