Effect of La2O3／γ—Al2O3 Catalyst on the Activation of CH4 and CO2 to C2 Hydrocarbons under Non—equilibrium Plasma

In the reaction of methane and carbon dioxide to C2 hydrocabons under non-equilibrium plasma, methane conversion was decreased,but selectivity of C2 hydroxarbons was increased when using La2O3/γ-Al2O3 as catalyst. So the yield of C2 hydrocarbons was higher than using plasma alone. The synergism of La2O3/γ-Al2O3 and plasma gave methane conversion of 24.9% and C2 yield of 18.1%. The distribution of C2 hydrocarbons changed when Pd-La2O3/γ-Al2O3 was used as catalyst,the major C2 product was ethylene.     

Ni的掺入对复合氧化物LaFeO3的结构及性质的影响

合成子Ｎｉ替代铁酸稀土复合氧化物ＬａＦ３１－ｘＮｉｘＯ３（ｘ＝０．１－０．６），对样品进行了ＸＲＤ、ＩＲ及Ｍｏｓｓｂａｕｅｒ谱测试，结果表明：ｘ＝０＼１，０＼２，０＼３的样品为正交相，ｘ＝０．５，０．６的样品为菱方相；伴随相结构从正交向菱方结构的转变，ＩＲ谱上Ｆｅ（Ｎｉ）－Ｏ键伸振动谱带向高频移动近２０ｃｍ＾－１，Ｍｏｓｓｂａｕｅｒ谱测试表明Ｆｅ均处于＋３自旋态，Ｎｉ离子以＋３价进入晶格。     

甲烷氧化偶联Ti-La-Li系多元氧化物催化剂的表面碱性和表面活性氧种

利用ＣＯ２－ＴＰＤ方法考察了Ｔｉ－Ｌａ－Ｌｉ系多元氧化物催化剂的表面碱性，实验发现：Ｃ２选择性与表面碱强度呈顺变关系，而ＣＨ４转化率与ＣＯ２的脱附峰面积呈顺变关系。同时，利用ＸＰＳ，Ｏ２－ＴＰＤ等方法对该体系催化剂的表面活性氧种进行了表征与研究。结果表明：催化剂的表面晶格氧与Ｃ２选择性有关，表面吸附氧与甲烷转化（包括偶联和深度氧化）有关。Ｏ２－ＴＰＤ实验发现催化剂的表面存在三种氧。α（１００℃≤ｔ     

A Novel Catalyst for Liquid Phase Hydrogenation of m-Dinitrobenzene to m-Phenylenediamine

A novel lanthana-promoted nickel catalyst supported on silica for the liquid phase hydrogenation of m-dinitrobenzene to m-phenylenediamine was prepared by an incipient wetness sequential impregnation method. It was found that Ni-La/SiO2 catalyst exhibited high activity and stability for m-dinitrobenzene hydrogenation. Over this catalyst, the conversion of m-dinitrobenzene and the yield of m-phenylenediamine were up to 97.1% and 93.5%, respectively,at 373 K and 2.6 MPa hydrogen pressure after reaction for 1 h.     

Hydrothermal Synthesis and Structure of a New 3D Lanthanide—Carboxylate Framework,[La（btec）1／2（H2btec）1／2（H2O）]n（H4btec=1,2,4,5—Benzeneteracarboxylic acid）

The title complex, [La(btec)_1/2(H₂btec)_1/2 (H₂O)]_n (H₄btec= 1, 2,4,5‐benzenetetracarboxylic acid) (1) was synthesized by the hydrothermal reaction of 1,2,4,5‐benzenetetracarboxylic dianhydride with La(NO₃)₃·6H₂O in H₂O, and crystallizes in the triclinic system, space group P‐1 with a = 0.64403(3) nm, b = 0.94500(4) nm, c = 0.96380(5) nm, a = 88.535(2)°, β = 100.314(2)°, γ = 76.6470(10)°, V = 1.60968(10) nm³, Z = 2, and final R = 0.0274, R_w = 0.0735. In 1, each La(m) ion is coordinated by eight oxygen atoms from six carboxylate groups and one coordinated water molecule. Two different coordination modes of H₄btec were present in the structure, one of which contains two protonated carboxylate groups to balance the charge.     

EDTA-甘氨酸联合法制备LaAlO3基电解质材料及其电性能

采用EDTA-甘氨酸联合法(EGCP)合成具有钙钛矿结构的La0.90Sr0.10Al0.97Mg0.03O3-δ(LSAM)粉体。采用TG-DSC,XRD,ICP-OES和TEM对粉体进行表征。在750℃下,无定形结构的粉末直接转化为钙钛矿结构的LSAM粉体。经1000℃煅烧3 h后的粉体,团聚程度低,粒径分布均匀,平均粒径约为77 nm,具有良好的烧结性能。通过SEM对材料的显微结构进行观察并分析其对电性能的影响。采用直流四电极法在空气中测定材料的总电导率,在800℃时,EGCP合成的LSAM电解质的总电导率为1.50×10-2S.cm-1,比固相法的高47.1%。     

稀土镧在腈纶纤维化学镀银中的应用及其电化学性能

采用化学镀法(镀液中加入适量的稀土镧)在硅烷偶联剂改性后的腈纶纤维表面沉积金属银,由粒径分析、X射线衍射、扫描电子显微镜、阴极极化曲线以及循环伏安曲线等方法对其进行表征,研究了硝酸镧对化学镀银沉积速度、镀层质量和电化学性能的影响。结果表明,镀银液中加入适宜的硝酸镧,银的沉积速率和腈纶纤维表面银镀层的表面质量均有不同程度的提高。电化学测试表明,镀银液中增大硝酸镧的浓度(0～0.01 g/L),阴极极化曲线极化度增大,氧化还原峰的电流上升,电沉积的速度加快。     

La3+,Ce4+对制备堇青石材料晶相转变及烧结性能的影响

以菱镁矿风化石、工业氧化铝和二氧化硅微粉为原料,加入不同含量氧化镧、氧化铈添加剂,通过固相反应合成制备堇青石材料。用XRD法和SEM法表征试样中的晶相组成和显微结构,用X’Pert Plus软件计算主晶相的晶格常数、晶胞体积和试样的相对结晶度,用半定量法计算试样中各晶相含量,用Scherrer公式计算主晶相的粒径大小。研究分析了La3+,Ce4+对制备堇青石材料晶相组成、主晶相粒径大小、晶胞常数、试样相对结晶度、显微结构及烧结性能的影响。结果表明:氧化镧比氧化铈具有更好的助堇青石烧结性,加入氧化镧的堇青石试样具有更好的致密性;随着氧化镧、氧化铈加入量的增加,堇青石晶胞常数和晶胞体积呈现先增大后减小趋势;Ce4+更高的电场强度促进了堇青石材料更容易发生晶相转变形成莫来石。     

阻抑动力学光度法测定稀土氧化物中痕量镧(Ⅲ)

阻抑动力学光度法是测定痕量镧(Ⅲ)的新方法.在十六烷基三甲基溴化铵(CT-MAB)存在下,H3PO4介质中痕量镧(Ⅲ)对溴酸钾-氧化考马斯亮蓝的褪色反应具有阻抑作用.通过研究试剂用量、反应温度、反应时间和干扰离子等因素的影响,证明阻抑动力学光度法可以用于稀土氧化物中痕量镧(Ⅲ)的测定,测定结果可靠.     

Ni-La/CexZr1-xO2对甲烷部分氧化/CH4-CO2重整耦合制合成气的催化剂制备及反应性能

通过共沉淀法制备铈锆固溶体作为载体,采用等体积、分步浸渍的方法制备了一系列10% Ni-3% La/CexZr1-xO2（X=0、0.16、0.5、0.75、1）催化剂,并将其应用到甲烷部分氧化和甲烷二氧化碳重整耦合制合成气的反应中。对不同Ce/Zr比的催化剂性能展开研究,采用XRD、H2-TPR、SEM手段对载体及催化剂进行了表征。结果表明,铈锆固溶体的形成不仅提高了催化剂表面活性组分的分散度,使催化剂表面NiO晶粒尺寸从26.5 nm减到13.7 nm;而且能够加强活性组分与载体之间的相互作用,提高催化剂的热稳定性能;随着Ce/Zr比的增加,催化剂的转化率、选择性及稳定性随之增强,其关系为：Ni-La/Ce0.75Zr0.25O2 > Ni-La/Ce0.5Zr0.5O2 > Ni-La/Ce0.16Zr0.84O2。